• Journal of the Korean Ceramic Society
• /
• v.25 no.2
• /
• pp.117-124
• /
• 1988

The properties of the powders of the system Al2O3-ZrO2-Y2O3 prepared by precipitation method were investigated. Al2(SO4)3$.$18H2O3, ZrOCl2$.$8H2O and YCl3$.$6H2O were used as starting materials. Amorphous aluminum hydrate prepared by precipitation method was completely transformed to alpha Al2O3 as a result of calcining at 1100$^{\circ}C$ for 1 hr and gamma, delta and theta phases appeared as transition phases. In ZrO2-Y2O3 system prepared by co-precipitation method, the crystallization temperature of ZrO2 was increase with Y2O3 contents. The coupled crystallization occured in coprecipitated Al2O3-ZrO2-Y2O3 system, therefore the formation temperature of alpha Al2O3 and ZrO2-Y2O3 system. In this ternary system, the powder morphology showed a particular shape which was composed of large Al2O3 grains having small spherical ZrO2 particles within large Al2O3 grain and relatively large ZrO2 particles along the grian boundaries.

• Journal of the Korean Ceramic Society
• /
• v.41 no.4
• /
• pp.284-288
• /
• 2004

To improve mechanical properties of $Al_2$O$_3$/ZrO$_2$composites have been controlled dispersion of ultra low size ZrO$_2$ particles in $Al_2$O$_3$ ceramics by polymeric precursor method (Pechini process). In case of coprecipitation or mechanical mixing of ZrO$_2$ powders with $Al_2$O$_3$, homogeneous dispersion and controlling the ZrO$_2$ size were relatively difficult due to high sintering temperature. So the polyesterization process of Zr/Y(NO$_3$)$_3$-citric acid solution in ethylene glycol with the commercial sub-micron sized o(-alumina powder (Sumitomo AES-11(0.4 ${\mu}{\textrm}{m}$)) was adopted in order to obtain homogeneous dispersion of ZrO$_2$ in A1203. By this partial polyesterization process, the homogeneous dispersion of relatively low sized ZrO$_2$in $Al_2$O$_3$/ZrO$_2$composites was achieved at 1450∼1$600^{\circ}C$ of sintering temperature range and their mechanical properties were measured.

• Journal of the Korean Ceramic Society
• /
• v.39 no.7
• /
• pp.704-709
• /
• 2002

To improve the mechanical properties of $Al_2$O$_3$/ZrO$_2$composites, the homogeneous dispersion of ultra low size ZrO$_2$ particles in $Al_2$O$_3$ceramics have been controlled by coprecipitation method. In case of mechanical mixing of ZrO$_2$ powders with $Al_2$O$_3$, homogeneous dispersion and controlling the ZrO$_2$ size were relatively difficult due to high sintering temperature. So nanosized Zr hydroxide was coprecipitated from ZrOCl$_2$/Y(NO$_3$)$_3$ solution with commercial sub-micron sized $\alpha$-alumina (Sumitomo : AES-11(0.4 ${\mu}{\textrm}{m}$)) and high purity ultra low sized $\alpha$-alumina (Taimei Chemical (0.22 ${\mu}{\textrm}{m}$)) for low temperature sintering. By this partial coprecipitation method, relatively low sized ZrO$_2$ dispersion in $Al_2$O$_3$/ZrO$_2$ composites was achieved at 150$0^{\circ}C$-1$600^{\circ}C$ of sintering temperature range and their mechanical properties were measured.

• Journal of the Korean Ceramic Society
• /
• v.28 no.1
• /
• pp.11-18
• /
• 1991

