• Journal of Korea Foundry Society
• /
• v.20 no.4
• /
• pp.247-253
• /
• 2000

Titanium was melted in the CaO-coated alumina crucible and the reaction between the melt and the coating layer was negligible. The volume fraction of the gas porosity was decreased with increasing pressure and the sound bar castings with no porosity was obtained under the Ar atmosphere of the pressure of $300kN/mm^2$. The surface of the casting obtained from CaO-coated graphite mold was slightly rougher than that from graphite without coating. The reaction product of titanium melt with the layer of CaO was mainly titanium oxide and that with graphite crucible was titanium cabide with small amount of titanium nitride.

• The Korean Journal of Ceramics
• /
• v.1 no.4
• /
• pp.219-223
• /
• 1995

Ceramic membranes of the supported $TiO_2-CeO_2$ were prepared by dip-coating method on an $\alpha-Al_2O_3$ porous substrate. The mean pore diameter of an alumina support was 0.125 um. The mean particle diameter of $TiO_2-CeO_2$ top layer varied with firing temperature and ranged from 20 to 85 nm. The thermal stability of the composite membranes was studied from their surface microstructure after calcination at $600-900^{\circ}C$. The supported $TiO_2-CeO_2$ composite membranes exhibited much higher heat resistance than the $TiO_2$ membrane.

• Proceedings of the Korean Powder Metallurgy Institute Conference
• /
• 2006.09a
• /
• pp.87-88
• /
• 2006

Ceramic-Metal Functionally Graded Materials (FGM) are of great interest for application as Thermal Barrier Coating (TBC) or Wear Resistant Coating (WRC). Spark Plasma Sintering (SPS) is a promising techniques for time-saving consolidation of laminated/graduated powder systems: SPS is a pressure-assisted electrical sintering method which directly applies a pulsed DC current as heat source. In the present work, production of $Al_2O_3-Ni$ FGMs by means of Spark Plasma Sintering is considered; effect of sintering condition on density, hardness and fracture toughness is studied. Problems correlated to this new processing technology are discussed.

• Proceedings of the Korean Nuclear Society Conference
• /
• 1997.05b
• /
• pp.159-164
• /
• 1997

Pyrolytic carbon layer was coated on A1203 balls by fluidized bed type chemical vapour deposition unit to develop the coating technology for the preparation of coated nuclear fuel. The deposition was carried out at the temperature ranges between 110$0^{\circ}C$ and 130$0^{\circ}C$ with various gas contents and flow rates. Source and carrier gas were propane and argon, respectively. X-ray analysis shows that the deposition layer was typical carbon spectra. The growth rate of carbon layer depended on the amount of source gas and the deposition temperature. For the alumina balls with 2mm in diameter, the deposition rate was 11${\mu}{\textrm}{m}$/hr in the flow gases containing 30% source gas at 130$0^{\circ}C$ with a total flow rate of 2.0$\ell$/min. Microstructural observation of the deposits with scanning electron microscope revealed that the deposits had relatively dense and isotropic structure. Chemical analysis by energy dispersive spectroscopy showed that the layer was pure carbon.

• Membrane Journal
• /
• v.15 no.2
• /
• pp.105-113
• /
• 2005

Silica membranes were prepared on a porous metal sheet by ultrasonic spray pyrolysis method for gas separation at high temperatures. In order to improve the permselectivity, silica was deposited in the sol-gel derived $silica/\gamma-alumina$ intermediate layer by pyrolysis of tetraethyl orthosilicate (TEOS) at 873 K. The pyrolysis with forced cross flow through the porous wall of the support was very effective in plugging mesopores, Knudsen diffusion regime, that were left unplugged in the membranes. At permeation temperature of 523 K, the silica/alumina composite membrane showed $H_2/N_2$ and water/methanol selectivity as high as 17 and 16, respectively, by molecular sieve effect.

• Analytical Science and Technology
• /
• v.6 no.2
• /
• pp.225-229
• /
• 1993

ATZ was prepared by adding an alumina sol equivalent to 2wt% as $Al_2O_3$ to an aqueous slurry of alumina (AKP-30) and zirconia (TZ-2Y or TZ-0Y) in the range of 10-30ATZ, followed by gelation, calcination, and sintereing between $1450^{\circ}C{\sim}1550^{\circ}C$ for 2h. They showed excellent microstructure with alumina grains of <$0.5{\mu}m$ and>99% of the theoretical density. Fracture toughness of ${\sim}8MPa{\cdot}m^{1/2}$ was observed around 20ATZ which was higher than $6MPa{\cdot}m^{1/2}$ obtainable by ball-milling.

