• Journal of the Korean Ceramic Society
• /
• v.36 no.10
• /
• pp.1016-1021
• /
• 1999

In this study activated carbon fibers were prepared from PAN-based carbon fibers by physical activation with steam or carbon dioxide. The variations in specific surface area amount of iodine adsorption and pore size distribution of the activated carbon fibers after the activation process were discussed. in steam activation BET surface area of about 1019 m2/g was obtained after 77% burn-off while carbn dioxide activation produced ACF with 694m2/g of BET surface area after 52% burn-off. However carbon dioxide activation produced at a similar degree of activation higher micropore volume(0.37 cc/g) and amount of iodine adsorption (1589mg/g) than steam activation. Nitrogen adsorption isotherms for (PAN based activated carbon fibers that prepared by physical activation were of type I in the Brunauer-Deming-Deming-Teller classification

• Journal of Environmental Science International
• /
• v.16 no.9
• /
• pp.1091-1098
• /
• 2007

Activated carbon was prepared from waste citrus peels by chemical activation with $ZnCl_2$. The optimal condition of carbonization was at $300^{\circ}C$ for 1.5 hr. Activation experiments with carbonized samples prepared at optimal carboniztion condition were carried out under various conditions such as activation temperature of 400 to $900^{\circ}C$, activation time of 0.5 to 2.0 hr, and $ZnCl_2$ ratio of 100 to 300%. In order to investigate the physical properties of the activated carbons prepared, iodine adsorptivities and specific surface areas were measured and their morphologies were observed from scanning electron microscopy. As $ZnCl_2$ ratio increased, activation yield decreased, while iodine adsorptivity and specific surface area increased. The optimal condition of activation was at 300% $ZnCl_2$ ratio and $300^{\circ}C$ for 1.5 hr, and then iodine adsorptivity and specific surface area was measured as about 862 mg/g and $756m^2/g$, respectively. SEM photography showed that the surface morphology was changed and many active pore were produced by chemical activation.

• Carbon letters
• /
• v.2 no.3_4
• /
• pp.176-181
• /
• 2001

A series of activated carbons were prepared from coconut shells and coal-tar pitch binder by physical activation with steam in this study. The effect of variable processes such as activation temperature, activation time and ratio of mixing was investigated for optimizing those preparation parameters. The activation processes were carried out continuously. The nitrogen adsorption isotherms at 77 K on pellet-shaped activated carbons show the same trend of Type I by IUPAC classification. The average pore sizes were about 19-21${\AA}$. The specific surface areas ($S_{BET}$) of pellet typed ACs increased with increasing the activation temperature and time. Specific surface area of AC treated for 90 min at temperature $900^{\circ}C$ was 1082 $m^2/g$. The methylene blue numbers continuously increased with increasing the activation temperature and time. On the other hand, iodine numbers highly increased till activation time of 60 min, but the rate of increase of iodine numbers decreased after that time. This indicates that new micropores were created and the existing micropores turned into mesopores and macropores because of increased reactivity of carbon surface and $H_2O$.

• Transactions on Electrical and Electronic Materials
• /
• v.15 no.2
• /
• pp.81-86
• /
• 2014

The process parameter in optimized KOH alkali activation of soft carbon series coke material in high purity was set with DOE experiments design. The activated carbon was produced by performing the activation process based on the set process parameters. The specific surface area was measured and pore size was analyzed by $N_2$ absorption method for the produced activated carbon. The surface functional group was analyzed by Boehm method and metal impurities were analyzed by XRF method. The specific surface area was increased over 2,000 $m^2/g$ as the mixing ratio of activation agent increased. The micro pores in $5{\sim}15{\AA}$ and surface functional group under 0.4 meq/g were obtained. The contents of the metal impurity in activated carbon which is the factor for reducing the electrochemical characteristics was reduced less than 100 ppm through the cleansing process optimization. The electrochemical characteristics of activated carbon in 38.5 F/g and 26.6 F/cc were checked through the impedance measuring with cyclic voltammetry scan rate in 50~300 mV/s and frequency in 10 mHz ~100 kHz. The activated carbon was made in the optimized activation process conditions of activation time in 40 minutes, mixing ratio of activation agent in 4.5 : 1.0 and heat treatment temperature over $650^{\circ}C$.