A precipitation method, one of the most effective liquid phase reaction methods, was adopted in order to prepare high-tech Al2O3/ZrO2 composite ceramics, and the effects of stress-induced phase transformation of ZrO2 on thermal shock behavior of Al2O3-ZrO2 ceramics were investigated. Al2(SO4)3.18H2O, ZrOCl2.8H2O and YCl3.6H2O were used as starting materials and NH4OH as a precipitation agent. Metal hydroxides were obtained by single precipitation(process A) and co-precipitation(process B) method at the condition of pH=7, and the composition of Al2O3-ZrO2 composites was fixed as Al2O3-15v/o ZrO2(+3m/o Y2O3). Critical temperature difference showing rapid strength degradation by thermal shock showed higher value in Al2O3/ZrO2 composites(process A : 20$0^{\circ}C$, process B : 215$^{\circ}C$) than in Al2O3(175$^{\circ}C$). The improvement of thermal shock property for Al2O3/ZrO2 composites was mainly due to the increase of strength at room temperature by adding ZrO2. The strength degradation was more severe for the sample with higher strength at room temperature. Crack initiation energies by thermal shock showed higher values in Al2O3/ZrO2 composites than in Al2O3 ceramics due to increase of fracture toughness by ZrO2.

• Journal of the Korean Ceramic Society
• /
• v.24 no.1
• /
• pp.33-40
• /
• 1987

The investigation includes phase equilibria of Al2O3-HfO2 Cr2O3-ZrO2, Cr2O3-HfO2, Al2O3-Cr2O3-ZrO2, Al2O3-Cr2O3-HfO2, Al2O3-ZrO2-HfO2, Cr2O3-ZrO2-HfO2, Al2O3-Cr2O3-ZrO2-HfO2. In the systems the solubility near the end members has been studied at 1500$^{\circ}C$ and 1600$^{\circ}C$, respectively. Selective Compositions were investigated in the area of the guarternary system where the phae relation was examined.

• Korean Journal of Materials Research
• /
• v.13 no.9
• /
• pp.572-580
• /
• 2003

Synthesizing behavior and microstructural evolution of $CaZrO_3$and $m-ZrO_2$in a thermal reaction process of $ZrSiO_4$-$xCaCO_3$mixtures, where x is 7 and 19, were investigated to determine the addition amount of CaO in CaO:$ZrO_2$:$SiO_2$ternary composition. CaZrO$_3$-Ca$_2$SiO$_4$precursor prepared by the mixture of $ZrSiO_4$and CaCO$_3$in aqueous suspending media was controlled to the acidic (pH=4.0) condition with HCI solution to enhance the thermal reaction. The addition amount of dispersant into the $ZrSiO_4$-$xCaCO_3$slip increased with increasing mole ratio of $CaCO_3$, which was associated with the viscosity of slip. Decarbonation reaction was activated with an increase of the addition amount of $CaCO_3$, showing different final temperatures in $ZrSiO_4$-$7CaCO_3$and $ZrSiO_4$-$19CaCO_3$mixtures as about 980 and 116$0^{\circ}C$, respectively, for finishing decarbonation reaction. The grain morphology was changed to spherical shape for all samples with an increase of sintering temperature. The grain size and phase composition of the synthesized composites depended on the mixture ratio of Zrsi04 and CacO3 powders, indicating that the main crystals were m-ZrO2 ($\leq$3 $\mu\textrm{m}$) and $CaZrO_3$ ($\leq$ 7 $\mu\textrm{m}$) in $ZrSiO_4$$>-7CaCO_3$and $ZrSiO_4$-$19CaCO_3$mixtures, respectively.

• Journal of the Korean Ceramic Society
• /
• v.31 no.1
• /
• pp.17-24
• /
• 1994

Al2O3-ZrO2(ZTA) composites were fabricated by a surface-induced coating of the precursor for the ZrO2 phase on the kinetically stable colloid particles of Al2O3. The fabricated composites were characterized by a uniform spatial distribution of the dispersed ZrO2 phase and by the absence of large ZrO2 grains throughout the Al2O3 matrix. The fracture toughness (KIC) and the bending strength of ZTA composites sintered at 1$600^{\circ}C$, respectively, were 5.6 MPa.m1/2 (for 20 wt% ZrO2) and 600 MPa (for 15wt% ZrO2). The fraction of tetragonal ZrO2 phase decreases as the total content of ZrO2, suggesting that both the stress-induced tlongrightarrowm transformation and the microcrack nucleation contribute to the toughening of the ZTA composites fabricated by the surface-induced coating.