• Journal of the Korean Ceramic Society
• /
• v.52 no.5
• /
• pp.366-373
• /
• 2015

Sol-gel binder was prepared by hydrolysis and condensation reaction using boehmite sol and methyltrimethoxysilane as a function of aging-time. The coating slurry was composed of a plate-shape alumina in the sol-gel binder for the EPD process, in which particles dispersed in the slurry were deposited on the electrode under an electric field due to the surface charge. We studied the effects of three parameters: the content of boehmite, the aging time, and the applied voltage, on the physical, thermal, and electrical properties of the hybrid composite films by EPD. The amount of boehmite was 10 ~ 20 wt% and the aging time was 0.5 ~ 72, with a fixed amount of plate-shape alumina of 10 wt%. The condition of applied voltage was 5 ~ 30 V with a distance of 2 cm between the electrode during the EPD process. We confirmed that a structure of hybrid composite films of well-ordered plate alumina was deposited on the substrate when the film was prepared using a sol-gel binder composed of 15 wt% boehmite with 1 hr aging time and EPD at 10 V. The process shows a weight loss of 7% at $500^{\circ}C$ in TGA and a breakdown voltage of 8 kV at $87{\mu}m$.

• 한국연소학회:학술대회논문집
• /
• 2006.10a
• /
• pp.235-241
• /
• 2006

Catalytic combustion is one of the suitable methods for micro power source due to high energy density and no flame quenching. Catalyst loading in the micro structured combustion chamber is one of the most important issues in the development of micro catalytic combustors. In this research, to coat catalyst on the chamber wall, two methods were investigated. First, $Al_2O_3$ was selected as a support of Pt and $Pt/Al_2O_3$ was synthesized through the alumina sol-gel procedure. To improve the coating thickness and adhesion between catalyst and substrate, heat resistant and water solvable organic-inorganic hybrid binder was used. Porous silicon was also investigated as a catalyst support for platinum. Through the parametric studies of current density and etching time, fabrication process of $1{\sim}2{\mu}m$ of diameter and about $25{\mu}m$ depth pores was confirmed. Coated substrates were test in the micro channel combustor which was fabricated by the wet etching and machining of SUS 304. Using $Pt/Al_2O_3$ coated substrate and Pt coated porous silicon substrate, conversion rate of fuel was over 95% for $H_2$/Air premixed gas.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2006.11a
• /
• pp.35-36
• /
• 2006

The influence of the concentration of precursor solution and the number of solution coatings on the densification of the Pb($Zr_xTi_{1-x}$)$O_3$(PZT) thick films was studied. PZT powder and PZT precursor solution were prepared by sol-gel method and PZT thick films were fabricated by the screen-printing method on the alumina substrates. The powder and solution of composition were PZT(70/30) and PZT(30/70), respectively. The coating and drying procedure was repeated 4 times. And then the PZT precursor solution was spin-coated on the PZT thick films. A concentration of a coating solution was 0.5 to 2.0 mol/L[M] and the number of coating was repeated from 0 to 6. The relative dielectric constant of the PZT thick film was increased with increasing the number of solution coatings and the thick films with 15M, 6-time coated showed the 698. The remanent polarization of the 1.5M, 6-time coated PZT thick films was 38.3 ${\mu}C/cm^2$.

• Journal of the Korean Ceramic Society
• /
• v.28 no.4
• /
• pp.338-346
• /
• 1991

The alumina-titania composite powders coated with Al2O3 were prepared by the method of hydrolysis-deposition of mixed aluminium salt solution of Al2(SO)4-Al(NO3)3-Urea. The effects of coating-process parameters on the characteristics of coated composite powders were also investigated. As the content of TiO2 dispersed in deionized water increased, the coated composite powders were found to be more uniform in size and unagglomerated. When TiO2 powders were coated for 30 min, the optimum TiO2 content in the coating process was 400 mg/ι. The size of TiO2 particle was increased approximately from 0.7${\mu}{\textrm}{m}$ to 1.0${\mu}{\textrm}{m}$ through coating of Al2O3. The IEP of coated composite powders was pH=8.3 identical to the value of aluminium hydroxides and the zeta-potential showed nearly similar values each other. When heat treating coated composite powders at 130$0^{\circ}C$, only two phases of TiO2(rutile) and Al2TiO5 were observed. These results showed that the suface of TiO2 could be uniformly coated with the aluminium hydroxide.