• Journal of the Korean Society for Heat Treatment
• /
• v.29 no.1
• /
• pp.1-7
• /
• 2016

Titanium and its alloys can be usually joined with brazing method. And the alloys should be brazed at low temperature to keep their original microstructure. In this study, the mechanical strength and microstructure of the CP-Ti joint-brazed with $Zr_{54}Ti_{22}Ni_{16}Cu_8$ filler metal having melting temperature of $774{\sim}783^{\circ}C$ were investigated. The tensile strengths of the joint-brazed at $800^{\circ}C$ with $100^{\circ}C/min$ of cooling rate showed more than 400 MPa which was as high as base metal. The $Widmanst{\ddot{a}}tten$ structure consisting of Ti and $Ti_2Ni$ phase was observed in the joint area. However, the tensile strengths of the joint-brazed at $800^{\circ}C$ with $15^{\circ}C/min$ of cooling rate were decreased and the Ti, $(Ti,Zr)_2Ni$ and $Ti_2Ni$ phases were observed at the joint area. It is believed that the $(Ti,Zr)_2Ni$ laves phases could decrease the mechanical strength of the joint and the cooling rate should be controled to get high strength of the titanium joint.

• Journal of the Korean Society for Heat Treatment
• /
• v.5 no.1
• /
• pp.41-49
• /
• 1992

The effects of alloying elements on the superplastic properties of Al-Li based alloys had been investigated. The intermediate thermo-mechanical treated (ITMT) Al-2.0wt%Li, Al-2.0wt%Li-1.0wt%Mg, Al-2.0wt%Li-0.12wt%Zr and Al-2.0wt%Li-1.2wt%Cu-1.0wt%Mg-0.12wt%Zr alloys were tested in tension at various temperature (400, 450, 500 and $550^{\circ}C$) and strain rate($6.7{\times}10^{-3}$, $1.0{\times}10^{-2}$, $1.6{\times}10^{-2}$ and $5.0{\times}10^{-2}/sec$). The results were as follows : The superplasticity in binary, ternary and pentanary alloys appeared at 500 to $550^{\circ}C$, and good strain rate for superplasticity. $1.6{\times}10^{-2}/sec{\sim}1.0{\times}10^{-2}/sec$ for a binary alloy and $1.0{\times}10^{-2}/sec{\sim}6.7{\times}10^{-3}/sec$ for ternary and pentanary alloys. A Zr-added ternary alloy had best value of elongation (730%) in four alloys at $550^{\circ}C$ of tension temperature and $1.0{\times}10^{-2}/sec$ of strain rate. The strain rate was greatly dependent on tension temperature and true strain rate was more than 1.0 at all test temperature and strain rate. In binary and Mg-added teranry alloys. the necks were slightly formed and their fracture surface had lips shape, but Zr-added ternary and pentanary alloy fractured along the grain boundary without necking. Their dislocations moved to grain boundary during superplasticity deformation and arranged perpendicular to grain boundary. Super plastic deformation was made by grain boundary slip of dislocation slip creep and model of core and mantle.

• Journal of Nuclear Fuel Cycle and Waste Technology(JNFCWT)
• /
• v.15 no.2
• /
• pp.125-133
• /
• 2017

KAERI is conducting research on spent cladding hulls and additive metals to generate a solidification host matrix for the noble metal fission product waste in anode sludge from the electro-refining process to minimize the volume of waste that needs to be disposed of. In this study, alloy compositions Zr-17Cr, Zr-22Cr, and Zr-27Cr were prepared with or without eight noble metals representing fuel waste using induction melting. The microstructures of the resulting alloys were characterized and electrochemical corrosion tests were conducted to evaluate their corrosion characteristics. All the compositions had better corrosion characteristics than other Zr-based alloys that were evaluated for comparison. Analysis of the leach solution after the corrosion test of the Zr-22Cr-8NM specimen indicated that the noble metals were not leached during corrosion under 500 mV imposed voltage, which simulates a highly oxidizing disposal environment. The results of this study confirm that Zr-Cr based compositions will likely serve as chemically stable waste forms.

• Korean Journal of Materials Research
• /
• v.10 no.7
• /
• pp.499-504
• /
• 2000

Recently there have been many investigations on the synthesis and properties of transition metal trialuminides based on Ti, Zr, V, Nb and Ta for use aircraft structure materials in an elevated environment. The effect of Zr additions on the formation behaviour of Al-Nb alloy was investigated. Al-1.3at.%(Nb+Zr) alloys with different Nb to Zr atomic 1:3, 1:1 and 3:1 were prepared by mechanical alloying(MA). The morphological changes and microstructural evolution of Al-Nb-Zr powders during MA were investigated by SEM, XRD and TEM. The intermetallic compound phase of $Nb_2Al\; and\; Al_3Zr_4$ was identified by X-ray diffraction. The intemetallic compound of $Al_3Zr,\; Al_3Nb$ and $Al_3Zr_4$ were formed by heat treatment for 1 hour at $500^{\circ}C$. The size of intermetallic compounds observed by TEM were approximately below 100nm, when they were heat treated after mechanically alloying for 30 hours.