• Bulletin of the Korean Chemical Society
• /
• v.35 no.1
• /
• pp.103-110
• /
• 2014

Sisal fiber, an agricultural resource abundantly available in china, has been used as raw material to prepare activated carbon with high surface area and huge pore volume by chemical activation with zinc chloride. The orthogonal test was designed to investigate the influence of zinc chloride concentration, impregnation ratio, activation temperature and activation time on preparation of activated carbon. Scanning electron micrograph, Thermo-gravimetric, $N_2$-adsorption isotherm, mathematical models such as t-plot, H-K equation, D-R equation and BJH methods were used to characterize the properties of the prepared carbons and the activation mechanism was discussed. The results showed that $ZnCl_2$ changed the pyrolysis process of sisal fiber. Characteristics of activated carbon are: BET surface area was $1628m^2/g$, total pore volume was $1.316m^3/g$ and ratio of mesopore volume to total pore volume up to 94.3%. These results suggest that sisal fiber is an attractive source to prepare mesoporous high-capacity activated carbon by chemical activation with zinc chloride.

• Journal of Korean Society for Atmospheric Environment
• /
• v.21 no.4
• /
• pp.471-478
• /
• 2005

The objective of this research is to improve adsorption efficiency of adsorbent made from MSWI (Municipal Solid Waste Incinerator) ny ash by $HNO_3$ activation. The acidity and the basicity were determined by Boehm's method and the surface structure was studied by BET method with N2 adsorption. The adsorption properties were investigated with benzene and MEK (Methylethylketone). $HNO_3$ activation can modify the surface property of an adsorbent such as specific surface area, pore volume, and functional group. According to the results, the specific surface area of the adsorbent was increased from $309.2m^2/g\;to\;553.2 m^2/g$ by activation. Also oxygen-containing functional groups were formed on it.

• Proceedings of the Korean Magnestics Society Conference
• /
• 2000.09a
• /
• pp.200-206
• /
• 2000

We have investigated the activation magnetic moment, which characterizes the basis magnetic moment acting as a single magnetic particle during magnetization reversal. The activation magnetic moment was measured from each local area on continuous ferromagnetic thin films, by analyzing the magnetic field dependence of magnetization reversal of the corresponding local area based on a thermally activated relaxation process. It was found that the activation magnetic moment was nonuniform on submicrometer scale; the fluctuation increased with increasing the number of layers in Co/Pd multilayers. The distribution could be well analyzed by exp($\delta$m$\^$3/2/), where $\delta$m is the deviation of the activation magnetic moment from the mean value.

• Journal of Magnetics
• /
• v.6 no.2
• /
• pp.70-72
• /
• 2001

We have investigated the activation magnetic moment, which characterizes the basic magnetic moment acting as a single magnetic particle during magnetization reversal. The activation magnetic moment was measured from each local area on continuous ferromagnetic thin films, by analyzing the magnetic field dependence of magnetization reversal of the corresponding local area, based on a thermally activated relaxation process. It was found that the activation magnetic moment was nonuniform on a submicrometer scale; the fluctuation increased with increasing the number of layers in Co/Pd multilayers. The distribution could be well described by exp($\delta m^{3/2}$), where $\delta$m is the deviation of the activation magnetic moment from the mean value.

• Carbon letters
• /
• v.10 no.4
• /
• pp.339-344
• /
• 2009

Henequen fiber was air-stabilized, carbonized, and steam-activated to obtain high surface area activated henequen fiber (AHF). Thermal behavior of henequen fibers has been studied by TGA. The structural morphology and characteristics were observed by SEM and BET surface area measurement. The yield of AHF from natural henequen was in the range of 20~25 wt%. Mesopores (2~2.5 nm) were developed on the AHF as the activation temperature was raised up to $700^{\circ}C$, and the band of mesopore size distribution moved to 15~30 nm when the activation were carried out at $900^{\circ}C$ for 30 min. The specific surface area and the total pore volume were about $1394\;m^2/g$ and $1.30\;cm^3/g$, respectively at this activation conditions.

• PNF and Movement
• /
• v.20 no.2
• /
• pp.235-241
• /
• 2022

Purpose: The purpose of this study was to identify the effects of low intensity blood flow restriction training (LBFR) on the central nervous system of healthy adults. Methods: Ten healthy right-handed adults (eight males and two females, mean age of 28.6 ± 2.87 years) were selected as study subjects. Functional magnetic resonance imaging (fMRI) was conducted to measure brain activation (BA) following LBFR and non-LBFR. The primary motor area, premotor area, and supplementary motor area, which are closely related to exercise, were set as the regions of interest. Results: The BA recorded during the LBFR condition was 931.7 ± 302.44 voxel, and the BA recorded during the non-LBFR condition was 1,510.9 ± 353.47 voxel. Conclusion: BA was lower during LBFR than during non-LBFR.