• Journal of the Korean Magnetics Society
• /
• v.25 no.3
• /
• pp.67-73
• /
• 2015

This is a basic research for improving soft magnetic property of Fe based nano crystalline alloy powder core. The main study is done around characteristics of permeability, core loss, and DC bias depending on amount of insulation coating agent and particle size. First, $Fe_{73.5}Si_{13.5}B_9Nb_3Cu_1$ amorphous alloy ribbon was fabricated by using the planar flow casting (PFC) device. Then, heat treatment and ball milling were done to obtain alloy powder. The amount of polyether imide (PEI) added to it was varied by 0.5, 1.0, 2.0, 2.5 wt% to have compression molding into $16ton/cm^2$. After going through crystalline heat treatment, the made toroidal nano crystalline powder core ($OD12.7mm^*ID7.62mm^*H4.75mm$) had smaller permeability as amount of insulation coating agent decreases. However, it was found out that core loss and DC bias characteristics have been improved. The reason for this results were expected to be because green density of power core decreases as amorphous alloy powder particles become smaller as amount of alloy powder insulation coating agent increases, it was determined that 1 wt% of insulation coating agent is appropriate. Also, for powder core made based on alloy powder size with amount of insulation coating agent fixed at 1 wt%, effective permeability and core loss were outstanding as particle size became bigger. However, characteristics of DC bias became worse as applied DC field increases. This is expected to be due to insulation effect, residual pores, or molding density of powder core resulting from thickness of coating on surface of alloy powder.

• Journal of the Korean Magnetics Society
• /
• v.7 no.4
• /
• pp.180-185
• /
• 1997

Variations of core loss and coercivity with heat treatment condition have been studied in amorphous ribbon core specimens. All measurements were performed at 10 kHz with a maximum induction of 0.1 T. With increasing annealing time, both core loss and coercivity of core specimens decreased first, reaching minimum values, and increased thereafter. Specimen heat treated in an air showed better soft magnetic properties than those treated in Ar atmosphere. The specimens annealed under magnetic field higher than 6 Oe in radial direction showed reduced core loss and coercivity. The field annealing effects were increased with increasing cooling rate near Curie temperature of the material. The specimen annealed under an applied field in perpendicular direction of the core showed increased coercivity and decreased permeability.

• Korean Journal of Materials Research
• /
• v.4 no.8
• /
• pp.847-854
• /
• 1994

An amorphous single phase and coexistent amorphous and hcp-Mg phases in Mg-Zn-Ce system were found to form in the composition ranges of 20 to 40% Zn, 0 to 10% Ce and 5 to 20% Zn, 0 to 5% Ce, respectively. A $Mg_{85}Zn_{12}Ce_{3}$ amorphous alloy containing nanoscale hcp-Mg particles was found to form either by melt spinning or by heat treatment of melt -spun ribbon. The particle size of the hcp-Mg phase can be controlled in the range of 4 to 20 nm. The mixed phase alloy prepared thus has a good bending ductility and exhibits high ultimate tensile strength($\sigma_{B}$) ranging from 670 to 930 MPa and fracture elongation($\varepsilon_{f}$) of 5.2 to 2.0%. The highest specific strength($\sigma_{B}$/density =$\sigma_{s}$)$3.6 \times 10^5N \cdot m/kg$. It should be noted that the highest values of flB, US and ？1 are considerably higher than those (690MPa,$2.5 \times 10^5N \cdot m/kg$and 2.5%) for amorphous Mg-Zn-Ce alloys. The increase of the mechanical strengths by the formation of the mixed phase structure is presumably due to a dispersion hardening of the hcp supersaturated solution which has the hardness higher than that of the amorphous phase with the same composition.

• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.8 no.4
• /
• pp.655-659
• /
• 1998

The effect of quenching speed of melt-spinning on intrinsic coercivity ($_iH_c$$) of annealed ribbons and the crystallization behavior from amorphous $Nd_{14.73}Fe_{78.67}B_{6.60}$ alloy have been studied. We have found that the intrinsic coecivity for annealed melt-spun ribbon is reduced with increasing of quenching rate. $\alpha$-Fe and $Fe_3B$ were formed as intermediate phases prior to the formation of $Nd_2Fe_{14}B$ phase during crystallization. The $Fe_3B$ is disappeared with crystallization of $Nd_2Fe_{14}B$ phase. But the $\alpha$-Fe phase is retained in fully crystallized ribbon by annealing. The intrinsic coercivity loss of annealed ribbon with increasing of quenching speed is believed to be due to existence of soft magnetic phase $\alpha$-Fe in annealed ribbons.

• Journal of the Korean Magnetics Society
• /
• v.2 no.2
• /
• pp.91-98
• /
• 1992

In a $Co_{67}Fe_{4.5}Nb_{2}Si_{10}B_{15}$ amorphous alloy ribbon the effect to two-step annealing on the soft magnetic properties has been studied. By two-step annealing method which the second annealing at low temperature of $310^{\circ}C$ for 2 hours is undertaken after the primary annealing at high temperature above $480^{\circ}C$ for 20 minutes at the vacuum state, the coercive force and the squareness are not changed nearly but the initial permeability at d.c. and the effective permeability at a.c. are remark-ably increased compared with the one-step annealing. The maxima of the initial permeability and the effective permeability at 1 kHz after the two-step annealing are 290,000 and 41,000, respectively, which are 30% higher than those of the one-step annealing. The change of magnetic properties with annealing temperature is discussed in terms of the residual stress, the domain size, the cluster and the crystalline phase.

