• Journal of the Korean Ceramic Society
• /
• v.42 no.7 s.278
• /
• pp.521-524
• /
• 2005

ZnO 2-D nanowall structure with around 100 nm thickness, which is composed of tens of nm scale ZnO single crystals, was fabricated through the low temperature chemical solution growth method. Electro Chemical Deposition (ECD) technique was applied to attach the ZnO seed crystals on ITO coated glass substrate. The ZnO nanowall structure was grown in the 0.015 mol$\%$ of aqueous solution of zinc nitrate and hexamethenamine at 60$^{\circ}C$ for 20 - 40 h. The nanowall structure depends on the ECD condition or the applied voltage and duration time. The nanowall shows a photoluminescence around 550 - 700 nm spectrum range.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2008.11a
• /
• pp.422-422
• /
• 2008

본 연구에서, 금 촉매가 4nm 증착된 GaN/$Al_2O_3$ 기판위에 nanowire와 nanowall과 같은 ZnO 나노구조물을 화학기상증착법을 이용하여 합성시켰다. 합성된 ZnO 나노구조물의 형상은 성장시간과 성장온도 조작을 통하여 제어하였다. 합성된 ZnO 나노구조물의 협상을 관찰하기 위해, 전계방출 주사전자현미경을 측정하였다. ZnO 나노구조물은 성장 온도가 $1000^{\circ}C$에서 $1100^{\circ}C$로 증가함에 따라 불균일한 막, nanowire, nanowall 형태로 형상이 점차적으로 변하였으며, 또한 각각의 성장온도에서 성장 시간이 증가함에 따라 나노와이어의 성장이 두드러지게 나타났다. 또한 합성된 ZnO 나노구조물의 결정성과 광학특성을 X-ray diffraction pattern과 상온 photoluminescence spectrum을 이용하여 각각 분석하였다. 이룰 통하여 합성된 ZnO 나노구조물은 wurzite 결정구조를 가지며, 380nm 영역에서 near band edge emission 에 의한 발광 peak와 500~550nm 영역에서 deep level emission에 의한 발광 peak이 나타나는 것을 확인하였다.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.21 no.7
• /
• pp.599-602
• /
• 2008

Growth of well-aligned ZnO nanostructures on various substrates such as GaN, ITO/glass, and sapphire was realized via a simple aqueous solution method at low temperature of $90^{\circ}C$. Morphology of ZnO nanostructures grown on various substrates as function of substrate was studied. It was found that ZnO nanostructures is a strong function of substrate. It was clearly observed that the morphology of ZnO nanostructures could be varied by change of substrate. Morphology, crystallinity, and crystal characteristics were carried out by FE-SEM, synchrotron x-ray scattering measurements, and high-resolution electron microscopy, respectively.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2008.11a
• /
• pp.399-399
• /
• 2008

Synthesis and characterization of ZnO structure such as nanowires, nanorods, nanotube, nanowall, etc. have been studied to multifunctional application such as optical, nanoscale electronic and chemical devices because it has a room-temperature wide band gap of 3.37eV, large exiton binding energy(60meV) and various properties. Various synthesis methods including chemical vapor deposition (CVD), physical vapor deposition, electrochemical deposition, micro-emulsion, and hydrothermal approach have been reported to fabricate various kinds of ZnO nanostructures. But some of these synthesis methods are expensive and difficult of mass production. Wet chemical method has several advantage such as simple process, mass production, low temperature process, and low cost. In the present work, ZnO nanorods are deposited on ITO/glass substrate by simple wet chemical method. The process is perfomed by two steps. One-step is deposition of ZnO seeds and two-step is growth of ZnO nanorods on substrates. In order to form ZnO seeds on substrates, mixture solution of Zn acetate and Methanol was prepared.(one-step) Seed layers were deposited for control of morpholgy of ZnO seed layers by spin coating process because ZnO seeds is deposited uniformly by centrifugal force of spin coating. The seed-deposited samples were pre-annealed for 30min at $180^{\circ}C$ to enhance adhesion and crystallinnity of ZnO seed layer on substrate. Vertically well-aligned ZnO nanorods were grown by the "dipping-and-holding" process of the substrates into the mixture solution consisting of the mixture solution of DI water, Zinc nitrate and hexamethylenetetramine for 4 hours at $90^{\circ}C$.(two-step) It was found that density and morphology of ZnO nanorods were controlled by manipulation of ZnO seeds through rpm of spin coating. The morphology, crystallinity, optical properties of the grown ZnO nanostructures were carried out by field-emission scanning electron microscopy, high-resolution electron microscopy, photoluminescence, respectively. We are convinced that this method is complementing problems of main techniques of existing reports.

• Proceedings of the Materials Research Society of Korea Conference
• /
• 2009.11a
• /
• pp.32.2-32.2
• /
• 2009

21세기의 IT 및 NT를 선두 하게 될 나노소자의개발은 10년 전부터 아주 활발히 연구되고 있다. 최근, 이러한 나노소자의 연구 가운데 주목할 만한 물질이 ZnO 이다. ZnO를 기반으로 한 나노구조는 여러 성장 법으로 성장이 용이하고, 그 물리적, 광학적 특성이 우수하여 광 전소자 응용에 크게 이바지할 물질로 관심을 끌고 있다. 이 가운데 나노선은 소자제작이 용이해 가장 많이 이용되고 있다. 나노선을기반으로 한 소자제작은 bottom-up 공정을 지향하고 있지만, 아직은 top-down 방식이 소자제작의 주류를 이루고 있다. 특히, 나노선 FET 소자제작 시에는 여전히 top-down이 사용되고 있으며, 채널로 사용되는 나노선의 어레이공정은 소자제작 시 가장 큰 어려움으로 대두되고 있다. 하지만, 이러한나노선의 수평 어레이 공정을 감소시킬 구조로 기판에 수평으로 배열된 나노월 구조가 제안되고 있다. 나노월구조는 어레이 공정 수를 크게 감소시켜 생산가격 면에서 큰 이점을 가져올 것으로 생각된다. 하지만, 이러한 ZnO 나노월은 GaN 기판에 한정하여 성장되고 있으며, 일부 Si 기판 위에 성장할지라도나노 사이즈가 아닌 마이크로 사이즈의 거친 표면을 가지는 박막구조로 보고되었다. 때문에, 가격적으로 비싸고 응용성이 제한적인 비전도성 기판을 대신하여, 가격이 저렴하고 응용성이 넓은 Si과 같은 전도성 기판에 나노월 구조를 성장하는 기술이 요구되고 있다. 본 연구에서는 Mg의 도입으로 자발적으로 형성된 비정질 MgO층 위에 상 분리된 MZO 비정질-단결정 층들을 이용하여 어떠한 기판에서도 나노월 구조가 성장할 수 있는 기반 기술을 소개한다.