• Bulletin of the Korean Chemical Society
• /
• 제35권1호
• /
• pp.189-196
• /
• 2014

Water dispersible ZnS based nanocrystals: ZnS (blue), ZnS:Cu (green) and ZnS:Mn (yellow-orange) were synthesized by capping the surface of the nanocrystals with a mercaptopropionic acid (MPA) molecule. The MPA capped ZnS based nanocrystal powders were characterized by using XRD, HR-TEM, EDXS, FT-IR, and FT-Raman spectroscopy. The optical properties of the colloidal nanocrystals were also measured by UV/Vis and photoluminescence (PL) spectroscopies in aqueous solvents. The PL spectra showed broad emission peaks at 440 nm (ZnS), 510 nm (ZnS:Cu) and 600 nm (ZnS:Mn), with relative PL efficiencies in the range of 4.38% to 7.20% compared to a reference organic dye. The measured average particle sizes from the HR-TEM images were in the range of 4.5 to 5.0 nm. White light emission was obtained by mixing these three nanocrystals at a molar ratio of 20 (ZnS):1 (ZnS:Cu):2 (ZnS:Mn) in water. The measured color coordinate of the white light was (0.31, 0.34) in the CIE chromaticity diagram, and the color temperature was 5527 K.

• 대한화학회지
• /
• 제53권6호
• /
• pp.677-682
• /
• 2009

본 논문에서는 ZnS:Mn/ZnS 코어-쉘 양자점을 유기금속전구체의 열분해 방법으로 합성하였다. 쉘의 형성온도를 135$^{\circ}C$로 고정한 반면 코어 나노입자의 합성 온도 조건을 다양화 하여 각 조건하에서 형성된 양자점들의 특성을 조사하였다. 실험을 통해 얻은 양자점들은 UV-Vis, 액체 photoluminescence (PL) spectroscopy 방법으로 광 특성을 조사하였으며, 또한 XRD, HR-TEM, 및 EDXS 분석으로 입자크기와 조성 등을 측정하였다. 실험 결과 가장 좋은 광 특성을 보인 나노입자의 합성조건은 코어와 쉘 모두 135$^{\circ}C$인 것으로 밝혀 졌으며, 이 조건에서 얻은 양자점은 583 nm 의 PL 발광 피이크와 42.15%의 높은 양자효율을 나타내었다. HR-TEM 으로 측정한 ZnS:Mn/ZnS 양자점의 평균 입자크기는 지름이 약 4.0 - 5.4 nm 정도였으며, 특히 150$^{\circ}C$의 온도 조건에서는 타원형의 입자가 형성되는 것이 관찰되었다.