• Transactions on Electrical and Electronic Materials
• /
• 제9권2호
• /
• pp.67-72
• /
• 2008

Al-doped p-type ZnO thin films were fabricated by RF magnetron sputtering on n-Si (100) and homo-buffer layers in pure oxygen ambient. ZnO ceramic mixed with 2 wt% $Al_2O_3$ was selected as a sputtering target. XRD spectra show that the Al-doped ZnO thin films have ZnO crystal structure. Hall Effect experiments with Van der Pauw configuration show that p-type carrier concentrations are arranged from $1.66{\times}10^{16}$ to $4.04{\times}10^{18}\;cm^{-2}$, mobilities from 0.194 to $198\;cm^2V{-1}s^{-1}$ and resistivities from 0.0963 to $18.4\;{\Omega}cm$. FESEM cross section images of different parts of a p-type ZnO:Al thin film annealed at $800^{\circ}C$ show a compact structure. Measurement for same sample shows that density is $5.40\;cm^{-3}$ which is smaller than theoretically calculated value of $5.67\;cm^{-3}$. Photoluminescence (PL) spectra at 10 K show a shoulder peak of p-type ZnO film at about 3.117 eV which is ascribed to electron transition from donor level to acceptor level (DAP).

• 한국산학기술학회논문지
• /
• 제8권5호
• /
• pp.1057-1061
• /
• 2007

본 연구에서는 AlAs와 ZnO target을 사용하여 RF magnetron sputtering 시스템에서 layer-by-layer 방법으로 증착한 ZnO 박막의 특성에 대하여 조사하였다. 또한 열처리 전에 $H_2O_2$용액을 사용한 처리가 박막 특성에 미치는 영향도 조사하였다. 연구 결과 열처리 조건에 따라 n-형 또는 p-형 박막이 형성되는 것으로 관찰되었다. 이러한 결과는 박막의 전도 형태를 임의로 수정할 수 있음을 의미하는 동시에 박막 특성의 열적 불안정성을 암시하는 것이기도 하다. 144시간까지 스트레스를 인가한 후 측정한 박막 특성 결과 열처리 과정 중 발생하는 이러한 박막 특성 변화는 열처리 전 박막을 30% $H_2O_2$용액에 1분간 처리함으로써 억제할 수 있는 것으로 관찰되었다.

• 한국전기전자재료학회:학술대회논문집
• /
• 한국전기전자재료학회 2007년도 추계학술대회 논문집
• /
• pp.410-411
• /
• 2007

To investigate the ZnO LED which are interested in the next generation of short wavelength LEDs and Lasers, the ZnO thin films were deposited by RF magnetron sputtering system. The p-type ZnO thin film, fabricated by means of the ampoule-tube method, was used to make the ZnO p-n junction, and its characteristics was analyzed. The ampoule-tube method was used to make the p-type ZnO based on the As diffusion, and the hall measurement was used to confirm that the p-type is formed. the current-voltage characteristics of the ZnO p-n junction were measured to confirm the rectification characteristics of a typical p-n junction and the low leakage voltage characteristics. Analysis of ZnO LED V-I curve will provide a very useful technology for producing the UV ZnO LED and ZnO-based devices.

• Transactions on Electrical and Electronic Materials
• /
• 제12권4호
• /
• pp.169-173
• /
• 2011

In this study, Al-N codoped p-type zinc oxide (ZnO) thin films were deposited on Si and homo-buffer layer templates in a mixture of $N_2$ and $O_2$ gas with ceramic ZnO:(2 wt% $Al_2O_3$) as a sputtering target using DC- magnetron sputtering. X-ray diffraction spectra of two-theta diffraction showed that all films have a predominant (002) peak of ZnO Wurtzite structure. As the $N_2$ fraction in the mixed $N_2$ and $O_2$ gases increased, field emission secondary electron microscopy revealed that the surface appearance of codoped films on Si varied from smooth to textured structure. The p-type ZnO thin films showed carrier concentration in the range of $1.5{\times}10^{15}-2.93{\times}10^{17}\;cm^{-3}$, resistivity in the range of 131.2-2.864 ${\Omega}cm$, and mobility in the range of $3.99-31.6\;cm^2V^{-1}s^{-1}$ respectively.

• 한국전기전자재료학회:학술대회논문집
• /
• 한국전기전자재료학회 2007년도 하계학술대회 논문집 Vol.8
• /
• pp.55-56
• /
• 2007

The p-type ZnO thin film, fabricated by means of the ampoule-tube method, was used to make the ZnO p-n junction, and its characteristics was analyzed. The ampoule-tube method was used to make the p-type ZnO based on the As diffusion, and the hall measurement was used to confirm that the p-type is formed. the current-voltage characteristics of the ZnO p-n junction were measured to confirm the rectification characteristics of a typical p-n junction and the low leakage voltage characteristics. Using the ampoule-tube to fabricate the p-type ZnO will provide a very useful technology for producing the UV ZnO LED and ZnO-based devices.

