• Journal of the korean academy of Pediatric Dentistry
• /
• v.30 no.1
• /
• pp.143-152
• /
• 2003

The aims of the present study was to observe resin tag of the resin/enamel, dentin interface produced by self-etching adhesive systems and evaluate effect of additional acid etching on resin tag formation. Three self-etching primer(SE bond, AQ bond and L Pop) and an one bottle adhesive(Single bond) were used. Flat occlusal enamel and dentin disks were obtained from extracted human molars. A total of 20 surfaces were collected and divided into four groups of 5 samples. One-half of each specimen in each group was etched with 35% phosphoric acid prior to the application of each adhesive system, with the second half being kept unetched. Subsequently, resin composite was placed and polymerized. The samples were sliced and immersed into HCl and NaOCl solutions, followed by drying and sputter coating for examination with a SEM. The results were as follows; 1. Additional etching side of dentin displayed longer and thicker resin tag than unetched side in all self-etching adhesive groups. 2. In enamel, additional etching side displayed deeper and more distinct etching pattern than unetched side except L Pop. There is no difference between etched and unetched enamel in L Pop. The results obtained suggest the self-etching adhesive did not etch enamel and penetrate into dentinal tubule as deeply as did additional etching. Further research should include the evaluation of the relationship of boding strength, microleakage and resin tag morphology.

• The Journal of Korean Academy of Prosthodontics
• /
• v.53 no.4
• /
• pp.295-300
• /
• 2015

Purpose: The aim of this study was to evaluate the shear bond strength between Ni-Cr alloy and composite resin using universal adhesive systems coMPared to conventional method using metal primers. Materials and methods: For this study, a total of 120 cast commercial Ni-Cr alloy (Vera Bond 2V) disks were embedded in acrylic resin, and their surfaces were smoothed with silicon carbide papers and airborne-particle abrasion. Specimens of each metal were divided into 6 groups based on the combination of metal primers (Metal primer II, Alloy primer, Metal & Zirconia primer, MKZ primer) and universal adhesive systems (Single Bond Universal, All Bond Universal). All specimens were stored in distilled water at $37^{\circ}C$ for 24 hours. Shear bond strength testing was performed with a universal testing machine at a cross head speed of 1 m/min. Data (MPa) were analyzed using one-way ANOVA and the post hoc Tukey's multiple comparison test (${\alpha}$=.05). Results: There were significant differences between Single Bond Universal, All Bond Universal, Metal Primer II and Alloy Primer, MKZ Primer, Metal & Zirconia Primer (P<.001). Conclusion: Universal Adhesive system groups indicated high shear bond strength value bonded to Ni-Cr alloy than that of conventional system groups using primers except Metal Primer II. Within the limitations of this study, improvement of universal adhesive systems which can be applied to all types of restorations is recommended especially non-precious metal alloy. More research is needed to evaluate the effect of silane inclusion or exclusion in universal adhesive systems.

• Restorative Dentistry and Endodontics
• /
• v.26 no.5
• /
• pp.399-408
• /
• 2001

Tooth bleaching has been prevailing recently for its ability to recover the color and shape of natural teeth without reduction of tooth material. However, it has been reported that bleaching procedure adversely affects the adhesive bond strength of composite resin to tooth. At the same time the bond strength was reported to be regained by application of some chemical agents. The purpose of this in vitro study was to investigate the effect of the removal of residual peroxide on the composite- enamel adhesion and also evaluated fracture mode between resin and enamel after bleaching. Sixty extracted human anterior and premolars teeth were divided into 5 groups and bleached by combined technique using of office bleaching with 35 % hydrogen peroxide and matrix bleaching with 10% carbamide peroxide for 4 weeks. After bleaching, the labial surfaces of each tooth were treated with catalase, 70% ethyl alcohol, distilled water and filled with composite resin. Shear bond strength was tested and the fractured surfaces were also examined with SEM. Analysis revealed significantly higher bond strength values. (p＜0.05) for catalase-treated specimens, but water-treated specimens showed reduction of bond strength, alcohol- treated specimens had medium value between the two groups(p＜0.05). The fracture mode was shown that the catalase group and the alcohol group had cohesive failure but the water sprayed group had adhesive failure. It was concluded that the peroxide residues in tooth after bleaching seems to be removed by gradual diffusion and the free radical oxygen from peroxide prevents polymerization by combining catalyst in the resin monomer. Therefore it may be possible to eliminate the adverse effect on the adhesion of composite resin to enamel after bleaching by using water displacement solution or dentin bonding agent including it for effective removal of residual peroxide.

