• Proceedings of the Korea Technical Association of the Pulp and Paper Industry Conference
• /
• 2011.04a
• /
• pp.327-338
• /
• 2011

This study was carried in order to manufacture the high quality coated paper. High quality includes not only properties of coated paper but also final print quality. In this study, new acrylic-styrene emulsion was polymerized in laboratory and compared with styrene-butadiene latex. Low-shear viscosity of coating color was decreased with increasing acrylic-emulsion dosage. WRV was increased with addition and decreased with substitution of acrylic-emulsion. Paper gloss, brightness and whiteness were increased and PPS and opacity was slightly decreased with acrylic-emulsion. Ink gloss was increased with using No. 3 acrylic-emulsion due to lower ink setting properties. However No.1, 2 emulsion shows opposite situation. Surface strength of coated paper was increased with using No. 3 acrylic-emulsion These results indicate that high quality coated paper can be manufactured with using No. 3 acrylic-emulsion.

• Journal of Korea Technical Association of The Pulp and Paper Industry
• /
• v.44 no.1
• /
• pp.37-42
• /
• 2012

This study was carried in order to manufacture the high quality coated paper. High quality includes not only physical and optical properties of coated paper but also final print quality. In this study, new acrylic-styrene emulsion was polymerized in laboratory and compared with conventional styrene-butadiene latex. Low-shear viscosity of coating color was decreased with increasing acrylic-emulsion dosage. Small amount of acrylic emulsion addition increased water retention, but further addition decreased it. Acrylic-emulsion addition improved paper gloss, brightness and whiteness, but decreased PPS and opacity slightly. Ink gloss was increased with using No. 3 acrylic-emulsion due to lower ink setting properties. However No. 1 and 2 emulsion showed the opposite result. Surface strength of coated paper was increased with using No. 3 acrylic-emulsion. These results indicate that high quality coated paper can be manufactured with using No. 3 acrylic-emulsion.

• Journal of Adhesion and Interface
• /
• v.20 no.4
• /
• pp.135-139
• /
• 2019

In this work, flame retardant acrylic emulsion pressure sensitive adhesives were newly polymerized combining phosphorous flame retardant monomer and acrylic monomer like butyl acrylate, 2-ethylhexyl acrylate, methyl methacrylate, acrylic acid, and 2-hydroxyethyl methacrylate. The process of polymerization showed 100% of conversion at solid content of 65%, and viscosity of acrylic emulsion was increased up to 5500 cps when phosphorous flame retardant monomer was added into acrylic emulsion. The structure of flame retardant acrylic emulsion was identified using FT-IR and thermal properties like glass transition temperature (Tg) were checked by differential scanning calorimeter (DSC). Acrylic emulsion without phosphorous flame retardant monomer had Tg of -44.1℃ and peel strength of 2,100gf/inch, however, flame retardant acrylic emulsion showed maximum Tg (-31.4℃) and peel strength of 200gf/inch when 15 part of phosphorous flame retardant monomer was added. Flammability test was also conducted to confirm the application of flame retardant acrylic emulsion as the flame retardant addtive.

• Proceedings of the Korea Technical Association of the Pulp and Paper Industry Conference
• /
• 2011.04a
• /
• pp.339-347
• /
• 2011

This study was carried out in order to manufacture the high quality coated paper. High quality coated paper includes not only present state but also the state of the future. So in this study, acrylic-styrene emulsion which polymerized in laboratory was compared with SB(Styrene-butadiene) latex during thermal aging. The coated paper with three different formulations which controlled the dosage of acrylic-styrene emulsion were prepared. The coated paper were thermally aged at $105^{\circ}C$ for 18days and the optical properties were measured. Brightness, whiteness and CIE L value were higher during thermal aging with increasing amount of acrylic-styrene emulsion. CIE $a^*$ value was higher and CIE $b^*$ value decreased with increasing amount of acrylic-styrene emulsion. These results indicate that high quality coated paper which has anti -thermal aging property can be manufactured with acrylic-styrene emulsion.

• Journal of the Korea Institute of Building Construction
• /
• v.20 no.1
• /
• pp.35-41
• /
• 2020

The thin coating material used in the outer insulation finishing method is a finishing material mainly based on acrylic emulsion. In this study, the properties of silane modified acrylic emulsion and silica dispersed acrylic emulsion were evaluated. Experimental results showed that the silane modified acrylic emulsion had no significant effect on improving tensile strength, but was effective in improving the performance of adhesion strength, water absorption coefficient, and hot and cold repeat resistance. Silica-dispersed acrylic emulsions were effective in improving tensile strength, and at 10% substitution rate, they were effective in improving the performance of adhesion strength, water absorption coefficient and hot / cold resistance. Through this, it was judged that a composite emulsion capable of improving the performance of the acrylic emulsion could be prepared.