• 한국태양에너지학회 논문집
• /
• 제39권1호
• /
• pp.33-40
• /
• 2019

Al-doped ZnO (AZO) thin films were synthesized on Si(100) wafers via plasma enhanced metal organic chemical vapor deposition (PE-MOCVD) method using diethyl zinc (DEZ) and N-methylpyrrolidine alane (MPA) as precursors. Effects of Al/Zn mixing ratio, plasma power on the surface morphology, crystal structure, and electrical property were investigated with SEM, XRD and 4-point probe measurement respectively. Growth rate of the film decreased slightly with increasing the Al/Zn mixing ratio, however electrical property was enhanced and resistivity of the film decreased greatly about 2 orders from $9.5{\times}10^{-1}$ to $8.0{\times}10^{-3}{\Omega}cm$ when the Al/Zn mixing ratio varied from 0 to 9 mol%. XRD analysis showed that the grain size increased with increasing the Al/Zn mixing ratio. Growth rate and electrical property were enhanced in a mild plasma condition. Resistivity of AZO film decreased down to $7.0{\times}10^{-4}{\Omega}cm$ at an indirect plasma of 100 W condition which was enough value to use for the transparent conducting oxide (TCO) material.

• 한국전기전자재료학회:학술대회논문집
• /
• 한국전기전자재료학회 2007년도 하계학술대회 논문집 Vol.8
• /
• pp.68-69
• /
• 2007

We have prepared p-type ZnO:Al films in pure oxygen ambient on n-type Si (100) and homo buffer layers by RF magnetron sputtering system. Hall effect measurement shows that the film annealed at $600^{\circ}C$ possesses p-type conductivity and the film annealed $800^{\circ}C$ does not. PL spectra show different properties of p- and n-type ZnO film. The corresponding peaks of PL spectra of p- and n-type show at about same positions. The intensities of high photon energy of n-type film on buffer shows decreasing tendency.

• 한국신재생에너지학회:학술대회논문집
• /
• 한국신재생에너지학회 2011년도 춘계학술대회 초록집
• /
• pp.130.2-130.2
• /
• 2011

본 연구에서는 RF magnetron sputtering을 이용하여 실리콘 박막 태양전지용 ZnO:Al 전면전극을 제작하고 다양한 식각조건에 따른 ZnO:Al 박막의 표면형상 변화와 함께 전기적 및 광학적 특성 변화를 조사하였다. pin 구조를 갖는 실리콘 박막 태양전지의 효율 향상을 위해서는 입사광의 산란효과에 따른 광포획 증가가 필수적이며 이를 위하여 ZnO:Al 전면전극의 표면텍스처링 형성이 필요하다. 식각용액으로는 HCl과 HF 등을 사용하였으며 식각용액 농도 및 식각시간을 변화시켰다. 식각 후의 ZnO:Al 박막의 표면형상은 SEM(Scanning Electron Microscope)과 AFM(Atomic Force Microscope)을 이용하여 분석을 하였고, UV-visible-nIR spectrometer를 이용하여 총 투과도 및 산란 투과도를 측정하였다. 이 외에도 four-point probe 및 Hall measurement를 이용하여 전기적 특성 변화를 조사하였다. 다양한 식각조건에 따라 제조된 ZnO:Al 박막 위에 실리콘 박막 태양전지를 제작하여 전면전극의 표면형상에 따른 태양전지 성능변화를 비교 분석하였다.

• 한국전기전자재료학회:학술대회논문집
• /
• 한국전기전자재료학회 2007년도 추계학술대회 논문집
• /
• pp.442-443
• /
• 2007

Al-N co-doped ZnO films were fabricated on n-Si (100) and homo-buffer layers in the mixture of oxygen and nitrogen at $450^{\circ}C$ by magnetron sputtering. Target was ZnO ceramic mixed with $2wt%Al_2O_3$. XRD spectra show that as-grown and $600^{\circ}C$ annealed films are prolonged along crystal c-axis. However they are not prolonged in (001) plane vertical to c-axix. The films annealed at $800^{\circ}C$ are not prolonged in any directions. Codoping makes ZnO films unidirectional variation. XPS show that Al content hardly varies and N escapes with increasing annealing temperature from $600^{\circ}C\;to\;800^{\circ}C$. The electric properties of as-grown films were tested by Hall Effect with Van der Pauw configuration show some of them to be p-type conduction.

• 한국전기전자재료학회논문지
• /
• 제24권3호
• /
• pp.177-181
• /
• 2011

We have studied structural, optical, and electrical properties of the Al-doped ZnO (AZO) thin films being usable in transparent conducting oxides. The AZO thin films were deposited on the corning 1737 glass plate by the RF magnetron sputtering system. To find optimal properties of AZO for transparent conducting oxides, the RF power in sputtering process was varied as 40 W, 60 W, and 80 W, respectively. As RF power increased, the crystallinity of AZO thin film was decreased, the optical bandgap of AZO thin film increased. The transmittance of the film was over 80% in the visible light range regardless of the changes in RF power. The measurement of Hall effect characterizes the whole thin film as n-type, and the electrical property was improved with increasing RF power. The structural, optical, and electrical properties of the AZO thin films were affected by Al dopant content in AZO thin film.