• Transactions of the Korean Society of Mechanical Engineers B
• /
• v.25 no.10
• /
• pp.1365-1372
• /
• 2001

In the planar flow casting(PFC) process, the conditions of the melt puddle between nozzle and rotating wheel affect significantly the quality and dimensional uniformity of the downstream ribbon. For stable puddle formation, the nozzle is placed very close to the quenching wheel, so the surface-tension and wall-adhesion forces have an important effect upon the fluid flow.\`In this study the planar flow casting process has been mode]ed using the VOF method for free surface tracking. The transient puddle formation from the present analysis shows good agreements with the previous experimental results. Furthermore, the variation of melt temperature and the corresponding cooling rate of the melt have been examined. The present results also show how the melt puddle can be farmed on the rotating substrate, how the melt flows within the puddle, and how the changes of the process variables affect the puddle formation and its corresponding fluid flow and heat transfer behavior.

• Journal of Powder Materials
• /
• v.13 no.5 s.58
• /
• pp.327-335
• /
• 2006

In the development of new hydrogen absorbing materials for a next generation of metal hydride electrodes for rechargeable batteries, metastable Mg-Ni-based compounds find currently special attention. Amor phous-nanocrystalline $Mg_{63}Ni_{30}Y_7$ and $Mg_{50}Ni_{30}Y_{20}$ alloys were produced by mechanical alloying and melt-spinning and characterized by means of XRD, TEM and DSC. On basis of mechanically alloyed Mg-Ni-Y powders, complex hydride electrodes were fabricated and their electrochemical behaviour in 6M KOH (pH=14,8) was investigated. The electrodes made from $Mg_{63}Ni_{30}Y_7$ powders, which were prepared under use of a SPEX shaker mill, with a major fraction of nanocrystalline phase reveal a higher electrochemical activity far hydrogen reduction and a higher maximum discharge capacity (247 mAh/g) than the electrodes from alloy powder with predominantly amorphous microstructure (216 mAh/g) obtained when using a Retsch planetary ball mill at low temperatures. Those discharge capacities are higher that those fur nanocrystalline $Mg_2Ni$ electrodes. However, the cyclic stability of those alloy powder electrodes was low. Therefore, fundamental stability studies were performed on $Mg_{63}Ni_{30}Y_7$ and $Mg_{50}Ni_{30}Y_{20}$ ribbon samples in the as-quenched state and after cathodic hydrogen charging by means of anodic and cathodic polarisation measurements. Gradual oxidation and dissolution of nickel governs the anodic behaviour before a passive state is attained. A stabilizing effect of higher fractions of yttrium in the alloy on the passivation was detected. During the cathodic hydrogen charging process the alloys exhibit a change in the surface state chemistry, i.e. an enrichment of nickel-species, causing preferential oxidation and dissolution during subsequent anodization. The effect of chemical pre-treatments in 1% HF and in $10\;mg/l\;YCl_3/1%\;H_2O_2$ solution on the surface degradation processes was investigated. A HF treatment can improve their anodic passivation behavior by inhibiting a preferential nickel oxidation-dissolution at low polarisation, whereas a $YCl_3/H_2O_2$ treatment has the opposite effect. Both pre-treatment methods lead to an enhancement of cathodically induced surface degradation processes.

• Journal of Powder Materials
• /
• v.28 no.4
• /
• pp.293-300
• /
• 2021

We investigate the effect of phosphorous content on the microstructure and magnetic properties of Fe_83.2Si_5.33-0.33xB_10.67-0.67xP_xCu_0.8 (x = 1-4 at.%) nanocrystalline soft magnetic alloys. The simultaneous addition of Cu and P to nanocrystalline alloys reportedly decreases the nanocrystalline size significantly, to 10-20 nm. In the P-containing nanocrystalline alloy, P atoms are distributed in an amorphous residual matrix, which suppresses grain growth, increases permeability, and decreases coercivity. In this study, nanocrystalline ribbons with a composition of Fe_83.2Si_5.33-0.33xB_10.67-0.67xP_xCu_0.8 (x = 1-4 at.%) are fabricated by rapid quenching melt-spinning and thermal annealing. It is demonstrated that the addition of a small amount of P to the alloy improves the glass-forming ability and increases the resistance to undesirable Fe_x(B,P) crystallization. Among the alloys investigated in this work, an Fe_83.2Si₅B₁₀P₁Cu_0.8 nanocrystalline ribbon annealed at 460℃ exhibits excellent soft-magnetic properties including low coercivity, low core loss, and high saturation magnetization. The uniform nanocrystallization of the Fe_83.2Si₅B₁₀P₁Cu_0.8 alloy is confirmed by high-resolution transmission electron microscopy analysis.