• Journal of the Microelectronics and Packaging Society
• /
• v.29 no.1
• /
• pp.61-66
• /
• 2022

This study is to increase the surface area and maximize the effect of the catalyst by coating a nanometersized metal catalyst material on the anode layer using atomic layer deposition (ALD) technology. ALD process is known to produce uniform films with well-controlled thickness at the atomic level on substrates. We measured the performance by coating metals (Ni) on Ni/YSZ, which is the most widely known anode material for solid oxide fuel cells. ALD coatings began to show a decrease in cell performance over 3 nm coatings.

• Journal of the Korean Ceramic Society
• /
• v.36 no.8
• /
• pp.791-798
• /
• 1999

The preparation method of yttria-stabilized zirconia(YSZ) thin film for an anode support type solid oxide fuel cell(SOFC) by electrophoretic deposition(EPD) and dip-coating was studied. And the difference in both preparation method was investigated through basic understanding of processing parameters which may significantly affect weight microstruxcture and defect of film. In dip-coating the thickness of film increased with time until 30 s and then the weight of film decreased with time due to particle falling off from the coagulated film. In EPD although the weight of film increased with time and applied constant-current sagging of the film was observed when the applied current was less that 0.035 mA/$cm^2$ and more than 120 s. Since YSZ thin film by EPD on porous substrate was dense smooth and homogeneous it was expected to be suitable for the electrolyte of an anode support type SOFC.

• Journal of the Korean institute of surface engineering
• /
• v.50 no.6
• /
• pp.460-464
• /
• 2017

As increasing thermal efficiency of the gas turbine, the performance improvement of thermal barrier coatings is also becoming important. Ytrria stabilized zirconia(YSZ) is the most popular materials for ceramic top coating because of its low thermal conductivity. In order to enhance the performance of thermal barrier coatings for hot sections in the gas turbine, suspension plasma spraying was developed in order to feed nano-sized powders. YSZ coatings formed by suspension plasma spraying showed better performance than YSZ coatings due to its exclusive microstructure. In this research, two YSZ coatings were deposited by suspension vacuum plasma spraying at 400 mbar and 250 mbar. Microstructures of YSZ coatings were analyzed by scanning electron image(SEM) on each spraying conditions, respectively. Crystalline structure transformation was not detected by X-ray diffraction. Thermal conductivity of suspension vacuum plasma sprayed YSZ coatings were measured by laser flash analysis. Thermal conductivity of suspension vacuum plasma sprayed YSZ coatings containing horizontally oriented nano-sized pores and vertical cracks showed $0.6-1.0W/m{\cdot}K$, similar to thermal conductivity of YSZ coatings formed by atmospheric plasma spraying.

• Korean Journal of Materials Research
• /
• v.9 no.8
• /
• pp.792-797
• /
• 1999

The 8mol.%Y$_2$$O_3$-$ZrO_2$mainly employed as an electrolyte of solid oxide fuel cells(SOFCs) shows excellent electrical properties but has a weakness in the mechanical properties. Since the electrolyte of SOFCs requires both good electrical and mechanical properties, this study was conducted to meet both requirements. The electrolyte thin films were produced on the LSM(cathode material) substrate of a cell and Si wafer. Four electrolyte film types of single layer and the multiple layer, consisting of 3-YSZ(3mol.%$Y_2$$O_3$) with excellent mechanical properties and 8-YSZ with the excellent electric conduction, were produced by electron beam coating technology. Ther crystal structure and the mechanical properties were also analysed. As the results of the study, the 3-YSZ thin film turned out to be in the tetragonal, partially monoclinic phase, while the 8-YSZ thin film showed the cubic phase. The residual stress in the multiple layer was lower than that of the single layer. The microhardness of the multiple layer was similar to that of the existing 8-YSZ single layer both before and after annealing treatment.

• Proceedings of the Membrane Society of Korea Conference
• /
• 2002.05a
• /
• pp.35-41
• /
• 2002

Dense oxygen ionic conducting materials can be used for oxygen separation membranes at high temperatures. However, they show relatively low permeation flux because of their large resistances. To reduce resistances and improve the oxygen permeation flux, thin dense yttria-stabilized-zirconia (YSZ)/Pd composite dual-phase membranes were fabricated by a new approach that combines the reservoir method and chemical vapor deposition (CVD). A thin porous YSZ layer was coated on a porous alumina support by dip-coating the YSZ suspension. A continuous Pd phase was formed inside pores of the YSZ layer by the reservoir method. The residual pores of the YSZ/Pd layer were plugged with yttria/zirconia by CVD to ensure the gas tightness of the membranes. The oxygen permeation fluxes through these composite membrane were 2.0$\times$10$^{-8}$ mol/cm$^2$.s and 4.8$\times$10$^{-8}$ mol/cm$^2$.s at 105$0^{\circ}C$ when air and oxygen were used as the permeate gases, respectively. These oxygen permeation values are about 1 order of magnitude higher than those of pure YSZ membranes prepared under similar conditions.

