• The Journal of Advanced Prosthodontics
• /
• 제5권2호
• /
• pp.92-97
• /
• 2013

PURPOSE. All-ceramic crowns are subject to fracture during function. To minimize this common clinical complication, zirconium oxide has been used as the framework for all-ceramic crowns. The aim of this study was to compare the fracture strengths of two computer-aided design/computer-aided manufacturing (CAD/CAM) zirconia crown systems: Lava and Digident. MATERIALS AND METHODS. Twenty Lava CAD/CAM zirconia crowns and twenty Digident CAD/CAM zirconia crowns were fabricated. A metal die was also duplicated from the original prepared tooth for fracture testing. A universal testing machine was used to determine the fracture strength of the crowns. RESULTS. The mean fracture strengths were as follows: $54.9{\pm}15.6$ N for the Lava CAD/CAM zirconia crowns and $87.0{\pm}16.0$ N for the Digident CAD/CAM zirconia crowns. The difference between the mean fracture strengths of the Lava and Digident crowns was statistically significant (P<.001). Lava CAD/CAM zirconia crowns showed a complete fracture of both the veneering porcelain and the core whereas the Digident CAD/CAM zirconia crowns showed fracture only of the veneering porcelain. CONCLUSION. The fracture strengths of CAD/CAM zirconia crowns differ depending on the compatibility of the core material and the veneering porcelain.

• 대한치과보철학회지
• /
• 제44권3호
• /
• pp.275-283
• /
• 2006

Statement of problem. There have been many studies about marginal discrepancy of single restorations made by various systems and materials. However most of the statistical inferences are not definite because of sample size, measurement number, measuring instruments, etc, and there have been few studies about the marginal fit of the Digident CAD/ CAM zirconia ceramic crowns. Purpose. The purpose of this study was to compare the marginal fit of the anterior single restorations made by using the Digident CAD / CAM zirconia ceramic crowns with metal-ceramic restorations and to obtain more accurate information by using a large enough sample size and by making sufficient measurements per specimen. Material and Methods. The crowns were made from one extracted maxillary central incisor pre-pared with a 1mm shoulder margin and $6^{\circ}$ taper walls by milling machine. The in vitro marginal discrepancies of the digident CAD / CAM zirconia ceramic crowns and control groups(metal ceramic crowns) were evaluated and compared. Twenty crowns per each system were fabricated. Measurements of a crown were recorded at 50 points that were randomly selected for marginal gap evaluation. Parametric statistical analysis was performed for the results. Conclusion. Within the limitations of this in vitro study, the following conclusions were drawn: 1. Mean gap dimensions and standard deviations at the marginal opening for maxillary incisal crowns were $88{\pm}10{\mu}m$ for the control (metal-ceramic crowns), $92{\pm}4{\mu}m$ for Digident CAD / CAM zirconia ceramic crowns. 2. Marginal gap between Digident CAD / CAM zirconia ceramic crowns and metal ceramic crowns did not show significant difference (P>.05). 3. The Digident CAD/ CAM zirconia ceramic crowns and metal ceramic crowns showed clinically acceptable marginal discrepancy.

• 대한치과보철학회지
• /
• 제45권1호
• /
• pp.12-20
• /
• 2007

Purpose: The purpose of this study was to compare the fracture strength of the zirconia monolithic all-ceramic crowns according to the thickness (0.5mm, 0.8mm, 1.1mm) and metal-ceramic crowns (1.0mm, 1.5mm) Material and method: Twelve crowns for each of 3 zirconia crown groups were fabricated using CAD/CAM system (Kavo, Germany) and twelve crowns for each of 2 metal-ceramic crown groups were made by the conventional method. All crowns were luted to the metal dies using resin cement. Half of the specimens were exposed to thermocycling ($5-55^{\circ}C$, 1 Hz) and cyclic loading (300,000 cycles, 50N). Subsequently, all crowns were mounted on the testing jig in a universal testing machine. The load was directed at the center of crown with perpendicular to the long axis of each specimen until catastrophic failure occurred. Analysis of variance and Tukey multiple comparison test (P<.05) were used for statistical analysis of all groups, and paired t-test (P<.05) was followed for statistical comparison between each groups' fracture load before and after cyclic loading. Results: 1. The fracture strength of the zirconia monolithic crowns and the metal-ceramic crown increased as thickness increased (P<.05). 2. The cyclic loading and thermocycling significantly decreased the fracture strength of the zirconia monolithic crowns (P<.05). 3. The standard deviation of fracture strength of the zirconia monolithic crowns was very low. Conclusion: The fracture strength of the zirconia monolithic crowns for the posterior area tends to be higher with thickness increased and 0.8mm or over in thickness is recommended to have similar or over the fracture strength of metal-ceramic crowns.