• Polymer(Korea)
• /
• v.34 no.1
• /
• pp.58-62
• /
• 2010

The acrylic monomers were graft-polymerized to starch as matrix polymer by emulsion polymerization. Viscosity and particle size of the emulsion were increased with starch contents due to interaction with water and particle swelling toward the water phase by hydroxy group of starch. Chemical stability of the emulsion was also increased with enhancement of starch, but water and alkali resistance were reduced with increasing starch contents because of the increasement of hyrophilicity. Opacity of the starch-acrylic emulsion compound containing calcium carbonate was decreased with contents of starch by its intrinsic color. The film of starch-acrylic polymer showed more clear appearance with increasing starch contents owing to enhancement of amorphous state.

• Journal of the Korean Applied Science and Technology
• /
• v.27 no.4
• /
• pp.445-451
• /
• 2010

To prepare very stable acrylic type emulsion having a visible ray absorption property, in-situ preparation technique of $Cu_xS$ nanoparticle was adopted. Firstly, the acylic emulsions of methyl methacrylate(MMA), butyl acrylate(BA), and acrylonitrile(AN) were synthesized by pre-emulsion polymerization at $60^{\circ}C$ in the presence of anionic surfactant. Secondly, $Cu_xS$ nanocomposited emulsions were directly prepared in the prepolymerized acrylic emulsion with $CuSO_4$ at $50^{\circ}C$. The presnce of $Cu_xS$ nanoparticle in emulsion was confirmed by SEM and EDS. The final $Cu_xS$ nanocomposited emulsion showed an olive-green colour and good emulsion stability up to 1 month. In addition the PET films coated with our $Cu_xS$ nanocomposited emulsion absorbed effectively the visible ray.

• Journal of the Korean Recycled Construction Resources Institute
• /
• v.5 no.1
• /
• pp.111-116
• /
• 2010

The treatment of heavy metal, in the waste ash from incinerator and mine solid waste, by using alkali-soluble acrylic copolymer emulsion, that is effective in the absorption of heavy metal has been studied. It seemed that alkali soluble acrylic copolymer emulsion was very effective in the absorption of Hg, Pb, Cd and Cu in this test. Also, eco-friendly thixotropic grout, using alkali soluble acrylic copolymer emulsion, that is effective in the absorption of heavy metal, for the recycling of waste ash from incinerator and mine solid waste has been tested. It was observed that waste ash could be used as a raw material of eco-friendly thixotropic grout mortar due to the effectiveness of alkali soluble acrylic copolymer emulsion in the fixation of heavy metals including $Cr^{6+}$ from waste ash in this test.

• Journal of Adhesion and Interface
• /
• v.23 no.3
• /
• pp.80-86
• /
• 2022

In this study, water-based acrylic tackifier with different contents of 1-dodecanethiol(n-DM), a chain transfer agent(CTA), were synthesized to improve the performance and adhesive properties of water-based acrylic pressure sensitive adhesive(PSA). In order to investigate the change in physical properties according to the amount of water-based acrylic tackifier added, 10/20/30 phr of water-based acrylic tackifier was added to the water-borne acrylic emulsion to measure the physical properties. The molecular weight and glass transition temperature(T_g) of the synthesized water-based acrylic tackifier tended to decrease as the content of n-DM increased. When a water-based acrylic tackifier was added to the water-borne acrylic emulsion, the peel strength and heat-resistance were increased. Also, when the water-based acrylic tackifiers were added at 10 phr or 20 phr, the best value was shown.

• Journal of the Korean Applied Science and Technology
• /
• v.25 no.4
• /
• pp.485-494
• /
• 2008

The acrylic coating emulsions were prepared by the emulsion polymerization to protect the surface of steel plate from the corrosion chemicals like acid, base and salt water. MMA(methyl methacrylate), styrene, BA(butyl acrylate), and 2-HEMA(2-hydroxyethyl methacrylate) were used as monomer. KPS(potassium persulfate) and SBS(sodium bisulfite) as redox initiator and SDBS(sodium dodecylbenzene sulfonate) as emulsifier were used on the emulsion polymerization reaction. The most stable in-situ coating was obtained when 10% of MMA was added. Both particle size and quantity in emulsion were decreased as increasing the mount of SDBS. the most stable prepared coating emulsion with polyisocyanate crosslinker showed very high anticorrosion properties on the coated steel layer to salt water, whereas no significant improvement of anticorrosion property to acdic and basic condition it showed.