• Applied Chemistry for Engineering
• /
• v.17 no.3
• /
• pp.250-254
• /
• 2006

Reaction of $CO_2$ with $Li_{2}ZrO_{3}$ has been investigated in a TGA and the effects of $H_{2}$ and CO on the removal of $CO_{2}$ using $Li_{2}ZrO_{3}$ were evaluated in a packed bed reactor. The initial rate of $CO_{2}$ removal reaction of $Li_{2}ZrO_{3}$ increased with the increase of gas flow rate up to 100 mL/min and then was maintained, which implied the disappearance of the gas film resistance. The reaction of $CO_{2}$ with $Li_{2}ZrO_{3}$ took place as the first order and the range of optimum temperature was found to be about $500{\sim}600^{\circ}C$. XRD and SEM analysis showed the formation of crystalline $Li_{2}ZrO_{3}$ and porous $Li_{2}ZrO_{3}$/$ZrO_{2}$. The presence of $H_{2}$ did not affect the adsorption of $CO_2$ with $Li_2ZrO_3$. On the other hand, CO inhibited the sorption of $CO_{2}$ into $Li_{2}CO_{3}$(L) on $Li_{2}ZrO_{3}$.

• Journal of the Korean Ceramic Society
• /
• v.34 no.2
• /
• pp.145-156
• /
• 1997

ZrO2 phase transformations depending on the type and amount of dopants and the sintering temperatures were studied for the 2 components (CaO-, Y2O3-, MgO-ZrO2) and the 3 components(MgO-ZrO2-Al2O3)ZrO2 powder by X-ray diffraction and Raman spectroscopy. In the CaO- and Y2O3-ZrO2 systems, as the CaO and Y2O3 contents increased to 6~15mol% and 3~15mol% respectively, we were not able to identify between tetragonal and cubic in the X-ray diffraction patterns. On the other hand, all Raman modes shifted to lower wavenumbers, decreasing in intensity and the number of bands, markedly. These phenomena were caused by tetragonallongrightarrowcubic phase transformation and interpreted by the breakdown of the wave vector selection rule(k=0) and the structural disorder associated with the formation of oxygen sublattice which was caused by the substitution between Zr4+ ion and Ca2+ or Y3+ ion in ZrO2 matrix. The monoclinic to cubic phase transformation occurred in 10mol% MgO-ZrO2 system. As the Al2O3 content increased from 0 to 20mol% in the MgO-ZrO2-Al2O3 systems, cubic phase transformed to monoclinic phase, this is because the MgO didn't play a role in a stabilizer because of the formation of the spinel(MgAl2O4) by the reaction between MgO and Al2O3, Also, the ZrO2 phase transformation was explained by the change of it's lattice parameters depending on the type and amount of dopants. Namely, as the amount of dopant increased to 10~13mol%, the axial ra-tio c/a came close to unity with increasing the lattice parameter a and decreasing the lattice parameter c. At that time, the tetragonallongrightarrowcubic phase transformation occurred.

• Journal of the Korean Ceramic Society
• /
• v.37 no.11
• /
• pp.1058-1064
• /
• 2000

연속슬립캐스팅 및 상압소결법으로 $Al_2$O$_3$/ZrO$_2$적층복합체를 제조하였으며, 적층복합체에서 ZrO$_2$층을 단사정, 정방정 및 입방정으로 각각 달리 적층하여 균열생성 및 전파 거동에 미치는 ZrO$_2$상의 영향을 고찰하였다. 균열 생성은 냉각시 $Al_2$O$_3$층과 ZrO$_2$층 간의 열팽창 계수의 차이에 의한 열적불일치응력이 가장 큰 요인으로 작용하였다. 적층체 내에 존재하는 균열은 tetra-ZrO$_2$의 경우 적층두께 조절로 가능하였으며, cubic-ZrO$_2$의 경우는 냉각속도 조절로 균열밀도로 크게 낮출 수 있었다. $Al_2$O$_3$/ZrO$_2$적층체를 구성하는 세가지 ZrO$_2$상(mono, tetra, cubic)들 중에서 cubic-ZrO$_2$가 포함된 적층체의 경우 $Al_2$O$_3$와 ZrO$_2$계면에 형성된 잔류압축응력으로 인한 균열굴절 효과를 얻을 수 있었다.