• The Journal of Advanced Prosthodontics
• /
• 제5권3호
• /
• pp.319-325
• /
• 2013

PURPOSE. The objective of this study was to determine the effect of the color of a background substructure on the overall color of a zirconia-based all-ceramic crown. MATERIALS AND METHODS. Twenty one posterior zirconia crowns were made for twenty subjects. Seven premolar crowns and six molar crowns were cemented onto abutments with metal post and core in the first and second group. In the third group, eight molar crowns were cemented onto abutments with a prefabricated post and composite core build-up. The color measurements of all-ceramic crowns were made before try-in, before and after cementation. A repeated measure ANOVA was used for a statistical analysis of a color change of all-ceramic crowns at ${\alpha}$=.05. Twenty four zirconia specimens, with different core thicknesses (0.4-1 mm) were also prepared to obtain the contrast ratio of zirconia materials after veneering. RESULTS. $L^*$, $a^*$, and $b^*$ values of all-ceramic crowns cemented either on a metal cast post and core or on a prefabricated post did not show significant changes (P>.05). However, the slight color changes of zirconia crowns were detected and represented by ${\Delta}E{^*}_{ab}$ values, ranging from 1.2 to 3.1. The contrast ratios of zirconia specimens were 0.92-0.95 after veneering. CONCLUSION. No significant differences were observed between the $L^*$, $a^*$, and $b^*$ values of zirconia crowns cemented either on a metal cast post and core or a prefabricated post and composite core. However, the color of a background substructure could affect the overall color of posterior zirconia restorations with clinically recommended core thickness according to ${\Delta}E{^*}_{ab}$ values.

• The Journal of Advanced Prosthodontics
• /
• 제10권1호
• /
• pp.65-72
• /
• 2018

PURPOSE. The aim of this in vitro study was to investigate the fracture resistance under chewing simulation of implant-supported posterior restorations (crowns cemented to hybrid-abutments) made of different all-ceramic materials. MATERIALS AND METHODS. Monolithic zirconia (MZr) and monolithic lithium disilicate (MLD) crowns for mandibular first molar were fabricated using computer-aided design/computer-aided manufacturing technology and then cemented to zirconia hybrid-abutments (Ti-based). Each group was divided into two subgroups (n=10): (A) control group, crowns were subjected to single load to fracture; (B) test group, crowns underwent chewing simulation using multiple loads for 1.2 million cycles at 1.2 Hz with simultaneous thermocycling between $5^{\circ}C$ and $55^{\circ}C$. Data was statistically analyzed with one-way ANOVA and a Post-Hoc test. RESULTS. All tested crowns survived chewing simulation resulting in 100% survival rate. However, wear facets were observed on all the crowns at the occlusal contact point. Fracture load of monolithic lithium disilicate crowns was statistically significantly lower than that of monolithic zirconia crowns. Also, fracture load was significantly reduced in both of the all-ceramic materials after exposure to chewing simulation and thermocycling. Crowns of all test groups exhibited cohesive fracture within the monolithic crown structure only, and no abutment fractures or screw loosening were observed. CONCLUSION. When supported by implants, monolithic zirconia restorations cemented to hybrid abutments withstand masticatory forces. Also, fatigue loading accompanied by simultaneous thermocycling significantly reduces the strength of both of the all-ceramic materials. Moreover, further research is needed to define potentials, limits, and long-term serviceability of the materials and hybrid abutments.

• The Journal of Advanced Prosthodontics
• /
• 제12권5호
• /
• pp.283-290
• /
• 2020

PURPOSE. The present study aimed to evaluate the clinical applicability of monolithic zirconia (MZ) crowns of different thickness via determination of fracture resistance and marginal fit. MATERIALS AND METHODS. MZ crowns with 0.5, 0.8, 1.0, and 1.5 mm thickness and porcelain fused to metal (PFM) crowns were prepared, ten crowns in each group. Marginal gaps of the crowns were measured. All crowns were aged with thermal cycling (5 - 55℃/10000 cycle) and chewing simulator (50 N/1 Hz/lateral movement: 2 mm, mouth opening: 2 mm/240000 cycles). After aging, fracture resistance of crowns was determined. Statistical analysis was performed with one-way ANOVA and Tukey's HDS post hoc test. RESULTS. Fracture loads were higher in the PFM and 1 mm MZ crowns compared to 0.5 mm and 0.8 mm crowns. 1.5 mm MZ crowns were not broken even with the highest force applied (10 kN). All marginal gap values were below 86 ㎛ even in the PFM crowns, and PFM crowns had a higher marginal gap than the MZ crowns. CONCLUSION. The monolithic zirconia exhibited high fracture resistance and good marginal fit even with the 0.5 mm thickness, which might be used with reduced occlusal thickness and be beneficial in challengingly narrow interocclusal space.

