The aim of this paper is to consider the effect of the manufacturing processes on corrosion and centerline cracking of ancient bronze spoons. The ancient bronze spoons in question were made by several steps of forging, in reheated condition with cast ingots. The manufacturing method is similar to that of the modern spoons. The investigations include observations from light and scanning electron microscopes of the microstructure in terms of the crack propagation. Cracks in the centerline are caused by solute segregation in the center-line region; this solute is solidified in the final stage of bronze spoon manufacture. Centerline cracking is also caused by ${\alpha}$ phase segregation, accompanied by forged overlapping along the longitudinal direction of the spoons. A vertical stripe with cracks along the centerline of the spoon's width is formed by folding in the wrought process. The overlapping area causes crack propagation with severe corrosion on the spoon surfaces over a period of a thousand years. The failure mechanisms of ancient bronze spoons may be similar to that of modern spoons, and the estimation of the failure mechanisms of ancient spoons can be appropriate to determine failure causes for such modern spoons.

• 보존과학회지
• /
• 제34권6호
• /
• pp.493-502
• /
• 2018

현재 유기공방에서는 전통기술로 하나의 방짜유기 숟가락을 만들기 위해 10단계의 작업 공정을 거쳤으며, 형태 제작에 큰 영향을 주는 열간 단조는 3~4단계의 과정을 거친다. 열간 단조를 통해 방짜유기 숟가락의 미세조직은 수지형상의 ${\alpha}$상이 미세화되고 잘게 분산되었으며, 두드림이 가해진 부분의 ${\alpha}$상에는 쌍정이 생성되었다. 또한 ${\alpha}$상은 가해지는 망치질에 따라 점점 다각형에서 원형으로 변형되었다. 이 과정에서 서로 근접한 ${\alpha}$상은 합쳐지는 현상이 발생하였고, 담금질 후에도 합쳐진 상태로 존재하였다. 이처럼 여러 개의 ${\alpha}$상이 합쳐진 미세조직은 방짜조성의 청동유물에서도 관찰되는 것으로 기술체계의 연관성을 보여준다. 방짜조성의 Cu-22%Sn 합금을 대상으로 실시한 열간 단조 실험결과, 주조 당시 형성된 수지상의 감소율은 가공횟수에 따라 비례했으며, 두드림 작업에 의한 결정립의 미세화는 재질의 강도를 높이는 효과를 준 것으로 판단된다. 고대 유적에서 출토된 청동유물과 전통 유기공방에서 만든 방짜유기에서 동일하게 관찰되는 메자국은 문헌으로 남아 있지 않은 고대의 방짜유기 기술체계가 오늘날의 방짜유기 전통기술로 전승되었음을 보여준다.