• Journal of the Korean Chemical Society
• /
• v.50 no.3
• /
• pp.237-242
• /
• 2006

Nowadays, LEDs has been applied to the luminescent devices of various fields because of the invention of high efficient blue chip. Recently, especially, the white LEDs composed of InGaN blue chips and a yellow phosphor (YAG:Ce3+) have been investigated extensively. With the exception of YAG:Ce3+ phosphor, however, there are no reports on yellow phosphor that has significant emission in the 450~470 nm excitation range and this LED system is the rather low color rendering index due to their using two wavelength. Hence, we have attempted to synthesize thiogallate phosphors that efficiently under the long wavelength excitation range in the present case. Among those phosphors, we have synthesized Sr2Ga2S5:Eu2+ phosphor by change the host material of SrGa2S4:Eu2+ which is well known phosphor and we investigated the luminescent properties. In order to obtain the harmlessness and simplification of the synthesis process, sulfide materials and mixture gas of 5 % H2/95 % N2 were used instead of the CS2 or H2S gas. The prepared phosphor shows the yellow color peaking at the 550 nm wavelength and it possible to emit efficiently under the broad excitation band in the range of 300~500 nm. And this phosphor shows high luminescent intensity more than 110 % in comparison with commercial YAG:Ce3+ phosphor and it can be applied for UV LED due to excitation property in UV region.

• Korean Journal of Optics and Photonics
• /
• v.24 no.2
• /
• pp.64-70
• /
• 2013

In this paper, two white light emitting diodes(LEDs) were manufactured by using two kinds of yellow phosphor, YAG:Ce and $(Sr,Ba)_2SiO_4:Eu$, and their spectroscopic properties were compared and analyzed. We found that the asymmetric double sigmoidal function can be applied to both white LEDs to obtain the center wavelength, the half width, and the skewness parameters. According to this analysis, the half width of the emitting spectrum of silicate phosphor was smaller than that of YAG phosphor, indicating smaller color rendering index. However, the silicate phosphor exhibited better color stability depending on the driving current than the YAG phosphor. The current dependence of the luminous efficacy of both white LEDs was investigated, which showed that efficacy decreased monotonically with current. The efficacy of the silicate-based white LED was lower than that of the YAG-based LED by about 10~12 lm/W.

• Current Optics and Photonics
• /
• v.1 no.6
• /
• pp.613-617
• /
• 2017

Due to optimal advances such as chromatic performance, durability, low power consumption, high efficiency, long-lifetime, and excellent environmental friendliness, white LEDs (WLEDs) are widely used in vehicle front lighting, backlighting, decorative lighting, street lighting, and even general lighting. In this paper, the remote packaging WLEDs (RP-WLEDs) with bi-layer red-emitting $Sr_2Si_5N_8:Eu^{2+}$ and yellow-emitting YAG:Ce phosphor was proposed and investigated. The simulation results based on the MATLAB software and the commercial software Light Tools indicated that the color rendering index (CRI) of bi-layer phosphor RP-WLEDs had a significant increase. The CRI had a considerable increase from 72 to 94. In conclusion, the results showed that bi-layer red-emitting $Sr_2Si_5N_8:Eu^{2+}$ and yellow-emitting YAG:Ce phosphor could be a prospective approach for manufacturing RP-WLEDs with enhanced optical properties.

• Bulletin of the Korean Chemical Society
• /
• v.33 no.4
• /
• pp.1141-1146
• /
• 2012

Ce-doped $Y_3Al_5O_{12}$ (YAG:Ce) phosphor powder was prepared using a ${NO_3}^-$-malonic acid-$NH_4NO_3-NH_3{\cdot}H_2O$ system. The YAG:Ce precursor was ignited at $240^{\circ}C$ and the resulting powder contained YAG:Ce crystallites (42%) - active in the visible region at 460 nm - amorphous particles (53%) - inactive at visible wavelengths - and less than 3% oxide (3%) crystallite impurities. The impurities transformed to acitive YAG:Ce crystallites at above $800^{\circ}C$. At above $1000^{\circ}C$, the amorphous phase became YAG phase and isolated $Ce_2O$ crystallites emerged. The powder particles comprised < $4{\mu}m$ secondary aggregates of 20 nm primary particles. The thermal dusting of the secondary particles coincided with the aggregation of the secondary particles at above $900^{\circ}C$.

• Journal of the Korean Ceramic Society
• /
• v.56 no.1
• /
• pp.71-76
• /
• 2019

Monochromatic amber phosphor in glasses (PiGs) for automotive LED applications were fabricated with $YAG:Ce^{3+}$, $CaAlSiN_3:Eu^{2+}$ phosphors and Pb-free silicate glass. After synthesis and thickness-thinning process, PiGs were mounted on high-power blue LED to make monochromatic amber LEDs. PiGs were simple mixtures of 566 nm yellow YAG, 615 nm red $CaAlSiN_3:Eu^{2+}$ phosphor and transparent glass frit. The powders were uniaxially pressed and treated again through CIP (cold isostatic pressing) at 200 MPa for 20 min to increase packing density. After conventional thermal treatment at $550^{\circ}C$ for 30 min, PiGs were applied by using GPS (gas pressure sintering) to obtain a fully dense PiG plate. As the phosphor content increased, the density of the sintered body decreased and PiGs containing 30 wt% phosphor had full sintered density. Changes in photoluminescence spectra and color coordination were investigated by varying the ratio of $YAG/CaAlSiN_3$ and the thickness of the plates. Considering the optical spectrum and color coordinates, PiG plates with $240{\mu}m$ thickness showed a color purity of 98% and a wavelength of about 605 nm. Plates exhibit suitable optical characteristics as amber light-converting material for automotive LED applications.

• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.31 no.5
• /
• pp.212-217
• /
• 2021

The applicability of the white LED from the blue LED of the coating film as a binder for surface and curved coatings were confirmed. The particle size of YAG is D₅₀: 9~10 ㎛, and the crystal structure is garnet (Y₃Al₅O₁₂), cubic. The coating film had no cracks, at the same time, the silica sol was uniformly coated with YAG phosphor, and the YAG content and thickness in the coating film showed a tendency to increase up to 40 ㎛ in proportion to the increase in the amount added. Furthermore, as the YAG content increased, the PL emission intensity increased and the color coordinate shift toward the end of the chromatic locus curve was confirmed.

• Current Photovoltaic Research
• /
• v.8 no.2
• /
• pp.50-53
• /
• 2020

GaN based photoelectrode has shown good potential owing to its better chemical stability and tunable bandgap with materials such as InN and AlN. Tunable bandgap allows GaN to make the maximum utilization of solar spectrum, which could improve photoelectrode performance. However, the problems about low photoelectrode performance and photo-corrosion still remain. In this study, we attempt to investigate the photoelectrochemical (PEC) properties of phosphor application to InGaN photoelectrode. Experimental result shows YAG:Ce³⁺ and beta-SiALON phosphor result in the highest photoelectrode performance of InGaN.

• Journal of the Semiconductor & Display Technology
• /
• v.18 no.1
• /
• pp.10-14
• /
• 2019

In this study, we synthesized two $Y_3Al_5O_{12}:Ce^{3+}$ phosphors ($7{\mu}m$-sized and $2{\mu}m$-sized YAG) with different sizes by controlling particles sizes of starting materials of the phosphors for white LED. In the smaller one ($2{\mu}m$-sized YAG), its photoluminescence intensity in the reflective mode was 63 % that of the bigger one ($7{\mu}m$-sized YAG); the quantum efficiencies were 93 % and 70 % for the smaller and the bigger ones. Two kinds of white LED packages with the same color coordinates were fabricated with a blue package (chip size $53{\times}30$) and two phosphors. The luminous flux of the white LED package with the smaller YAG phosphor was 92 % of that with the bigger one, indicating that the quantum efficiency of phosphor dispersed inside LED package was higher than that of the pure powder. It was consistently confirmed by the optical simulation (LightTools 6.3). It is notable according to the optical simulation that the white LED with the smaller phosphor showed 24 % higher luminous efficiency. If the smaller one had the same quantum efficiency as the bigger one (~93 %). Therefore, it can be suggested that the higher luminous efficiency of white LED can be possible by reducing the particle size of the phosphor along with maintaining its similar quantum efficiency.

• Journal of Powder Materials
• /
• v.19 no.3
• /
• pp.220-225
• /
• 2012

YAG:Ce yellow phosphor particles were synthesized by spray pyrolysis with changing the solution properties and their luminous properties, crystal structure, and morphological changes were studied by using PL measurement, XRD, and SEM analysis. It was clear that the solution properties significantly affected the crystal phase, crystallite size, the PL intensity, and the morphology of YAG:Ce particles. At low calcination temperature, the addition of urea only to the spray solution was helpful to form a pure YAG phase without any impurity phases, as the result, the highest luminescence intensity was achieved at the calcination temperature of $900^{\circ}C$. When the calcination temperatures were larger than $1300^{\circ}C$, however, the YAG particles prepared without any additive showed the highest luminescent intensity. Regardless of the solution conditions, the emission intensity of YAG:Ce particles prepared by spray pyrolysis showed a linear relation with the crystallite size. In terms of the morphology of YAG:Ce particles, the addition of both DCCA and $NH_4OH$ to the spray solution was effective to prepare a spherical and dense structured YAG particles.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 1999.11a
• /
• pp.525-528
• /
• 1999

The luminescence of bismuth and cerium doped yttrium aluminum based Phosphors $Y_{3}$/Al$_{5}$/O$_{12}$ and (Y$_{0.8}$/Gd$_{0.2}$)$_3$Al$_{5}$/O$_{12}$ prepared by a solid-state reaction method were studied. These samples which were fired at 1, 20$0^{\circ}C$ show the characteristic X-ray diffraction patters for the main phase(420) of YAG. This study indicates that the both flux and remained bismuth after the firing phosphor materials give rise to affect the photoluminescence properties. Therefore, it was investigated that both the XRD patterns arid the PL properties were affected by the controlling experimental process variables.riables.les.