• Progress in Superconductivity and Cryogenics
• /
• v.8 no.3
• /
• pp.9-12
• /
• 2006

Batch type co-evaporation EDDC (Evaporation using Drum in Dual Chambers) system was recently manufactured to fabricate 100m - long SmBCO superconducting coated conductor. As a preliminary study before the fabrication of long tape. short CC samples have been fabricated using the EDDC system and their crystal texture and $I_c$ properties were investigated. $1.2 {\mu}m$-thick SmBCO layers were deposited on $CeO_2/YSZ/CeO_2$ buffered Ni-W tapes. $I_c$ of 128A/cm-w and corresponding $J_c$ of $1.1 MA/cm^2$ at 77K in self-field were obtained for SmBCO CC tape. In-field property of SmBCO CC was confirmed to be better than that of YBCO deposited by PLD.

• Progress in Superconductivity and Cryogenics
• /
• v.9 no.1
• /
• pp.9-13
• /
• 2007

Coated conductor(CC) is recently in actively progress for the research and development, and its can be used various stabilizer lot the specific requirements for each application. Among various superconducting applications, coated conductor applied to superconducting fault current limiters(SFCLS) bypasses fault current to its stabilizer, where the surge is abruptly reduced ; thus, stainless steel, which has large resistivity can be a suitable stabilizer for SFCLS. Despite high n-value of the YBCO, CC stabilized with stainless steel did not effectively limit the first peak fault current. In the short circuit test results of AMSC's 344S, a half period delay was observed between the fault and the generation of resistance(60Hz). In this paper, we performed short-circuit experiments with stacked and unstacked CC and compared the test results to analyze effective fault current limiting characteristics. we compared time of the generated resistance as the fault current limiting characteristics and made the samples one is the stacked CC and the other is unstacked CC. These samples were used equal numbers of pieces of CC. In addition, comparison and analysis was made for the stacked structure by measuring fault current limiting characteristics with respect to thermal insulation by impregnating with epoxy resin.

• Progress in Superconductivity and Cryogenics
• /
• v.11 no.2
• /
• pp.7-10
• /
• 2009

Effects of $BaCO_3$ purity on the superconducting properties of top seeded melt growth (TSMG) processed $Y_{1+x}Ba_2Cu_3O_{7-y}$ (Y1+x, x=0.1 and 0.2) superconductors were investigated. $YBa_2Cu_3O_{7-y}$ (Y123) powder prepared using $BaCO_3$ with 99.75% purity and commercially available Y123 powder of 99.9% were used for the fabrication of single Y123 grain superconductors. $T_c$ values of the Y1+x samples prepared using low purity Y123 powder were slightly lower than those of the samples prepared using a high purity powder. In addition to the lower $T_c$, an anomalous peak effect in the intermediate magnetic fields was observed in Y1+x samples prepared using the low purity $BaCO_3$ powder. The slight decrease in $T_c$ and the anomalous peak effect are ascribed to the possible incorporation of a Y123 phase with impurity elements such as strontium and calcium included in the $BaCO_3$powder of 99.7%. The result suggests that the low purity $BaCO_3$ powder of a low price can be used as a raw power for the fabrication of single grain YBCO bulk superconductors.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2003.07a
• /
• pp.565-568
• /
• 2003

2세대 초전도 선재로 알려져 있는 $YBa_2Cu_3O_{7-\delta}$ coated conductor는 금속모재/완충층/초전도층/보호층의 구조를 가진다. 2개 이상의 산화물 다층 박막으로 이루어진 완충층은 금속기판의 집합조직을 초전도층까지 전달하는 역할, 금속기판의 금속이 초전도층으로 확산되어 초전도층의 전기적 특성을 열화시키는 것을 막아주는 확산장벽으로의 역할 등을 수행한다. 1차 완충층은 금속기판의 집합조직을 유지하여야하며, 금속기판의 산화를 방지하면서 증착 되어야 한다. coated conductor 제조를 위한 첫 단계로 Pulsed Laser Deposition법을 이용하여 cube texture된 Ni 기판 위에 $Y_2O_3$ 박막을 증착 하였다. 최적의 증착 조건을 찾기 위해 증착 챔버의 산소 및 $H_2/Ar$ 혼합가스 분압과 기판온도를 변화시키면서 증착 하였다. $Y_2O_3$층의 (100) 집합조직은 기판온도 $600{\sim}700^{\circ}C$와 산소 분압 $0.01{\sim}0.1mTorr$에서 증착된 Y2O3 박막에서 금속기판과 유사한 집합조직을 얻을 수 있었다. 최적의 증착 조건에서 $Y_2O_3$ (222) ${\Phi}-scan$의 full width at half maximum (fwhm)이 $11^{\circ}$이고 (400) ${\omega}-scan$ fwhm은 $6^{\circ}$이었다.