• Journal of the Korean Ceramic Society
• /
• v.38 no.10
• /
• pp.936-941
• /
• 2001

The influence of the ${Al_2}{O_3}$ particle size on flaw tolerance of the $ZrO_2/{Al_2}{O_3}$ composites prepared by mixing 5.31 mol% ${Y_2}{O_3}$-4.45 mol% ${Nb_2}{O_5}$-90.31 mol% $ZrO_2$ and ${Al_2}{O_3}$ was investigated. The composites exhibited rising R-curve behavior and plateau fracture toughness of 7.9 and $8.8MPam^{1/2}$ for the additions of 20 vol% of 0.2 and $2.8{\mu}m$ ${Al_2}{O_3}$ particles, respectively. The difference in the fracture toughness resistance was attributed mainly to the grain size of tetragonal $ZrO_2$ phase in the composites, which scaled with the ${Al_2}{O_3}$ particle size.

• Journal of the Korean Ceramic Society
• /
• v.37 no.4
• /
• pp.354-358
• /
• 2000

Tetragonal (t)-ZrO2/Al2O3 composites doped with Y2O3, Nb2O5, and Fe2O3 ((Y, Nb, Fe)-TZP/Al2O3) were prepared over the range containing Fe2O3 from 0.1 to 0.5 mol% with 0.1 mol% intervals to evaluate the effect of Fe2O3 addition on chromaticity, hydrothermal stability, and mechanical property of the composites. After autoclaving for 20 h at 18$0^{\circ}C$ under 3.5 MPa water vapor pressure, no tlongrightarrowm phase transformation was observed probably due to the preferential solid solubility of Fe2O3 in Al2O3, the presence of the rigid Al2O3 particles, and the inherent phase stability of (Y, Nb)-TZP. The optimized strength and the fracture toughness of the composite were 700 MPa and 8.5 MPa.m1/2, respectively, when 0.1 mol% Fe2O3 was added. The composites have shown a gradual color change from a slightly white ivory to a pale yellowish brown with increasing the Fe2O3 concentration.

• Journal of Technologic Dentistry
• /
• v.34 no.1
• /
• pp.11-21
• /
• 2012

Purpose: Densification and mechanical properties of dental zirconia ceramics were evaluated by different sintering methods. Materials and Methods: Y-TZP zirconia block(Kavo $Everest^{(R)}$ ZS blank, Kavo dental GmbH, Bismarckring, Germany) was used in this study. Sintering were performed in heat sintering furnace and microwave sintering furnace, and then experimented and analyzed on a change in densification according to the sintering time, a change in densification according to thickness, flexural strength and micro-structure in zirconia specimens. Results: Microwave sintering was very effective in considerable mechanical properties such as flexural strength and bulk density was drastically increased than conventional electric heating method. It is also shown that microwave sintering time was faster and more economical than common method to be present in qualities which equal or exceed. Conclusion: It will be important to seek the accurate sintering condition of dental zirconia by microwave sintering method and the continuous research is necessary for the study of relationship between sintering methods and mechanical properties.

• Restorative Dentistry and Endodontics
• /
• v.41 no.3
• /
• pp.167-175
• /
• 2016

Objectives: Endodontically treated teeth with insufficient tooth structure are often restored with esthetic restorations. This study evaluated the cytotoxicity and biological effects of yttria partially stabilized zirconia (Y-TZP) blocks in combination with several dental cements. Materials and Methods: Pairs of zirconia cylinders with medium alone or cemented with three types of dental cement including RelyX U200 (3M ESPE), FujiCEM 2 (GC), and Panavia F 2.0 (Kuraray) were incubated in medium for 14 days. The cytotoxicity of each supernatant was determined using 3-(4,5-dimethylthiazole- 2-yl)-2,5-diphenyltetrazolium bromide (MTT) assays on L929 fibroblasts and MC3T3-E1 osteoblasts. The levels of interleukin-6 (IL-6) mRNA were evaluated by reverse transcription polymerase chain reaction (RT-PCR), and IL-6 protein was evaluated by enzyme-linked immunosorbent assays (ELISA). The data were analyzed using one-way ANOVA and Tukey post-hoc tests. A p < 0.05 was considered statistically significant. Results: The MTT assays showed that MC3T3-E1 osteoblasts were more susceptible to dental cements than L929 fibroblasts. The resin based dental cements increased IL-6 expression in L929 cells, but reduced IL-6 expression in MC3T3-E1 cells. Conclusions: Zirconia alone or blocks cemented with dental cement showed acceptable biocompatibilities. The results showed resin-modified glass-ionomer based cement less produced inflammatory cytokines than other self-adhesive resin-based cements. Furthermore, osteoblasts were more susceptible than fibroblasts to the biological effects of dental cement.

