• Proceedings of the Korean Society for Technology of Plasticity Conference
• /
• 2005.05a
• /
• pp.266-269
• /
• 2005

The effect of exit temperature on the thickness of recrystallization layer during Al extrusion process was investigated. The recrystallization layer of an extruded Al alloy is an important feature of the product in a wide range of applications, particularly those within the automotive industry. The thicker recrystallized layer in the Al alloys can give rise to a number of problems including reduced fatigue resistance and orange peel during cold forming. But the interaction of extrusion process variables with the thickness of recrystallization layer is poorly understood, and there is limited information available regarding the role of the main hot extrusion variables. Using the 3650 US ton extrusion press, this paper describes the effect of the main process variables such as billet temperature, ram speed, and exit temperature on the thickness of recrystallization layer for the A6XXX Al alloy.

• Transactions of Materials Processing
• /
• v.18 no.4
• /
• pp.342-346
• /
• 2009

Forming characteristics for the bundle extrusion of Cu-Ti bimetal wires are investigated, which can identify the process conditions for weak mechanical bonding at the contact surface during the direct extrusion of a Cu-Ti bimetal wire bundle. Bonding mechanism between Cu and Ti is assumed as a cold pressure welding. Then, the plastic deformation at the contact zone causes mechanical bonding and a new bonding criterion for pressure welding is developed as a function of the principal stretch ratio and normal pressure at the contact surface by analyzing micro local extrusion at the contact zone. The averaged deformation behavior of Cu-Ti bimetal wire is adopted as a constitutive behavior at a material point in the finite element analysis of Cu-Ti wire bundle extrusion. Various process conditions for bundle extrusions are examined. The deformation histories at the three points, near the surface, in the middle and near the center, in the cross section of a bundle are traced and the proposed new bonding criterion is applied to predict whether the mechanical bonding at the Cu-Ti contact surface happens. Finally, a process map for the direct extrusion of Cu-Ti bimetal wire bundle is proposed.

• Proceedings of the Korean Society of Precision Engineering Conference
• /
• 2005.06a
• /
• pp.499-502
• /
• 2005

A process map has been developed, which can identify the process conditions for weak mechanical bonding at the contact surface during the direct extrusion of a Cu-Ti bimetal bar. Bonding mechanism between Cu and Ti was assumed as a cold pressure welding. Then, the plastic deformation at the contact zone causes mechanical bonding and a new bonding criterion for pressure welding was developed as a function of the principal stretch ratio and normal pressure at the contact surface by analyzing micro local extrusion at the contact zone. Finite element analyses for extrusion of Cu-Ti bimetal bars were performed for various process conditions. The deformation history at the contact surface was traced and the proposed new bonding criterion was applied to predict whether the mechanical bonding at the Cu-Ti contact surface happens. Finally, a process map for the extrusion of Cu-Ti bimetal bar is suggested.

• Fibers and Polymers
• /
• v.1 no.2
• /
• pp.103-110
• /
• 2000

Flow analysis of profile extrusion is essential for design and production of a profile extrusion die. Velocity, pressure, and temperature distribution in an extrusion die are predicted and compared with the experimental results. A two dimensional numerical method is proposed for three dimensional analysis of the flow field within the profile extrusion die by applying a modified cross-sectional numerical method. Since the cross-sectional shape of the die is varied gradually, it is assumed that the pressure is constant within a cross-sectional plane that is perpendicular to the flow direction. With this assumption, the velocity component in the cross-sectional direction is neglected. The exact cross-sectional shape at any position is calculated based on the geometry of standard cross-sections. The momentum and energy equations are solved with proper boundary conditions at a cross-section and then the same calculation is carried out for the next cross-section using the current calculated values. An L-shaped profile extrusion die is produced and employed for experimental investigation using a commercially available polypropylene. Numerical prediction for the varying cross-sectional shape provides better results than the previous studies and is in good agreement with the experimental results.

