• 한국전기전자재료학회:학술대회논문집
• /
• 한국전기전자재료학회 2010년도 하계학술대회 논문집
• /
• pp.298-298
• /
• 2010

In this study, both structural, dielectric properties of the NKN-0.94BNT-0.06BT ceramics were investigated. All samples of the NKN-0.94BNT-0.06BT ceramics were fabricated by conventional mixed oxide method with Pt electrodes. We report the improved electrical properties in the perovskite structure composed of the NKN, BNT and the BT ceramics. We investigated the effects of NKN, BT on the structural and electrical properties of the NKN-0.94BNT-0.06BT ceramics. The dielectric and structural properties of the NKN-0.94BNT-0.06BT ceramics were superior to those of single composition NKN, NKN-BNT and those values for the NKN-0.94BNT-0.06BT ceramics were 1455, 0.025 and $29.04{\mu}C/cm^2$.

• 한국세라믹학회지
• /
• 제50권3호
• /
• pp.180-185
• /
• 2013

We investigated the characteristics of hot-pressed pure yttria ceramics, and annealed them in an oxidation atmosphere. Regardless of the heat treatment in the oxidation atmosphere, XRD analysis showed that all the samples had a $Y_2O_3$ phase without structural change. Even though the color variation of the hot-pressed $Y_2O_3$ ceramics was due to the sintering temperatures, the oxidation process turned the color of the $Y_2O_3$ ceramics into white. The color change during oxidation treatment appears to be related to oxygen defects. In addition, oxygen defects also affected the weight change and microstructure of the $Y_2O_3$ ceramics. The $Y_2O_3$ ceramic sintered at $1600^{\circ}C$ had a $5.03g/cm^3$ density, which is close to the theoretical density of $Y_2O_3$. As the sintering temperature increased, small homogeneous grains grew to large grains which affected the Vickers hardness. $Y_2O_3$ ceramics hot-pressed at $1600^{\circ}C$ and annealed at $1200^{\circ}C$ had a flexural strength of 140MPa.

• 대한전기학회논문지:전기물성ㆍ응용부문C
• /
• 제51권8호
• /
• pp.335-339
• /
• 2002

Ba(Mgl-xCox)TaO3[BMCT] ceramics were prepared by the conventional mixed oxide method. The ceramics were sintered at the temperature of 1525~$1625^{\circ}C$ for 5hr. in air. The crystal structure of BMCT ceramics was investigated by the XRD. The microstructure of the specimens were observed by SEM. The Microwave dielectric properties of BMCT specimens were investigated as a function of composition and sintering temperature. All BMCT ceramics sintered over 1575$^{\circ}C$ were showed a polycrystalline complex perovskite structure. The density of BMCT (90/10) specimen sintered at $1575^{\circ}C$ was 7.75g/㎤. As the Co contents decreased, the ordering parameter of B-site in BMCT increased. In the case of the BMCT(90/10) ceramics sintered at $1575^{\circ}C$ for 5 hours, dielectric constant, quality factor and temperature coefficient of resonant frequency for microwave dielectrics application were a good value o( 25, 17, 845 at 10㎓ and +2.4 ppm/${\circ}$, respectively.

• 대한전기학회:학술대회논문집
• /
• 대한전기학회 2006년도 추계학술대회 논문집 전기물성,응용부문
• /
• pp.20-21
• /
• 2006

In this study, structural and microwave dielectric properties of the ${Ba_5}{B_4}{O_{15}}$ (B=Ta, Nb} cation-deficient perovskite ceramics with sintering temperature were investigated. All sample of the ${Ba_5}{B_4}{O_{15}}$ (B=Ta, Nb) ceramics prepared by conventional mixed oxide method and sintered at $1325^{\circ}C{\sim}1575^{\circ}C$. The bulk density and dielectric constant of the ${Ba_5}{Ta_4}{O_{15}}$ ceramics were increased continuously with increasing of sintering temperature. And the bulk density and dielectric constant of the ${Ba_5}{Nb_4}{O_{15}}$ ceramics was increased in $1375^{\circ}C{\sim}1400^{\circ}C$ but decerased in $1425^{\circ}C$. In the case of ${Ba_5}{Ta_4}{O_{15}}$ ceramics sintered at $1475^{\circ}C$ and ${Ba_5}{Nb_4}{O_{15}}$ ceramics sintered at $1400^{\circ}C$, The dielectric constant and quality factor, and temperature coefficient of the resonant frequency (TCRF) were 25.15, 53,105 GHz, $-3.06\;ppm/^{\circ}C$ and, 39.55, 28,052 GHz, $5.7\;ppm/^{\circ}C$ respectively.

