• Korean Journal of Materials Research
• /
• v.20 no.12
• /
• pp.676-680
• /
• 2010

Most TCOs such as ITO, AZO(Al-doped ZnO), FTO(F-doped $SnO_2$) etc., which have been widely used in LCD, touch panel, solar cell, and organic LEDs etc. as transparent electrode material reveal n-type conductivity. But in order to realize transparent circuit, transparent p-n junction, and introduction of transparent p-type materials are prerequisite. Additional prerequisite condition is optical transparency in visible spectral region. Oxide based materials usually have a wide optical bandgap more than ~3.0 eV. In this study, single-phase transparent semiconductor of $SrCu_2O_2$, which shows p-type conductivity, have been synthesized by 2-step solid state reaction at $950^{\circ}C$ under $N_2$ atmosphere, and single-phase $SrCu_2O_2$ thin films of p-type TCOs have been deposited by RF magnetron sputtering on alkali-free glass substrate from single-phase target at $500^{\circ}C$, 1% $H_2$/(Ar + $H_2$) atmosphere. 3% $H_2$/(Ar + $H_2$) resulted in formation of second phases. Hall measurements confirmed the p-type nature of the fabricated $SrCu_2O_2$ thin films. The electrical conductivity, mobility of carrier and carrier density $5.27{\times}10^{-2}S/cm$, $2.2cm^2$/Vs, $1.53{\times}10^{17}/cm^3$ a room temperature, respectively. Transmittance and optical band-gap of the $SrCu_2O_2$ thin films revealed 62% at 550 nm and 3.28 eV. The electrical and optical properties of the obtained $SrCu_2O_2$ thin films deposited by RF magnetron sputtering were compared with those deposited by PLD and e-beam.

• Proceedings of the Materials Research Society of Korea Conference
• /
• 2010.05a
• /
• pp.54.1-54.1
• /
• 2010

산화물 기반의 TFT는 유리, 금속, 플라스틱 등 기판 종류에 상관없이 균일한 제작이 가능하며, 상온 및 저온에서 대면적으로 제작이 가능하고, 저렴한 비용으로 제작 가능하다는 장점 때문에 최근 많은 연구가 이루어지고 있다. 현재 TFT 물질로 많이 연구되고 있는 산화물은 ZnO (3.4 eV)나 InOx (3.6 eV), GaOx (4.9 eV), SnOx(3.7 eV)등의 물질과 각각의 조합으로 구성된 재료들이 주로 사용되고 있으며, 가장 많은 연구가 이루어진 ZnO 기반의 TFT는 mobility와 switching 속도에서 우수한 특성을 보이나, 트렌지스터의 안정성이 떨어지는 것으로 보고 되고 있다. 그러나 IGZO 물질의 경우 결정학적으로 비정질이며 상온 및 저온에서 대면적으로 제작이 가능하고, 높은 전자 이동도의 특성을 가지고 있는 장점 때문에 최근 차세대 산화물 트렌지스터로 각광받고 있다. IGZO TFT 소자의 경우 Ag, Au, In, Pt, Ti, ITO 등 다양한 전극 물질이 사용되고 있는데, 이들 중 active channel과 ohmic contact을 이루는 Al, Ti, Ag의 적용을 통해 향상된 성능을 얻을 수 있다. 하지만 이들 전극 재료는 TFT 소자 제작시 필수적인 열처리 공정에 노출되면서 active channel 과 전극 사이 계면에 문제점을 야기할 수 있다. 특히, Ti의 경우 산화가 잘되기 때문에 전극계면에 TiO2를 형성하여 contact resistance의 큰 영향을 미치는 것으로 보고 되고 있다. 본 연구에서는 ohmic 전극재료인 Ti 또는 Ti/Au를 적용하여 TFT 소자 제작 및 특성에 대한 평가를 진행했으며, 열처리에 따른 전극과 IGZO 계면 사이의 미세구조와 전기적인 특성간의 상관관계를 연구하였다. 이를 통해, 소자 제작 공정을 최적화하고 신뢰성 있는 소자 특성을 얻을 수 있었다.

• Electrical & Electronic Materials
• /
• v.7 no.3
• /
• pp.243-251
• /
• 1994

ITO(Indium Tin Oxide) film with thickness of 1500.angs. was prepared by an e-beam evaporator onto a glass and a p-type InP wafer (100) LEC grown Zn-doped p=2.3*10$\^$16/cm$\^$-3/), in which the components of ITO used for evaporation source were hot pressed pellets 1 mole% ln$\_$2/O$\_$3/+9 mole% SnO$\_$2/, and evaporated in O$\_$2/ ambient. The optimum conditions to preparation of ITO thin film were the substrate temperature of 350.deg. C, the injected oxygen pressure of 2*10$\^$-4/ torr, and the evaporation speed of 0.2-0.3.angs./sec, respectively. In these optimum conditions, the resistivity and the carrier concentration were 5.3*10$\^$-3/ .ohm.-cm, 6.5*10$\^$20/cm$\^$-3/, and the transmittance was over 80%. From the results of J-V measurements in ITO/p-InP structure solar cells, the higher pressure of injected oxygen, the more open circuit voltage. The efficiency of ITO/p-InP solar cell without the grid line contact, prepared by the optimum evaporation conditions, was 7.19%. By using the grid line contact, the efficiency, the open circuit voltage, the short circuit current density, the fill factor, the series resistance, and the shunt resistance were 8.5%, 0.47V, 29.48 mAcm$\^$-2/ , 61.35%, 3.ohm., and 26.6k.ohm., respectively.