• Journal of the Korean institute of surface engineering
• /
• v.31 no.1
• /
• pp.12-23
• /
• 1998

The Thermal Barrier Coating(TBC) has been used to improve the heat barrier and tribological properties of the aircraft engine and the automobile engine in high temperature. Especially, the high temperature tribological propertied of the cylinder haed and the piston crown of diesel engine was emphasized. Therefore, the purpose of this work was to evaluate the microstructure, tribological propeer in high tempearmal shock resistance and bonding strength of five layer functionally gradient TBC for the applications. The five layerwere composed with 100% ceramic insulating later, 75(ceramic):25 (metal) layer, 50:50 layer, 25:75 layer and 100% metal bonding layer to redude the thermal stress. the YSL and MSL poweders were the insulation ceramics powers. The NiCrAly, Inconel625 and SUS powders were the bonding and mixingg powders for plasma spray process. According to the result of high temperature wear test, the wera resistance of YSZ/NiCrAlY siytem was most out standing at 600 and $800^{\circ}C$. At $400^{\circ}C$, the wear resistance of YSZ/Inconel system was better than others. Wear volume at other temperature because of the low temperature degration of zirconia. The thermal shock mechanism of 5 later is the vertical crack gegration in insulating layer. this means that the initial cracks were generated in the top layer, and then developed into the composite layers during thermal shock test. Finally, these cracks werereached to the interface of coating and substrate and also, these vertioal cracks join with the horizontal cracks of the each layers. The bonding strength of YSZ/NiCrAlY and YSZ/Inconel 5 layer system is better than other 5layer systems. The theramal shock resistance of thermal barrier coating s with 5 layer system is better than that of 3 layers and 2 layers.

• Proceedings of the KWS Conference
• /
• 2003.05a
• /
• pp.111-113
• /
• 2003

The existing heating unit is indirect-heating method that make use or the nichrome wire or halogen lamp. The indirect-heating method has the demerits of long warming time, high power consumption and many organization parts. In this study, the heating unit of direct-heating method manufactured as being the thermal spray coating of conductive heating material on the surface of heating unit in order to improve the demerits of indirect-heating method. And YSZ added Ni-20Cr that had moderate electrical resistivity was chosen of the conductive heating material.

• Korean Journal of Materials Research
• /
• v.32 no.4
• /
• pp.200-209
• /
• 2022

In this study, defects generated in the YSZ coating layer of the IN738LC turbine blade are investigated using an optical microscope and SEM/EDS. The blade YSZ coating layer is composed of a Y-Zr component top coat layer and a Co component bond coat layer. A large amount of Cr/Ni component that diffused from the base is also measured in the bond coat. The blade hot corrosion is concentrated on the surface of the concave part, accompanied by separation of the coating layer due to the concentration of combustion gas collisions here. In the top coating layer of the blade, cracks occur in the vertical and horizontal directions, along with pits in the top coating layer. Combustion gas components such as Na and S are contained inside the pits and cracks, so it is considered that the pits/cracks are caused by the corrosion of the combustion gases. Also, a thermally grown oxide (TGO) layer of several ㎛ thick composed of Al oxide is observed between the top coat and the bond coat, and a similar inner TGO with a thickness of several ㎛ is also observed between the bond coat and the matrix. A PFZ (precipitate free zone) deficient in γ' (Ni₃Al) forms as a band around the TGO, in which the Al component is integrated. Although TGO can resist high temperature corrosion of the top coat, it should also be considered that if its shape is irregular and contains pore defects, it may degrade the blade high temperature creep properties. Compositional and microstructural analysis results for high-temperature corrosion and TGO defects in the blade coating layer used at high temperatures are expected to be applied to sound YSZ coating and blade design technology.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.25 no.7
• /
• pp.552-557
• /
• 2012

In this study, we have coated the inner surface of YSZ channel using LSM powder ink through depressurization process for making the cathode of a stacked planar-type SOFC module. To coat the surface of YSZ channel uniformly, we tried to find the optimum manufacturing condition for LSM ink. We used four different dispersants (BYK series) and two different solvents (ethanol and DMF) to make the LSM ink. It was revealed that the ink made with the ethanol solvent and the BYK-111 dispersant has the lowest viscosity, relatively low contact angle and most excellent dispersibility. After depressurizing a chamber filled with LSM ink and sintered YSZ channel, we have found that the YSZ channel was uniformly coated with LSM cathode. The LSM ink with 25 vol% BYK-111 showed the most uniform coating.

• Journal of the Korean institute of surface engineering
• /
• v.30 no.3
• /
• pp.183-190
• /
• 1997

Fabrication and crystallization characteristics of yttria($T_2O_3$) stabilized zirconia(YSZ) thin film by sol-gel process were studied. YSZ sol was synthesized with zirconium n-propoxide($Zr(OC_3H_7)_4)$) and yttrium nitrate pentahydrate ($Y(NO_3)_3.5H_2O$). YSZ film was prepared by depositing the polymeric sol on porous $Al_2O_3$ substrate by spin-coating, and the film characteristics were investigated by FRIR, TG-DTA, XRD, DSC, optical microscopy and SEM. The film topology was uniform and cracks were not found. It was found that the annealing temperature and the concentration of stabilizer affect the crystallization of YSZ film. The YSZ film began to crystallize from amorphous to tetragonal phase at 40$0^{\circ}C$, and it was not converted to cubic structure until $1100^{\circ}C$. It seemed that the grains were formed over $700^{\circ}C$and the average grain size was obtained about 0.2$\mu\textrm{m}$.