• Journal of the Korean Wood Science and Technology
• /
• 제52권3호
• /
• pp.234-242
• /
• 2024

In this study, the effect of carbonization temperature and mixing ratio of ceramics manufactured from sawdust, chaff and charcoal on sound absorption performance and density profile was investigated. The density profile of ceramics prepared by the addition rates of sawdust, chaff and charcoal showed the highest value at 91.00% when the ratio of sawdust, chaff and charcoal was 50:25:15. However, the difference in density profile according to the addition rate was insignificant. The density profile of ceramics manufactured according to the carbonization temperature showed the highest value of 88.06% when manufactured at 800℃. However, it does not show any particular trend, so it is understood that the effect of the carbonization temperature on the density gradient is small. On the other hand, the sound absorption coefficients of ceramics prepared by the addition rates of sawdust, chaff and charcoal is between 0.3 and 0.4 at almost all frequencies when the addition rates of sawdust, chaff and charcoal are 50:30:10 and 50:35:5, respectively. Therefore, as the chaff particles increased, the sound absorption performance was improved. In addition, the sound absorption coefficients of the ceramics manufactured at each carbonization temperature showed the highest value in the ceramics manufactured at 1,200℃.

• 한국전기전자재료학회:학술대회논문집
• /
• 한국전기전자재료학회 2001년도 하계학술대회 논문집
• /
• pp.153-156
• /
• 2001

(Ba$_{0.6-x}$Sr$_{0.4}$Ca$_{x}$)TiO$_3$ (x=0.10, 0.15, 0.20) ceramics were fabricated by the mixed-oxide method and their dielectric properties were investigated with variation of composition ratio, doped ZrO$_2$ (0.5, 1.0, 1.5, 2.0, 3.0 wt%) and sintered at 145$0^{\circ}C$. The dielectric constant and loss of the x=0.10 specimen applied field were 19.86 and 0.302 % at 0 V/cm, and 25.937 and 0.339 % at 300 V/cm, respectively. Dielectric constant were increased with increased applied field and decreased with increased frequency, and dielectric loss were within 0.1% at applied 800 MHz, respectively. all specimens showed fairly good applied field. Although, dielectric constant and loss of all specimen showed to tend of nearly the same. same.

• 한국결정성장학회지
• /
• 제18권6호
• /
• pp.242-247
• /
• 2008

$Fe_2O_3$, ZnO 등이 주성분인 EAF dust를 $30{\sim}70\;wt%$ 첨가한 규산염계 유리 및 결정화유리를 제조하고, 시편내부에 생성된 상 및 미세구조와 물리적 특성과의 관계를 고찰하였다. 또한 제조된 유리와 결정화유리의 결정화 거동을 상분석 및 미세구조 관찰을 통하여 분석하였다. EAF dust가 30 wt% 첨가된 용융체의 경우 전형적인 비정질 XRD 패턴을 나타냈으며, 그 이상 첨가된 용융체에는 미용해 된 결정상이 일부 존재하였다. 모든 결정화유리에서는 franklinite, willemite 그리고 augite 결정상이 형성되었다. 결정화유리의 비중은 같은 조성의 유리에 비하여 높았고, EAF dust 함량에 따라 함께 증가하였다. 또한 결정화 유리의 열적 및 기계적 특성이 유리보다 우수하게 나타났다. 즉 유리는 EAF dust 첨가량과 함께 열팽창 계수가 증가하였으나 결정화유리에서는 반대로 감소하였다. 또한 EAF dust 첨가량에 따라 비커스 경도는 유리 및 결정화유리 모두 증가되었으며 같은 조성에서 결정화 유리의 경도값이 항상 더 높게 나타났다.