• Transactions of Materials Processing
• /
• v.19 no.6
• /
• pp.352-356
• /
• 2010

This paper was designed to fabricate the micro-spur gear by the LIGA and hybrid powder extrusion process. It is important to manufacture a micro-die with a high aspect ratio and determine appropriate extrusion conditions for a microforming. Ni has been used to fabricate micro-dies. LIGA process was capable to produce micro-extrusion dies with close tolerance, longer bearing length and adequate surface quality. Superplastic Al-78Zn powders have the great advantage in achieving deformation under low stresses and exhibiting good micro-formability with average strain rate raging from $10^{-3}$ to $10^{-2} s^{-1}$ and constant temperature ranging from 503 to 563K. Al-78Zn powders were compacted into a cylindrical shape ($\Phi3\times$h10mm) under compressive force of 10kN and, subsequently, the compacted powders were extruded by the hybrid powder extrusion process controlling of the temperature holing time for a improvement on formability of Al-22Zn powder. Micro-extrusion has succeeded in forming micro-gear shafts.

• Proceedings of the Korean Society for Technology of Plasticity Conference
• /
• 2007.05a
• /
• pp.246-249
• /
• 2007

It is very important that there are saving resource and energy in the future as well as in these day. Weight saving of structural parts, which are formed by extrusion, plays a key role in manufacturing field. Extruded aluminum parts' cross sections are constant in the axial direction by conventional extrusion method. Especially these aluminum parts used in the car need other processes to vary the cross section in the axial direction. Thus, applications of these parts are limited by high cost. if the cross section of the parts is variable by only extrusion, application of extruded aluminum parts will more increase. Therefore, a new CNC extruder which can control the section area of a car part was invented the nation's first. Using the extrusion machine, the experiment was performed to validate the workability.

• Transactions of the Korean Society of Mechanical Engineers
• /
• v.18 no.8
• /
• pp.2005-2015
• /
• 1994

An analytical method based on the upper bound approach for the cup-bar axisymmetric combined extrusion is presented to determine the deformation zones as well as extrusion load and deformed geometry in the early stage. A new kiematically admissible velocity field is derived by the appropriate transformation of the original velocity field and applying the flow function approach. The derived velocity field is directly related to the boundary function for the plastically deforming zones and the parameter controlling the flow direction to the forward part or backward part. Experiments are carred out with the annealed aluminum 2024 at room temperature for the various area reductions. The workhardening effect is considered in the formulation as a function of the height ratio between the deformed billet and the orighinal billet to calculate the extrusion pressures. The theoretical predictions for the extrusion loads and deformed configuration are in good agreement with the experimental results.

• Proceedings of the Korean Society of Precision Engineering Conference
• /
• 2003.06a
• /
• pp.414-417
• /
• 2003

A copper-clad aluminium composite bar is lighter and less expressive than a commercial copper alloy bar. Copper-clad aluminium composite bar can be fabricated by hot hydrostatic extrusion process. In this work, the effect of die angle on the compressive properties of copper-clad aluminium composites fabricated using hydrostatic extrusion process was investigated experimentally. The results showed that optimum half die angle was in the range of 40$^{\circ}$ to 50$^{\circ}$ for an extrusion ratio of 19. The results also showed that the half die angle had little influence on the compressive strength of copper-clad aluminium composites. A diffusion layer increased with increasing die angle.

• Proceedings of the Korean Society for Technology of Plasticity Conference
• /
• 1995.10a
• /
• pp.143-149
• /
• 1995

A simple kinematically admissible velocity field is proposed to drtermine the final-stage extrusion load and the average extruded length in the square-die forward extrusion of non-axisymmetric bars from circular billets. The proposed velocity field is applied to the square-die extrusion of trochoidal gear-shaped bars and rectangular-shaped bars, the profile function of a rectangular being approximated by using a Fourier series. Experiments have been carried out with hard solder billets at room temperature. The theoretical predictions of the extrusion load are in good agreements with the experimental results and there is generally reasonable agreements in average extruded length between theory and experiment.

• Transactions of Materials Processing
• /
• v.4 no.4
• /
• pp.390-397
• /
• 1995

A simple kinematically admissible velocity field is proposed to determine the final-stage extrusion load and the average extruded length in the square-die forward extrusion of non-axisymmetric bars from circular billets. The proposed velocity field is applied to the square-die extrusion of trochoidal gear-shaped bars and rectangular-shaped bars. The profile function of a rectangle is approximated by using a Fourier series. Experiments have been carried out with hard solder billets at room temperature. The theoretical predictions of the extrusion load are in good agreements with the experimental results and there is generally reasonable agreements in average extruded length between theory and experiment.