• 한국세라믹학회지
• /
• 제33권6호
• /
• pp.693-699
• /
• 1996

YIG precursor powder was obtained by homogeneous precipitation in chloride salt solution by thermal decom-position of urea. It was found that ferric ions precipitated prior to yttrium ions. The precipitate was minute and spherical in shape. The precipitate formed consisted of the mixture of amorphous and ferric oxyhydroxide. Crystallization of YIG was proceeded by solid state reaction of intermediate YFeO3 and Fe2O3 in the temperature range of 85$0^{\circ}C$ to 140$0^{\circ}C$. Single phase of YIG was obtained by heat-treatment of the powder at 140$0^{\circ}C$ for 6 hrs in air. The powder calcined was molded into pellets and sintered in air. The maximum density of 4,92 g/cm3(95.1% of theoretical density) was obtainable for the pellet sintered at 145$0^{\circ}C$ using the powder calcined at 90$0^{\circ}C$.

• 한국세라믹학회지
• /
• 제36권3호
• /
• pp.293-300
• /
• 1999

고주파 마그네트론 스퍼터법을 이용한 YIG(yttrium iron garnet)박막 제조시 기판유형, 기판온도, 스퍼터전력, 스퍼터가스 등의 증착변수와 증착후 열처리 조건이 YIG 박막의 결정성, 화학조성, 미세구조 그리고 자기적 특성에 미치는 영향에 대하여 고찰하였다. 75$0^{\circ}C$ 이상의 온도에서 수행한 증착후 열처리에 의하여 비정질 박막이 결정화되었으며, 특히 GGG(gadolinium gallium garnet)기판 위에 제조된 박막은 강한 (111)우선배향성을 나타냈다. 박막조성은 스퍼터가스 내의 산소분율에 민감하게 영향을 받았으며, 산소분율이 20%인 스퍼터가스를 사용하여 제조된 박막은 Y2.88Fe3.84O12의 조성을 나타내었다. 증착후 열처리 온도가 90$0^{\circ}C$로부터 110$0^{\circ}C$로 증가함에 따라, GGG 기판위의 박막의 표면거칠기는 2.5nm에서 40nm로 증가하였으며, 보자력과 강자성 공명 선폭은 감소하였다.

• 한국재료학회지
• /
• 제6권3호
• /
• pp.275-281
• /
• 1996

YIG 전구체 분말은 요소의 열분해반응을 이용한 균일침전법에 의해서 질산염으로부터 제조하였다. 침전은 철이온이 먼저 침전한 후 이트륨이온이 침전하는 과정으로 이루어졌다. YGI전구체 분말은 철산화물과 비정질로 구성되어 있으며 그 분말의 대략적인 화학식은 2.5Fe2O3.Y3(OH)9-2x(CO3)x.nH2O로 되어있다. YIG 전구체 분말의 열분해과정은 dehydration, 철산화물의 recrystallization, yttrium carbonate 및 yttrium oxide의 형성과 고상반응등 여러단계로 구성되어 있다. 열처리온도가 증가함에 따라 Y2O3와 Fe2O3의 고상반응에 의해 YFeO3 intermediate을 경유해서 YIG상이 형성됨을 확인하였다. 단일상의 YIG는 120$0^{\circ}C$에서 6시간 공기중에서 소성함에 의해서 얻을 수 있었다.

• 한국세라믹학회지
• /
• 제40권9호
• /
• pp.855-858
• /
• 2003

Liquid Phase Epitaxy (LPE)법으로 Yttrium Iron Garnet (YIG:Y$_3$Fe$_{5}$O$_{12}$) 단결정 후막을 성장시킬 때 PbO계 응제에서는 Pb 이온이 성장되는 결정내로 혼입되어 성장된 막의 격자상수를 증가시키고, 일축 자기이방성 상수값(Ku)을 변화시키거나 전기 전도도를 변화시킨다. 또한 광 흡수율을 증가시키는 등의 성장된 막의 물성에 악영향을 미친다. 열처리 후 Pb 이온의 휘발로 인한 결정내의 농도감소로 성장된 단결정 후막의 격자상수가 평균 0.0115$\AA$ 감소하였다.