• Korean Journal of Materials Research
• /
• v.9 no.10
• /
• pp.978-984
• /
• 1999

ZrNbFeCu-xSn 합금을 진공 아크 용해법으로 제조하여 $360^{\circ}C$의 물, $400^{\circ}C$의 수증기 및 36$0^{\circ}C$의 70ppm LiOH 분위기에서 부식실험을 실시하였으며, 시편의 미세구조는 광학현미경, SEM 및 TEM으로 관찰하였다. 36$0^{\circ}C$에서 210일까지 부식 실험한 결과 대부분의 합금이 천이 전 영역에서의 부식거동을 보였다. $400^{\circ}C$ 경우, 초기에는$ 360^{\circ}C$에서의 부식거동과 비슷한 경향을 보였으나 80일 이후부터는 천이현상이 발생하여 부식속도가 급격히 증가하는 경향을 나타내었는데, Sn량이 많을수록 보다 빠른 시간에 천이현상이 발생했다. LiOH 용액에서는 전반적으로 $400^{\circ}C$에서 보다 더 늦은 시간에 천이현상이 발생했다. 석출물은 Zr(Fe,Cu)$_2$나Zr(Fe,Cu)$_3$로 추정되는 성분을 가지지만, Sn의 증가에 따라 석출물의 조성이나 크기는 거의 변화가 없는 것으로 관찰되었다.

• Transactions of the Korean hydrogen and new energy society
• /
• v.15 no.4
• /
• pp.266-273
• /
• 2004

The objective of this study is an understanding of stress corrosion cracking of metals that is recognized to mostly limit the lifetime of the structural materials by comparing the features of delayed hydride cracking of zirconium alloys with those of stress corrosion cracking (SCC) of Ni-based alloys and hydrogen cracking of stainless steels. To this end, we investigated a dependence of delayed hydride cracking (DHC) velocity on the applied stress intensity factor and yield strength, and correlated a temperature dependence of the striation spacing and the DHC velocity. We reviewed a similarity of the features between the DHC of zirconium alloys, the SCC of Ni-based alloys and turbine rotor steels, and the hydrogen cracking of stainless steels and discussed the SCC phenomenon in metals with our DHC mode.

• Korean Journal of Materials Research
• /
• v.9 no.4
• /
• pp.386-391
• /
• 1999

The charge-discharge, the high-rate dischargeability, and the self discharge characteristics of the electrodes composed of rapidly solidified ZrV\ulcornerMn\ulcornerMo\ulcornerNi\ulcorneralloy, which has the form of partial substitution of Mn, Mo, Ni for V in $ZrV_2$ were studied. The alloys were prepared using Arc & RSP(Rapid Solidification Process) at the rotating roller speed of 2000 and 5000 rpm. Some of them were received heat treatment at$ 560 ^{\circ}C$ for 1 hour after the solidification to investigate the effect of the heat treatment. It was fond that cycle life was significantly improved by RSP, whereas discharge capacity, activation rte and high rate dischargeability were decreased compared with the conventional arc melting method. The capacity loss seems to be due to the loss of the crystallinity and the increase of the cycle life ascribed to the presence of the amporphous phase as well as the refined grain size of less than 0.2$\mu\textrm{m}$. Heat treatment of the alloy cooled at 2000 rpm improved the cycle life. In case of the alloys cooled at 5000 rpm, both the discharge capacity and the activation rate were significantly improved by the heat treatment.

• Journal of the Korean Society for Heat Treatment
• /
• v.4 no.3
• /
• pp.1-6
• /
• 1991

In this study, intermediate thermo-mechanical treated Al-2.0 wt%Li, and Al-2.0 wt%Li-1.2 wt%Cu-1.0 wt%Mg-0.12 wt%Zr alloys were tested in tension at $10^{\circ}C$ and elevated temperature(100, 200 and $300^{\circ}C$). The results are follows : The tensile strength of Al-Li-Cu-Mg-Zr alloy is the highest but the elongation of Al-Li alloy is the highest(106%) among the all alloys in tension at $300^{\circ}C$. The Portervin-LeChartlier effect is showed in AI-Li-Cu-Mg-Zr alloy at 10 and $100^{\circ}C$, because of tangled dislocation by Mg and Cu. In the true stress-strain curves of all alloy, the peaks of stress at $300^{\circ}C$ are showed at the strain less than 0.1. In the binary alloy, the dynamic restoration process at 200 and $300^{\circ}C$ is nearly similar to dynamic recovery type. The hot deformation stress is decreased with increase of dynamic recovery degree, but the elongation is increased. When the strain the strain rate are constant, the temperature dependence of hot deformation stress is increased with increase of deformation temperature. The elongation and degree of dynamic recovery are decreased with increase of hot deformation activation energy, but the deformation stresses slightly increased.

• Journal of Electrochemical Science and Technology
• /
• v.10 no.1
• /
• pp.82-88
• /
• 2019

Here, we report on nanocrystalline Si-Al-M (M = Fe, Cu, Ni, Zr) alloys for use as an anode for lithium-ion batteries, which were fabricated via a melt-spinning method. Based on the XRD and TEM analyses, it was found that the Si-Al-M alloys consist of nanocrystalline Si grains surrounded by an amorphous matrix phase. Among the Si-Al-M alloys with different metal composition, Ni-incorporated Si-Al-M alloy electrode retained the high discharge capacity of 2492 mAh/g and exhibited improved cyclability. The superior $Li^+$ storage performance of Si-Al-M alloy with Ni component is mainly responsible for the incorporated Ni, which induces the formation of ductile and conductive inactive matrix with crystalline Al phase, in addition to the grain size reduction of active Si phase.

• Proceedings of the Korean Nuclear Society Conference
• /
• 1999.05a
• /
• pp.234-234
• /
• 1999