• 한국환경과학회지
• /
• 제27권2호
• /
• pp.109-122
• /
• 2018

This study was conducted to investigate the removal characteristics of heavy metals and sulfate ion from acid mine drainage by porous zeolite-slag ceramics (ZS ceramics) that was prepared by adding wood flour as pore-foaming agent while calcining the mixtures of natural zeolite and converter slag. The batch test showed that the removal efficiency of heavy metals by pellet-type porous ZS ceramics increased as the particle size of wood flour was decreased and as the weight mixing ratio of wood flour to ZS ceramics was increased. The optimal particle size and weight mixing ratio of wood flour were measured to be $75{\mu}m$ and 7~10%, respectively. The removal test with the porous ZS ceramics prepared in these optimal condition showed very high removal efficiencies: more than 98.4% for all heavy metals and 73.9% for sulfate ion. Relative to nonporous ZS ceramics, the increment of removal efficiency of heavy metals by porous ZS ceramics with $75{\mu}m$ and 10% wood flour was 5.8%, 60.5%, 36.9%, 87.7%, 10.3%, and 57.4% for Al, Cd, Cu, Mn, Pb, and Zn, respectively. The mechanism analysis of removal by the porous ZS ceramics suggested that the heavy metals and sulfate ion from acid mine drainage are eliminated by multiple reactions such as adsorption and/or ion exchange as well as precipitation and/or co-precipitation.

• The Journal of Advanced Prosthodontics
• /
• 제5권3호
• /
• pp.262-269
• /
• 2013

PURPOSE. Perceived color of ceramics changes by the spectral power distribution of ambient light. This study aimed to quantify the amount of shifts in color and color coordinates of clinically simulated seven all-ceramics due to the switch of three ambient light sources using a human vision simulating spectroradiometer. MATERIALS AND METHODS. CIE color coordinates, such as $L^*$, $a^*$ and $b^*$, of ceramic specimens were measured under three light sources, which simulate the CIE standard illuminant D65 (daylight), A (incandescent lamp), and F9 (fluorescent lamp). Shifts in color and color coordinate by the switch of lights were determined. Influence of the switched light (D65 to A, or D65 to F9), shade of veneer ceramics (A2 or A3), and brand of ceramics on the shifts was analyzed by a three-way ANOVA. RESULTS. Shifts in color and color coordinates were influenced by three factors (P<.05). Color shifts by the switch to A were in the range of 5.9 to 7.7 ${\Delta}E{^*}_{ab}$ units, and those by the switch to F9 were 7.7 to 10.2; all of which were unacceptable (${\Delta}E{^*}_{ab}$ > 5.5). When switched to A, CIE $a^*$ increased (${\Delta}a^*$: 5.6 to 7.6), however, CIE $b^*$ increased (${\Delta}b^*$: 4.9 to 7.8) when switched to F9. CONCLUSION. Clinically simulated ceramics demonstrated clinically unacceptable color shifts according to the switches in ambient lights based on spectroradiometric readings. Therefore, shade matching and compatibility evaluation should be performed considering ambient lighting conditions and should be done under most relevant lighting condition.

• Transactions on Electrical and Electronic Materials
• /
• 제10권4호
• /
• pp.121-124
• /
• 2009

In this study, in order to develop compositions of ceramics suitable for piezoelectric actuator and ultrasonic vibrator applications using low temperature sintering, multilayer, PMN-PNN-PZT ceramics were fabricated using $Li_2CO_3$ and $Na_2CO_3$ as sintering aids. Their structural, piezoelectric and dielectric characteristics were investigated according to the Zr/Ti ratio. As the Zr/Ti ratio increased, the electromechanical coupling factor $k_p$, and piezoelectric constant $d_{33}$ and the mechanical quality factor $Q_m$ all increased with Zr/Ti ratio and then decreased after the ratio exceeded 50/50. At the ratio of Zr/Ti =49/51 and sintering temperature of $900^{\circ}C$; the density, electromechanical coupling factor $k_p$, dielectric constant ${\varepsilon}_r$ piezoelectric $d_{33}$ constant and mechanical quality factor $Q_m$ all showed the optimum values of 7.900 $g/cm^3$, 0.576, 856, 312 pC/N, 1,326, respectively. These property values are very suitable for multilayer ceramics actuator applications.