• Journal of the Korean institute of surface engineering
• /
• v.47 no.5
• /
• pp.239-243
• /
• 2014

The electrical and optical properties of amorphous In-Tin-Zinc-Oxide(ITZO) deposited at room temperature using rf-magnetron sputtering were investigated. The amorphous ITZO thin films were obtained at the composition of In:Sn:Zn = 6:2:2, 4:3:3, and 2:4:4, but the ITZO (8:1:1) showed a crystalline phase of bixbyite structure of In2O3. The resistivity of ITZO could be controlled by oxygen pressure in the sputtering ambient. The resistivity of post-annealed ITZO thin films exhibited the dependence on the amount of Indium. Optical energy band gap and transmittance increased as the amount of indium in ITZO increased. For the device application with ITZO, the bottom-gated thin-film transistor using ITZO as a active channel layer was fabricated. It showed a threshold voltage of 1.42V and an on/off ratio of $5.63{\times}10^7$ operated with saturation field-effect mobility of $14.2cm^2/V{\cdot}s$.

• Journal of the Korean Applied Science and Technology
• /
• v.33 no.4
• /
• pp.734-740
• /
• 2016

The micron-sized indium zinc tin oxide (IZTO) particles were prepared by spray pyrolysis from aqueous precursor solution for indium, zinc, and tin and organic additives such as citric acid (CA) and ethylene glycol (EG) were added to aqueous precursor solution for indium, zinc, and tin. The obtained IZTO particles prepared by spray pyrolysis from the aqueous solution without organic additives had spherical and filled morphologies, whereas the IZTO particles obtained with organic additives had more hollow and porous morphologies. The micron-sized IZTO particles with organic additives were changed fully to nano-sized IZTO particles, whereas the micron-sized IZTO particles without organic additives were not changed fully to nano-sized IZTO particle after post-treatment at $700^{\circ}C$ for 2 hours and wet-ball milling for 24 hours. Surface resistances of micron-sized IZTO's before post-heat treatment and wet-ball milling were much higher than those of nano-sized IZTO's after post-heat treatment and wet-ball milling. From IZTO with composition of 80 wt. % $In_2O_3$, 10 wt. % ZnO, and 10 wt. % $SnO_2$ which showed a smallest surface resistance IZTO after post-heat treatment and wet-ball milling, thin films were deposited on glass substrates by pulsed DC magnetron sputtering, and the electrical and optical properties were investigated.

• Proceedings of the Materials Research Society of Korea Conference
• /
• 2010.05a
• /
• pp.53.2-53.2
• /
• 2010

지금까지 능동 구동 디스플레이의 TFT backplane에 사용하고 있는 채널 물질로는 수소화된 비정질 실리콘(a-Si:H)과 저온 폴리실리콘(low temperature poly-Si)이 대표적이다. 수소화된 비정질 실리콘은 TFT-LCD 제조에 주로 사용되는 물질로 제조 공정이 비교적 간단하고 안정적이며, 생산 비용이 낮고, 소자 간 특성이 균일하여 대면적 디스플레이 제조에 유리하다. 그러나 a-Si:H TFT의 이동도(mobility)가 1 cm2/Vs이하로 낮아 Full HD 이상의 대화면, 고해상도, 고속 동작을 요구하는 UD(ultra definition)급 디스플레이를 개발하는데 있어 한계 상황에 다다르고 있다. 또한 광 누설 전류(photo leakage current)의 발생을 억제하기 위해서 화소의 개구율(aperture ratio)을 감소시켜야하므로 패널의 투과율이 저하되고, 게이트 전극에 지속적으로 바이어스를 인가 시 TFT의 문턱전압(threshold voltage)이 열화되는 문제점을 가지고 있다. 문제점을 극복하기 위한 대안으로 근래 투명 산화물 반도체(transparent oxide semiconductor)가 많은 관심을 얻고 있다. 투명 산화물 반도체는 3 eV 이상의 높은 밴드갭(band-gap)을 가지고 있어 광 흡수도가 낮아 투명하고, 광 누설 전류의 영향이 작아 화소 설계시 유리하다. 최근 다양한 조성의 산화물 반도체들이 TFT 채널 층으로의 적용을 목적으로 활발하게 연구되고 있으며 ZnO, SnO2, In2O3, IGO(indium-gallium oxide), a-ZTO(amorphous zinc-tin-oxide), a-IZO (amorphous indium-zinc oxide), a-IGZO(amorphous indium-galliumzinc oxide) 등이 그 예이다. 이들은 상온 또는 $200^{\circ}C$ 이하의 낮은 온도에서 PLD(pulsed laser deposition)나 스퍼터링(sputtering)과 같은 물리적 기상 증착법(physical vapor deposition)으로 손쉽게 증착이 가능하다. 특히 이중에서도 a-IGZO는 비정질임에도 불구하고 이동도가 $10\;cm2/V{\cdot}s$ 정도로 a-Si:H에 비해 월등히 높은 이동도를 나타낸다. 이와 같이 a-IGZO는 비정질이 가지는 균일한 특성과 양호한 이동도로 인하여 대화면, 고속, 고화질의 평판 디스플레이용 TFT 제작에 적합하고, 뿐만 아니라 공정 온도가 낮은 장점으로 인해 플렉시블 디스플레이(flexible display)의 backplane 소재로서도 연구되고 있다. 본 실험에서는 rf sputtering을 이용하여 증착한 a-IGZO 박막에 대하여 열처리 조건 변화에 따른 a-IGZO 박막들의 광학적, 전기적 특성변화를 살펴보았고, 이와 더불어 a-IGZO 박막을 TFT에 적용하여 소자의 특성을 분석함으로써, 열처리에 따른 Transfer Curve에서의 우리가 요구하는 Threshold Voltage(Vth)의 변화를 관찰하였다.