• Restorative Dentistry and Endodontics
• /
• v.38 no.4
• /
• pp.234-240
• /
• 2013

Objectives: This study evaluated the effects of intraradicular moisture on the pushout bond strength of a fibre post luted with several self-adhesive resin cements. Materials and Methods: Endodontically treated root canals were treated with one of three luting cements: (1) RelyX U100, (2) Clearfil SA, and (3) G-Cem. Roots were then divided into four subgroups according to the moisture condition tested: (I) dry: excess water removed with paper points followed by dehydration with 95% ethanol, (II) normal moisture: canals blot-dried with paper points until appearing dry, (III) moist: canals dried by low vacuum using a Luer adapter, and (IV) wet: canals remained totally flooded. Two 1-mm-thick slices were obtained from each root sample and bond strength was measured using a push-out test setup. The data were analysed using a two-way analysis of variance and the Bonferroni post hoc test with p = 0.05. Results: Statistical analysis demonstrated that moisture levels had a significant effect on the bond strength of luting cements (p < 0.05), with the exception of G-Cem. RelyX U100 displayed the highest bond strength under moist conditions (III). Clearfil SA had the highest bond strength under normal moisture conditions (II). Statistical ranking of bond strength values was as follows: RelyX U100 > Clearfil SA > G-Cem. Conclusions: The degree of residual moisture significantly affected the adhesion of luting cements to radicular dentine.

• The Journal of Korean Academy of Prosthodontics
• /
• v.38 no.4
• /
• pp.510-525
• /
• 2000

The effects of pretreatment of Co-Cr alloy, including two adhesive primers that contain either MDP or MAC-10, and silicoating on the bond The result sobtained as follows; o Strength of 4-META/MMA-TBB resin were investigated using FT-IR, SEM, and EDAX. o In the SEM observation of surface morphologies, the sandblasted specimen exibited a very rough surface, whereas the surfaces of the two groups primed with either MDP or MAC-10 were covered with a layer of primer, and the surface morphology of the silicoated specimen remained almost the same after sandblasting. o Before the thermocycling tests, the group treated with MDP demonstrated the highest mean tensile bond strength and the sandblasted group showed the lowest bond strength. o After 20,000 thermocyling, the mean tensile bond strength of the sandblasted group exhibited a 50% reduction in bond strength, while the others showed a $20\sim30%$ reduction. o Observation of the metal-resin interface revealed that in all groups the resin permeated the rough surface formed by sandblasting thereby producing a mechanical bond between the metal and the resin. It was also found that thermocycling resulted in a gap formation at the metal-resin interface of the specimens, and the sandblasted group exhibited a larger gap width than the other groups. o In fracture mode, all specimens indicated a cohesive fracture within the resin before thermocycling. However, thermocyling produced adhesive failure at the edge of the resin-metal interface in most specimens. The sandblasted group, which exhibited the lowest bond strength after thormocycling, also demonstrated the largest area of adhesive failure.

• Restorative Dentistry and Endodontics
• /
• v.35 no.6
• /
• pp.486-491
• /
• 2010

Objectives: This study examined the effect of 2% chlorhexidine on the ${\mu}TBS$ of a direct composite restoration using one-step self-etch adhesives on human dentin. Materials and Methods: Twenty-four extracted permanent molars were used. The teeth were assigned randomly to six groups (n = 10), according to the adhesive system and application of chlorhexidine. With or without the application of chlorhexidine, each adhesive system was applied to the dentin surface. After the bonding procedure, light-cure composite resin buildups were produced. The restored teeth were stored in distilled water at room temperature for 24 hours, and then cut and glued to the jig of the microtensile testing machine. A tensile load was applied until the specimen failed. The failure mode was examined using an operating microscope. The data was analyzed statistically using one-way ANOVA, Student's t-test (p < 0.05) and Scheffet's test. Results: Regardless of the application of chlorhexidine, the Clearfil $S^3$ Bond showed the highest ${\mu}TBS$, followed by G-Bond and Xeno V. Adhesive failure was the main failure mode of the dentin bonding agents tested with some samples showing cohesive failure. Conclusions: The application of 2% chlorhexidine did not affect the ${\mu}TBS$ of the resin composite to the dentin using a one-step self-etch adhesive.

