• Journal of Power System Engineering
• /
• v.17 no.2
• /
• pp.78-86
• /
• 2013

In this research, dilute colloidal suspension alumina nanofluids were prepared by dispersing alumina nanoparticles in DI water and ethylene glycol as base fluids. Particle size analyzer and TEM test results revealed that the size of the alumina nanofluids(3wt% and 5wt%) with dispersion time 3hrs were 46nm and 60nm respectively. Thermal conductivity of these alumina nanofluids was measured by means of hot wire technique using a LAMBDA system. For water based alumina nanofluids, thermal conductivity enhancement was from 2.29% to 3.06% with 5wt% alumina at temperatures ranging from 15 to $40^{\circ}C$. Whereas in case of ethylene glycol based alumina nanofluids under the same temperature range, thermal conductivity enhancement was from 9.6% to 10% with 5wt% alumina. An enhancement of 37% average convective heat transfer was achieved with 5wt% alumina nanofluids at Re of 1,100.

• Journal of the Korean Ceramic Society
• /
• v.25 no.5
• /
• pp.465-472
• /
• 1988

Alpha alumina powder with fine particle size and narrow particle size distribution was prepared by precipitation method using Al2(SO4)3.18H2O as a starting material. The alpha alumina powder was prepared by calcining aluminum hydroxide which was formed under various pH values. The sinterabilityof alpha alumina powder and the effect of MgO on the sinterability of alpha alumina powder were investigated. The sinterability of alpha alumina powder was the order of pH=10≒pH11>pH=7≒pH9, and alpha alumina obtained from boehmite which was prepared by precipitation method reached to 97.5% of theoretcal density by the pressureless sintering. The effect of MgO on volume shrinkage of alumina was very slight in the initial sintering stage but remarkable in the final sintering stage. It was also found that MgO controlled effectively the grain growth of alumina.

• Journal of the Korean Ceramic Society
• /
• v.51 no.5
• /
• pp.406-412
• /
• 2014

In this study, flat-tubular-type alumina filters were manufactured using alumina powder of two sizes ($2.4{\mu}m$ ALM-44 and $0.4{\mu}m$ AP 400) by an extrusion process. The manufactured alumina filter was sintered at $1200-1600^{\circ}C$ for 1 h. As particle size increased, the largest pore size, average pore size and porosity increased; but density and linear shrinkage decreased. The alumina filter fabricated using ALM-44 powder sintered at $1500^{\circ}C$ was confirmed as the best water treatment filter after investigation of the bending strength, water permeability and impurity-removal efficiency of the experimental filters. This flat-tubular-type alumina filter is expected to be useful not only for direct water treatment, but also for use as a support filter during coating processes, to control pore size.

• Journal of the Korean Ceramic Society
• /
• v.36 no.6
• /
• pp.662-670
• /
• 1999

Porous alumina was fabricated from pressureless powder packing forming method using powders granulated by spray drying. It was investigated the pore size distribution of fabricated porous alumina. The results of microstructural observation showed that intraganular pore size and intragranular pore size. At 1700$^{\circ}C$ there were no intragranular pores but it showed homogeneous distribution of intergranular pore size. The bending strength and shrinkage increased as porosity decreased. In case of thermal shock resistance sudden decrease of bending strength to $\Delta$T was not shown because intergranular large pore prevented sudden crack propagation.

• Bulletin of the Korean Chemical Society
• /
• v.23 no.8
• /
• pp.1127-1134
• /
• 2002

Fine ceramic particles of zirconia toughened alumina (ZTA), titania toughened alumina (TTA), and zirconia-titania toughened alumina (ZTTA) have been synthesized by ultrasonic spray pyrolysis (USP) at various temperatures from starting salt solutio ns of various compositions aiming for the development of catalytic material. These particles were characterized for properties such as shape, size and size distribution, diffraction pattern, and chemical and phase composition of elements by scanning electron microscopy (SEM), particle size analyzer (PSA), x-ray diffraction (XRD), and inductively coupled plasma-atomic emission spectroscopy (ICP-AES). Chemical compositions and sizes of ceramic composites have been controled by the stoichiometry of salt solutions and the flow rate of spraying solutions. The optimum experimental conditions for the various composite particle syntheses have been proposed.

