• Journal of the Korean Ceramic Society
• /
• v.26 no.1
• /
• pp.31-36
• /
• 1989

In order to synthesize AlN-polytypes from AlN-SiO2-Al2O3 system, composition A (AlN/SiO2/Al2O3=1/0.3/0.05, mole ratio) and composition B(AlN-SiO2-Al2O3=1/0.2/0.05, mole ratio) were used. AlN-polytypes were produced by nitriding the mixture at 175$0^{\circ}C$~190$0^{\circ}C$ under N2 atmosphere. For lower reaction temperature, 15R phase was produced and in the case of higher reaction temperature, AlN phase was only produced. As each composition was heated at 185$0^{\circ}C$ in N2 atmosphere, produced main phases were 15R phase for composition A and 21R phase for composition B respectively. The fracture surfaces of produced reactants showed porous skeleton structure.

• Journal of the Korean Ceramic Society
• /
• v.29 no.6
• /
• pp.419-430
• /
• 1992

Fabrication possibility of low-shrinkage alumina without oxidation and wetting agent was presented on the basis of observation about oxidation behavior, microstructure and physical characteristics of such reaction agents free Al2O3-Al system. The composition less than Al 10w/o where Al can act as a sintering agent for Al2O3 was excluded. Under the condition of present experiments oxidation of Al2O3-Al system was dependent not on holding time but mainly on oxidation temperature. In thes case of Al powder not comminuted effectively during powder mixing of Al2O3-Al, columnar structure which would act as a hindrance to the densification during sintering developed more during oxidation with higher Al contents, and which made the fabrication of low-shrinkage Al2O3 ceramics impossible. If Al powder was comminuted effectively due to co-mixed Al2O3 characteristics, densification was improved because of no columnar structure and made the fabrication of sintered body with -2.7% dimensional change and 81% relative density possible. As a result, it is possible to fabricate dense low-shrinkage Al2O3 ceramics without oxidation and wetting agent under conditions such as smaller particle size of Al, Al contents below 50v/o, higher green density of Al2O3-Al compact and the use of Al2O3 powder used for high-density ceramics.

• Journal of the Korean Ceramic Society
• /
• v.28 no.1
• /
• pp.11-18
• /
• 1991

A precipitation method, one of the most effective liquid phase reaction methods, was adopted in order to prepare high-tech Al2O3/ZrO2 composite ceramics, and the effects of stress-induced phase transformation of ZrO2 on thermal shock behavior of Al2O3-ZrO2 ceramics were investigated. Al2(SO4)3.18H2O, ZrOCl2.8H2O and YCl3.6H2O were used as starting materials and NH4OH as a precipitation agent. Metal hydroxides were obtained by single precipitation(process A) and co-precipitation(process B) method at the condition of pH=7, and the composition of Al2O3-ZrO2 composites was fixed as Al2O3-15v/o ZrO2(+3m/o Y2O3). Critical temperature difference showing rapid strength degradation by thermal shock showed higher value in Al2O3/ZrO2 composites(process A : 20$0^{\circ}C$, process B : 215$^{\circ}C$) than in Al2O3(175$^{\circ}C$). The improvement of thermal shock property for Al2O3/ZrO2 composites was mainly due to the increase of strength at room temperature by adding ZrO2. The strength degradation was more severe for the sample with higher strength at room temperature. Crack initiation energies by thermal shock showed higher values in Al2O3/ZrO2 composites than in Al2O3 ceramics due to increase of fracture toughness by ZrO2.

• Journal of the Korean Ceramic Society
• /
• v.36 no.4
• /
• pp.410-416
• /
• 1999

The reactivity of three kinds of spinels which CaO-Al2O3-SiO2 slag was investigated in terms of mineral phases and microstructures. New crystal products were not formed by reaction of 12CaO.7Al2O3 in the slag with spinels and free MgO components was preferenctially dissolved into slag for MgO-rich spinel and stoichiometric spinel. Meanwhile mineral phase was changed from 12CaO.7Al2O3 to CaO.Al2O3 to CaO.2Al2O3 finally to CaO.6Al2O3 having high melting point for Al2O3 -rich spinel. The Fe-oxide component of the slag was taken up by only stoichiometric spinel grains within the spinel clinker and the trapped amount of Fe-oxide was independent of MgO content of MgO in spinel clinker the more th resistance to slag corrosion but the less resistance to slag penetration.

• Journal of the Microelectronics and Packaging Society
• /
• v.12 no.3 s.36
• /
• pp.259-265
• /
• 2005

Characteristics of electroplated Ni films and $Ni-Al_2O_3$ composite films, such as yield strength, fracture elongation, and $Al_2O_3$ content, were evaluated as a function of electroplating current density. $Al_2O_3$ content was $11.48\~11.64\;vol\%$ for $Ni-Al_2O_3$ composite films electroplated at $5\~20\;mA/cm^2$, and decreased to $8.41\;vol\%$ at $30\;mA/cm^2$ $Ni-Al_2O_3$ possessed yield strengths higher than those of Ni films. Especially, $Ni-Al_2O_3$ fabricated at $5\;mA/cm^2$ exhibited $50\%$ improved yield strength. Fracture elongations of Ni and $Ni-Al_2O_3$ decreased with increasing the electroplating current density. $Ni-Al_2O_3$ electroplated at $5\;mA/cm^2$ exhibited more uniform dispersion of $Al_2O_3$ and higher yield strength and larger fracture elongation than the composite films processed at other current densities.

• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.8 no.2
• /
• pp.332-341
• /
• 1998

Reaction kinetics for the solid - state reaction of ${\alpha}-Al_2O_3$with amorphous $SiO_2$to produce mullite ($3Al_2O_3;{cdot};2SiO_2$) was studied in the temperature range of 1450~$1480^{\circ}C$. Rate of kinetic reaction were determined by using $SiO_2$- coated $Al_2O_3$ compact containing 28.16 wt.% $SiO_2$and heating the reactant mixtures in MgO at definite temperature for various times. Amount of products and unreacted reactants were determined by X-ray diffractometry. Data from the volume fraction and ratio of peak intensities of mullite indicated that the reaction of ${\alpha}-;Al_2O_3$ with $SiO_2$to form $3Al_2O_3\;{\cdot}\;2SiO_2$ start between 1450 and $1480^{\circ}C$. The activation energy for solid-state reaction was determined by using the Arrhenius equation; The activation energy was 31.9 kJ/mol.

• Journal of the Korean Ceramic Society
• /
• v.34 no.6
• /
• pp.553-560
• /
• 1997

A fine $\alpha$-Al2O3 powder was prepared by sol-gel process for membrane application. And it was carried out by adding 1.5wt% $\alpha$-Al2O3 powders(mean size : 87 nm) as seeds to the prepared sols and by controlling the heating schedule (the heating rate and the soaking time) to prevent the microstructural change, which occured during $\theta$-to $\alpha$Al2O3 phase transformation. The seeded $\alpha$-Al2O3 particles acted as the heterogeneous nucleation sites for the $\alpha$-Al2O3 nucleation during the transformation of $\theta$- to $\alpha$-Al2O3 and resulted in increasing the driving force of phase transformation to activate the formation of $\alpha$-Al2O3 phase at 82$0^{\circ}C$. By $\alpha$-Al2O3 seeding and controlling of heating condition the phase transformation of $\theta$- to $\alpha$-Al2O3 was accomplished at low temperature and the grain growth process was depressed. Therefore, the unsupported membrane could be fabricated in $\alpha$-Al2O3 . The average diameter of pores in the fabricated membrane was 7 nm and the porosity was 47%.

• Journal of the Korean Institute of Telematics and Electronics
• /
• v.27 no.6
• /
• pp.886-894
• /
• 1990

Sinterbility, microstructure, mechenical and electrical properties of yttriastabilized zirkconiz (92 mole % ZrO2 + 8 mole % Y2O3) doped with 0.5 mole % SiO2 and 0-2.O mole% Al2O3 were studied as a functin of Al2O3 addition. Sintered density increased with increasing Al2O3 addition up to o.5 mole%but decreased up to 1.0mole% Al2O3. Vickers hardness is proportional to sintered density. The specimen added 0.5mole% Al2O3 and 0.5mole% SiO2 exhibited a maximum conductivity. And the specimen added 0.5 mole % Al2O3 and 0.5 mole% SiO2 was measured a maximum electromotive force for a characteristics of oxyzen partial pressure.

• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.8 no.1
• /
• pp.97-105
• /
• 1998

Antioxidation mechanism of Al metal powders on $Al_2O_3-C$ refractory was investigated in temperature range from 800 to $1400^{\circ}C$. The addition of 5 wt% Al metal powders suppressed the oxidation of carbon in $Al_2O_3$-C sample. The carbons were distributed uniformly on the surface and the interface of the $Al_2O_3$-C-Al. Reaction products of $Al_4C_3$ and AIN were found with a composition of Al-C at temperatures between 800 and $1200^{\circ}C$ and transformed to $Al_2O_3$ above $1400^{\circ}C$. Cavity structures related to the to the formation of $Al_4C_3$ were observed for the AI-C after heating at $1000^{\circ}C$ ofr 1 hour. Thermodynamic mechanism was considered to discuss the formation $Al_4C_3$, AlN and their transformation to $Al_2O_3$, which leads to the effect of oxidation resistance.

• Journal of the Korean Ceramic Society
• /
• v.27 no.5
• /
• pp.583-588
• /
• 1990

Glass films in the binary system B2O3-SiO2 and Al2O3-SiO2 were prepared on soda-lime-silica slide glass by the dip-coating technique from TEOS and boric acid or aluminum nitrate. Thickness of the films varying with viscosity and withdrawal speed were measured and effect of composition and firing temperature on the properties such as transmittance and refractive index were investigated. nM2O3.(100-n)SiO2(M=B or Al) films containing up to 20mol% B2O3 and 40mol% Al2O3 were transparent. Maximum transmittance at visible range were obtained for the sample containing 15mol% Ba2O3 and 32.5mol% Al2O3 and heat-treated at 50$0^{\circ}C$, respectively. Refractive index of the film containing 15mol% B2O3 was mininum in the B2O3-SiO2 binary system and minimal refractive index was appeared at the film containing 32.5mol% Al2O3. In IP spectra, addition of B2O3 were increased absorption peak intensity of B-O and Si-O-B bond and addition of Al2O3 were decreased absorption peak intensity of Si-O bond, respectively.