• 한국세라믹학회지
• /
• 제33권9호
• /
• pp.1031-1037
• /
• 1996

• 한국자기학회:학술대회 개요집
• /
• 한국자기학회 2015년도 임시총회 및 하계학술연구발표회
• /
• pp.140-140
• /
• 2015

• 한국전기전자재료학회:학술대회논문집
• /
• 한국전기전자재료학회 2009년도 추계학술대회 논문집
• /
• pp.142-142
• /
• 2009

Bismuth-substituted yttrium iron garnet(Bi-YIG; $Bi_xY_{3-x}Fe_5O_{12}$, x=0, 0.5, 1.0, 1.5, 2.0) thin films were fabricated on glass substrates using a metal organic decomposition (MOD) method. The dielectric property was measured by NSMM(Near-field scanning microwave microscopy) system that operating frequency is 4 Ghz. The obtained reflection coefficient $S_{11}$ of the Bi:YIG thin films with different bismuth concentration was increased as the bismuth concentration increased due to the lattice mismatch and vacancy of ions because of a lager ionic radius of bismuth ion than yttrium ion.

• Journal of Magnetics
• /
• 제12권3호
• /
• pp.129-132
• /
• 2007

Bismuth-substituted yttrium iron garnet (Bi:YIG, $Bi_{0.5}Y_{2.5}Fe_5O_{12}$) films were deposited with aerosol deposition method and their magnetic and optical properties were investigated as a function of annealing temperature. Since the ceramic films deposited with aerosol deposition method have not a perfect crystal structure due to non-uniform internal stress occurred by mechanical collision during their deposition, the post annealing could be a key process to release its internal stress and to improve its micro structure for optimizing the magnetic and magneto-optic properties of films. The crystallinity of Bi: YIG film was improved with increase of annealing temperature, and the saturation magnetization increased up to 87 emu/cc at $800^{\circ}C$. The Faraday rotation increased up to $1.4deg/{\mu}m$ by annealing at $700^{\circ}C$ around the wavelength of $0.5{\mu}m$. The optical transmittance of the Bi:YIG film was also improved in visible region.

• 한국결정성장학회지
• /
• 제2권2호
• /
• pp.1-1
• /
• 1992

YIG는 분해용융을 하므로 FZ법을 개량한 TSFZ법을 적용하여 YIG단결정을 성장시켰다. 최적성장조건은 성장속도 1mm/hr, 상호역방향 회전속도 30rpm이었으며 소결 및 결정성장시 산화분위기를 필요로 하였고 성장된 결정의 질은 소결정도에 의해 많은 영향을 받았다. Melt내 기포의 생성은 철이온과 산소와의 반응에 의해 발생되었으며 기포의 밀도는 성장속도가 빨라질수록 증가하였다. 성장속도는 1mm/hr 이상일 경우에는 Cell Growth가 발생하였으며 결정의 가장자리에서 전위밀도가 증가하였다. 또한 성장된 결정에서는 제2상으로 Orthoferrite가 관찰되었다.

• 한국결정성장학회지
• /
• 제1권1호
• /
• pp.39-50
• /
• 1991

적외선 집중가열 방식의 FZ장치를 이용하여 floation zone 결정 성장기술을 변형한 traveling solvent floating zone(TSFZ)기술로 yttrium iron garnet(YIG: Y3Fe5O12) 단결정을 성장하였다. 또한 TSFZ기술을 확립하기 위하여 단결정 성장시 미치는 여러 가지 영향을 조사하였다. 성장된 YIG결정은 직경이 5~6mm, 길이가 15~36mm이었으며, 이때 성장조건은 성장속도 1mm/h, 회전속도 30rpm, gas flow rate 0.2 1/min, zone aspect ratio 0.9~1, convexity 0.29이었다.