• International Journal of Concrete Structures and Materials
• /
• v.6 no.2
• /
• pp.123-134
• /
• 2012

There is significant concern in the engineering community regarding the safety and effectiveness of fiber-reinforced polymer (FRP) strengthening of RC structures because of the potential for brittle debonding failures. In this paper, previous research programs conducted by other researchers were reviewed in terms of the debonding failure of FRP laminates externally attached to concrete. This review article also discusses the influences on bond strength and failure modes as well as the existing experimental research and developed equations. Based on the review, several important conclusions were re-emphasized, including the finding that the bond transfer strength is proportional to the concrete compressive strength; that there is a certain bond development length that has to be exceeded; and that thinner adhesive layers in fact lower the chances of a concrete-adhesive interface failure. It is also found that there exist uncertainty and inaccuracy in the available models when compared with the experimental data and inconsistency among the models. This demonstrates the need for continuing research and compilation of data on the topic of FRP's bond strength.

• Journal of the Korean Wood Science and Technology
• /
• v.52 no.4
• /
• pp.301-318
• /
• 2024

Contrary to other materials like metals, glass, etc., wood continuously interacts with the environment, increasing and decreasing its moisture content according to the humidity of the air and changing its dimensions by swelling or shrinking. Water diffusion through laminated solid wood is crucial in wood bonding processes. The adhesive layer might block the diffusion if the water vapor diffusion is perpendicular to the bond line. As a result of this blockage, different proportions of deformation appear on the two sides of the bond line, which causes stresses in the bonded assembly. The question arises of how long the bonded structure will keep its integrity due to moisture diffusion blockage, inevitable tensions appearing in the glue line, and how these stresses could be avoided. With cross laminated timber (CLT) solid wood panel production, this question gains new importance. Despite the relevance, only a limited number of publications are available. Comprehensive research would also be necessary considering both the molecular structure and diffusion properties of the adhesive adjusted to the wood species (covering possible substituting wood species, too). Overall, this review serves as a resource for enhancing our understanding of water vapor diffusion through wood adhesive layers and provides insights that have implications for reducing stresses in bonded wood assemblies and the performance of the bonded group over time. Furthermore, identifying knowledge gaps is necessary to establish the basis for investigating the diffusion property of CLT panels.

• Journal of the korean academy of Pediatric Dentistry
• /
• v.45 no.4
• /
• pp.436-444
• /
• 2018

The purpose of this study was to compare the shear bond strengths of 3-in-1 flowable composite to the enamel and dentin of primary teeth to previous adhesive systems. 110 primary incisors were prepared and divided into two groups: Dentin group included 5 groups: 1) Scotch bond Multi-purpose plus(DSM), 2) Single-bond 2(DSB), 3) Clearfil SE bond(DSE), 4) All bond universal(DAB), 5) Constic(DC), and Enamel group included 6 groups: 1) Scotch bond Multi-purpose plus(ESM), 2) Single bond 2(ESB), 3) Clearfil SE bond(ESE), 4) All bond universal(EAB), 5) Constic(EC), 6) Constic with additional etching(ECE). A cylinder of composite was bonded to the prepared surface, and the shear bond strength was measured. In the dentin groups, group DC had significantly lower shear bond strength than group DSE. No significant difference was found between group DC, group DSM, group DSB and group DAB. In the enamel groups, there was no significant difference between group EC, group ESE, and group EAB. This material showed lowest shear bond strength among all tested materials in both enamel and dentin groups, showing insignificant difference with some adhesive systems. Therefore, 3-in-1 flowable composite can be used for primary teeth restoration but further studies are needed.

• Journal of Korean Society of Occupational and Environmental Hygiene
• /
• v.1 no.2
• /
• pp.200-213
• /
• 1991

ln order to acquire the fundamental data for the organic solvents in bond and to contribute the health improvement of workers in deprtment of organic solvents in shoes manufacturing industries. The authors surveyed the contents of organic solvent in adhesive and determined the amount of volatilization of organic solvent by time and temperature with gaschromatography from March to September 1990. The results were as follows; 1) The kinds for organic solvents in bond were 9 that was Toluene, C-Hexane, N-Hexane, C-Hexanon, Aceton, Methyl Ethyl Keton, Dimethyl Formamide, Etyly Acetate. 2) Toluene and Methyl Ethyl Keton among the organic solvents in adhesive were over 80.18%. 3) The amount of volatilization of Methyl Cyclohexanone and Aceton by time and temperature were the most level than other compounds.