• The Journal of Korean Academy of Prosthodontics
• /
• v.31 no.3
• /
• pp.317-349
• /
• 1993

This study investigated the effect of filler particle size and weight% on mechanical properties of dental core porcelain. In alumina, variation in particle size and weight% and in zirconia, variation in weight%, all specimens were tested three-point bending strength, transmittance, thermal expansion coefficient, porosity and shrinkage and observed with SEM and analysed with X-ray diffractometer. In order to develop shrink-free porcelain, after firing alumina only, glass wasinfiltrated. And aluminum was added to alumina with the expanding character of aluminum oxidize into alumina, and was followed by second firing of glass infiltration procedure. Then mechanical properties were observed. The results of this study were obtained as follows. 1. The bending strength of zirconia was higher than that of alumina, and $5{\mu}m$ alumina had highest strength in variation of particle size of alumina. Except for $5{\mu}m$ alumina, increased with weight%, bending strength increased up to 80% and decreased at 90%. In case of glass infiltration, bending strength was slight higher than 80% and 90% of $5{\mu}m$ alumina. 2. Transmittance increased with increase of shrinkage, decrease of porosity, and with increase of filler size and had no direct correlation with weight%. 3. Thermal expansion coefficient of alumina group was $7.42\sim8.64\times10^{-6}/^{\circ}C$ and that of zirconia group was $9.83\sim12.11\times10^{-6}/^{\circ}C$ and the latter was higher than the former. 4. In x-ray diffraction analysis, alumina group and zirconia group increased $Al_2O_3$ peak and $t-ZrO_2$ peak with increase of weight%. The second phase(cristobalite peak) was observed in zirconia 40% group. 5. Porosity of zirconia was lower than that of alumina and $5{\mu}m$ alumina group had many pores with SEM. In case of low filler content, fracture occurred in glass and high filler content, in glass and filler. In case of aluminum addition to alumina, small oxidised aluminum was observed. 6. Zirconia group had high shrinkage than alumina group, and mixed group of alumina group had high shrinkage. In case of glass infiltration, shrinkage decreased and aluminum addition to alumina group was almost shrink-free.

• Journal of the Korean Ceramic Society
• /
• v.36 no.7
• /
• pp.718-724
• /
• 1999

Densification and grain growth behavior of bimodal size distributed alumina powder mixtures were investigated as a function of amount of coarse alumina powder. The specimens which contained coarse alumina powder for 60to 80wt% showed the highest green density. The amount of shrinkage of sintered specimen lineraly decreased with the increase of coarse alumina powder up to the content that showed the highest green density and then further addition of coarse alumina powder led to drastic decrease of shrinkage of specimen. Especially crack-like void were concurrently revealed in the sintered body with addition of coarse alumina powder above 60wt% When the sintering temperature increased up to 1650$^{\circ}C$ the amount of shrinkage of specimen linearly decreased and the grain growth were also retarded with increase of coarse lauminia powder.

• Journal of the Korean Ceramic Society
• /
• v.31 no.1
• /
• pp.1-10
• /
• 1994

Monodispersed alumina and Mg-doped alumina fine particles were prepared by controlled hydrolysis of alkoxides. Aluminium alkoxide and magnesium alkoxide were dissolved into complex solvent which was composed of hydrophobic n-octanol and hydrophilic acetonitrile. Hydroxypropyl cellulose(HPC) was used as a dispersant for the alumina particles. The size of these prepared powders was approximately 0.3 ${\mu}{\textrm}{m}$. In the case of sintering above 100$0^{\circ}C$, most of these prepared powders were transformed to $\alpha$-alumina. The relative density of the sintered body of these prepared powders at 1$600^{\circ}C$ was 98%. The sintered body of the Mg-doped alumina powder had more uniform grain size than that of the undoped alumina podwer.

• Journal of the Korean Ceramic Society
• /
• v.46 no.3
• /
• pp.306-312
• /
• 2009

The size of various alumina ceramics used in semiconductor and display industry is also required to increase with increase in wafer and panel size. In this research, large alumina ceramics was fabricated by filter pressing of alumina slurry using commercial powder and thereafter sintering at $1600^{\circ}C$ in gas furnace. The characteristics of large alumina ceramics thereby were compared to those of small alumina ceramics prepared by pressure forming such as uniaxial pressing and CIP. Careful control of properties of alumina slurry and filter pressing made the fabrication of large alumina ceramics possible, and its characteristics were equivalent to those of small alumina ceramics. The large alumina ceramics, prepared by sintering the green body of 63% relative density at $1600^{\circ}C$, exhibited both dense microstructure corresponding to 98.5% of relative density and 99.8% of high purity as in starting powder.

• Fire Science and Engineering
• /
• v.11 no.3
• /
• pp.15-23
• /
• 1997

In this study, the alumina for gas sensor was prepared by anodic oxidation. It was stable thermally and chemically, and pore diameter and pore distribution was uniform. And the shape of pore was cylinderical. The aluminum plate was carried out by the thermal oxidation, chemical polishing and electropolishing pretreatment. The pore diameter, pore size distribution, pore density and thickness of alumina was observed with the change of reaction temperature, electrolyte concentration and current density. As a results, It was able to use for carrier because alumina which was prepared by anodic oxidationhas uniform pore size distribution.