• The Journal of Advanced Prosthodontics
• /
• v.8 no.2
• /
• pp.137-143
• /
• 2016

PURPOSE. Grinding with less stress on 3Y-TZP through proper selection of methods and instruments can lead to a long-term success of prosthesis. The purpose of this study was to compare the phase transformation and physical properties after zirconia surface grinding with 3 different grinding burs. MATERIALS AND METHODS. Forty disc-shaped zirconia specimens were fabricated. Each Ten specimens were ground with AllCeramic SuperMax (NTI, Kahla, Germany), Dura-Green DIA (Shofu Inc., Kyoto, Japan), and Dura-Green (Shofu Inc., Kyoto, Japan). Ten specimens were not ground and used as a control group. After the specimen grinding, XRD analysis, surface roughness test, FE-SEM imaging, and biaxial flexural strength test were performed. RESULTS. After surface grinding, small amount of monoclinic phase in all experimental groups was observed. The phase change was higher in specimens, which were ground with Dura-Green DIA and AllCeramic SuperMax burs. The roughness of surfaces increased in specimens, which were ground with Dura-Green DIA and AllCeramic SuperMax burs than control groups and ground with Dura-Green. All experimental groups showed lower flexural strength than control group, but there was no statistically significant difference between control group and ground with Dura-Green DIA and AllCeramic SuperMax burs. The specimens, which were ground with Dura-Green showed the lowest strength. CONCLUSION. The use of dedicated zirconia-specific grinding burs such as Dura-Green DIA and AllCeramic SuperMax burs decreases the grinding time and did not significantly affect the flexural strength of zirconia, and therefore, they may be recommended. However, a fine polishing process should be accompanied to reduce the surface roughness after grinding.

• Journal of Technologic Dentistry
• /
• v.35 no.1
• /
• pp.19-27
• /
• 2013

Purpose: The aim of this research was to evaluate the shear bond strength of different zirconia veneering ceramics with and without liner glass materials to yttria partially-stabilized tetragonal zirconia polycrystalline(Y-TZP). Methods: Five co mmercial zirconia veneering ceramics were used in this study, E-Max(EM), Creation ZI(CR), Cercon ceram kiss(CE), Triceram(TR) and Zirkonzahn ICE(ZI). All samples were prepared according to manufacturer's instructions. Experimental industrially manufactured Y-TZP ceramic blocks(diameter: 2.7 mm; height: 13.5 mm) were used in this study. Shear bond strength between zirconia ceramic coping and zirconia veneering ceramics were evaluated by the push-shear bond test. The fracture load data were analyzed using ANOVA and Scheffe's test(${\alpha}$=0.05). The fractured surfaces of zirconia core ceraimc and zirconia veneering ceramics were observed using a scanning electron microscope(SEM). Results: The mean shear bond strengths ranged from 20 MPa ($20.12{\pm}6.34$ MPa) to 66.6 MPa ($66.62{\pm}10.01$ MPa). The Triceram(TRG) showed the highest value and Creation ZI(CR) showed the lowest value. In all groups, Zirconia liner and glass material groups was significantly higher shear bond strength than without liner(P<0.05), with the exception of Cercon ceram kiss(CE)groups. Conclusion: Zirconia bonding materials may have the advantage of improved bond strength between zirconia ceramic core and veneering ceramics.

• The Journal of the Korea Contents Association
• /
• v.18 no.10
• /
• pp.361-367
• /
• 2018

The purpose of this study was to evaluate the influence of hydrofluoric acid etching treatment on the bonding strength of yttria-stabilized tetragonal zirconia polycrystal(Y-TZP). Four groups of zirconia-resin cement specimens were prepared; 1) ZGS group (zirconia, no treatment), 2) ZGSH group (zirconia, hydrofluoric acid etching treatment) 3) H-ZGS group (Hybrid zirconia, no treatment) 4) H-ZGSH group (Hybrid zirconia, hydrofluoric acid etching treatment). The shear bond strength between zirconia and porcelain was measured using a Instron Universal Testing Machine(Model DBBP-500, Instron Corporation, Kyonggi, Korea). Data were statistically analyzed using independent t-test and two-way ANOVA(${\alpha}=0.05$). The ceramic-resin cement bonding strength was affected by hydrofluoric acid etching treatment(p<0.05). Digital microscope examination of the fracture surface showed mixed failures with adhesive and cohesive types in hydrofluoric acid etching treatment with treated zirconia and hybrid zirconia groups.