• 대한소아치과학회지
• /
• 제43권2호
• /
• pp.176-186
• /
• 2016

본 연구는 전치부 지르코니아 전장관을 위한 적정 치아 삭제량을 조사하기 위해 3차원 스캐너를 이용, 지르코니아와 다른 유치 전장관들의 크기와 형태를 분석하였다. 상악 좌측 유중절치, 유측절치 지르코니아 전장관과 금속관의 내/외면, 레진관의 외면을 스캔하여, 근원심경이 유사한 세 종류의 전장관을 한 군으로 만들어 분석하였다. 외면에서 모든 중절치, 1번 측절치 지르코니아 전장관이 같은 군의 전장관 중 가장 큰 순설경을 나타냈다. 내면에서 지르코니아 전장관은 금속관에 비해 근원심경 0.7-1.0 mm, 치관길이는 1 mm 가량 작았으며, 순설경은 중절치에서는 더 컸으나 측절치에서는 더 작았다. 비교결과, 지르코니아 전장관은 절단면 2.5-3.0mm, 근원심 1.5-2 mm, 순면 0.5-1 mm, 설면결절을 장축에 평행하게 삭제 후 측절치에서만 0.5 mm 설면삭제를 시행하는 것을 제안할 수 있다.

• 대한치과보철학회지
• /
• 제44권2호
• /
• pp.157-164
• /
• 2006

Purpose: The purpose of this study was to compare the fracture strength of the zirconia monolithic all-ceramic crowns according to the thickness(0.5 mm, 0.8 mm, 1.1 mm) and IPS Empress II ceramic crown of 1.5 mm thickness. Material and method: Eight crowns for each of 3 zirconia crown groups were fabricated using CAD/CAM system(Kavo, Germany) and eight Empress II crowns were made from silicone mold and wax pattern. Each crown group was finished in accordance with the specific manufacturer s instruction. All crowns were luted to the metal dies using resin cement and mounted on the testing jig in a universal testing machine. The load was directed at the center of crown with perpendicular to the long axis of each specimen until catastrophic failure occurred. Analysis of variance and Tukey multiple comparison test(p<.05) were applied to the data. Results and Conclusion: 1. The fracture strength of the zirconia monolithic all-ceramic crown was higher thickness increased(p<.05). 2 The fracture strength of 1.1 mm thickness zirconia monolithic all-ceramic crown was higher than the fracture strength of 1.5 mm thickness IPS Empress II crown(p<.05). 3. The fracture strength of 0.5 mm thickness zirconia monolithic all-ceramic crown exceeded maximum occlusal forces.

• 대한소아치과학회지
• /
• 제50권3호
• /
• pp.307-317
• /
• 2023

심미성에 대한 요구가 증가함에 따라 유구치 수복을 위한 지르코니아 전장관은 더 활발하게 사용되고 있으나, 지르코니아 전장관으로 수복한 치아를 장기간 추적 관찰하거나 다른 재료와 비교한 연구는 많지 않다. 따라서 이 연구의 목적은 인접면 우식증에 대한 지르코니아 전장관과 기성금속관의 36개월 동안의 생존율을 비교하여 평가하고, 각 기성관의 수복 실패 양상을 분석하는 것이다. 2017년부터 2019년까지 조선대학교 치과병원 소아치과와 두 개의 개인 치과의원에 내원하여 두 기성관으로 수복 치료를 받은 498명 환자에 대한 1,061개의 유구치에 대한 전자의무기록지와 방사선 사진을 수집하고 분석하였다. 생존분석 결과, 기성금속관으로 수복한 치아의 생존율이 지르코니아 전장관에 비해 유의하게 높았다. 치수 치료 시행 여부를 나눠 생존 분석을 시행한 결과, 치수 치료를 시행하지 않은 경우, 기성금속관의 생존율이 지르코니아 전장관에 비해 유의하게 높았던 반면, 치수 치료를 시행한 경우에는 두 기성관의 생존율에 유의한 차이가 없었다. 기성금속관의 주된 수복실패 원인은 비정상적 치근 흡수 또는 치근단 투과상 병소의 발생이었고, 지르코니아 전장관의 경우 수복물의 탈락이었다. 이 연구는 임상가들에게 구치부 기성관 재료 선택 시 참고 자료로 활용될 수 있을 것이라 생각된다.

• The Journal of Advanced Prosthodontics
• /
• 제7권6호
• /
• pp.475-483
• /
• 2015

PURPOSE. The objective of this study was to evaluate the influence of various cement types on the stress distribution in monolithic zirconia crowns under maximum bite force using the finite element analysis. MATERIALS AND METHODS. The models of the prepared #46 crown (deep chamfer margin) were scanned and solid models composed of the monolithic zirconia crown, cement layer, and prepared tooth were produced using the computer-aided design technology and were subsequently translated into 3-dimensional finite element models. Four models were prepared according to different cement types (zinc phosphate, polycarboxylate, glass ionomer, and resin). A load of 700 N was applied vertically on the crowns (8 loading points). Maximum principal stress was determined. RESULTS. Zinc phosphate cement had a greater stress concentration in the cement layer, while polycarboxylate cement had a greater stress concentration on the distal surface of the monolithic zirconia crown and abutment tooth. Resin cement and glass ionomer cement showed similar patterns, but resin cement showed a lower stress distribution on the lingual and mesial surface of the cement layer. CONCLUSION. The test results indicate that the use of different luting agents that have various elastic moduli has an impact on the stress distribution of the monolithic zirconia crowns, cement layers, and abutment tooth. Resin cement is recommended for the luting agent of the monolithic zirconia crowns.