• The Journal of Korean Academy of Prosthodontics
• /
• v.46 no.3
• /
• pp.227-237
• /
• 2008

STATEMENT OF PROBLEM: Zirconium oxide can be a substitute to titanium as implant materials to solve the esthetic problems of dark color in the gingival portion of implant restorations. PURPOSE: This study was performed to define attachment and growth behavior of osteoblast- like cells cultured on grooved surfaces of zirconium oxide and evaluate the genetic effect of zirconium oxide surfaces using the reverse transcriptase-polymerase chain reaction (RT-PCR). MATERIAL AND METHODS: MC3T3-E1 cells were cultured on (1) commercially pure titanium discs with smooth surface (T group), (2) yttrium-stabilized tetragonal zirconia polycrystal (Y-TZP) with machined surface (ZS group), and (3) Y-TZP with $100{\mu}m$ grooves (ZG group). Cell proliferation activity was evaluated through MTT assay and cell morphology was examined by SEM. The mRNA expression of Runx2, alkaline phosphatase, osteocalcin, TGF-${\beta}1$, IGF-1, G3PDH in E1 cells were evaluated by RT-PCR. RESULTS: From the MTT assay, after 48 hours of adhesion of MC3T3-E1 cells, the mean optical density value of T group and ZG group significantly increased compared to the ZS group. SEM images of osteoblast-like cells showed that significantly more cells were observed to attach to the grooves and appeared to follow the direction of the grooves. After 24 hours of cell adhesion, more spreading and flattening of cells with active filopodia formation occurred. Results of RT-PCR suggest that T group, ZS group, and ZG group showed comparable osteoblast-specific gene expression after 24 hours of cell incubation. CONCLUSION: Surface topography and material of implants can play an important role in expression of osteoblast phenotype markers. Zirconia ceramic showed comparable biological responses of osteoblast-like cells with titanium during a short-time cell culture period. Also, grooves influence cell spreading and guide the cells to be aligned within surface grooves.

• The Journal of Advanced Prosthodontics
• /
• v.12 no.1
• /
• pp.1-8
• /
• 2020

PURPOSE. To investigate the influence of crown material (lithium-disilicate, 3Y-TZP zirconia) and abutment type (rigid implant, resin tooth with artificial periodontium) on wear performance of their antagonist teeth and adjacent teeth. MATERIALS AND METHODS. A mandibular left first molar (#36) with adjacent human teeth (mandibular left second premolar: #35, mandibular left second molar: #37) and antagonistic human teeth (maxillary left second premolar: #25, maxillary left first molar: #26, maxillary left second molar: #27) was prepared simulating a section of the jaw. Samples were made with extracted human molars (Reference), crowned implants (Implant), or crowned resin tooth analogues (Tooth). Crowns (tooth #36; n = 16/material) were milled from lithium-disilicate (Li, IPS e.max CAD) or 3Y-TZP zirconia (Zr, IPS e.max ZirCAD, both Ivoclar Vivadent). Thermal cycling and mechanical loading (TCML) in the chewing simulator were applied simulating 15 years of clinical service. Wear traces were analyzed (frequency [n], depth [㎛]) and evaluated using scanning electron pictures. Wear results were compared by one-way-ANOVA and post-hoc-Bonferroni (α = 0.05). RESULTS. After TCML, no visible wear traces were found on Zr. Li showed more wear traces (n = 30-31) than the reference (n = 21). Antagonistic teeth #26 showed more wear traces in contact to both ceramics (n = 27-29) than to the reference (n = 21). Strong wear traces (> 350 ㎛) on antagonists and their adjacent teeth were found only in crowned groups. Abutment type influenced number and depth of wear facets on the antagonistic and adjacent teeth. CONCLUSION. The clinically relevant model with human antagonistic and adjacent teeth allowed for a limited comparison of the wear situation. The total number of wear traces and strong wear on crowns, antagonistic and adjacent teeth were influenced by crown material.

• The Journal of Advanced Prosthodontics
• /
• v.13 no.5
• /
• pp.269-280
• /
• 2021

PURPOSE. The objective of this study was to evaluate the effect of thickness reduction and fatigue on the failure load of monolithic zirconia crowns. MATERIALS AND METHODS. 140 CAD-CAM fabricated crowns (3Y-TZP, inCorisTZI, Dentsply-Sirona) with different ceramic thicknesses (2.0, 1.5, 1.0, 0.8, 0.5 mm, respectively, named G2, G1.5, G1, G0.8, and G0.5) were investigated. Dies of a mandibular first molar were made of composite resin. The zirconia crowns were luted with a resin composite cement (RelyX Unicem 2 Automix, 3M ESPE). Half of the specimens (n = 14 per group) were mouth-motion-fatigued (1.2 million cycles, 1.6 Hz, 200 N/ 5 - 55℃, groups named G2-F, G1.5-F, G1-F, G0.8-F, and G0.5-F). Single-load to failure was performed using a universal testing-machine. Fracture modes were analyzed. Data were statistically analyzed using a Weibull 2-parameter distribution (90% CI) to determine the characteristic strength and Weibull modulus differences among the groups. RESULTS. Three crowns (21%) of G0.8 and five crowns (36%) of G0.5 showed cracks after fatigue. Characteristic strength was the highest for G2, followed by G1.5. Intermediate values were observed for G1 and G1-F, followed by significantly lower values for G0.8, G0.8-F, and G0.5, and the lowest for G0.5-F. Weibull modulus was the lowest for G0.8, intermediate for G0.8-F and G0.5, and significantly higher for the remaining groups. Fatigue only affected G0.5-F. CONCLUSION. Reduced crown thickness lead to reduced characteristic strength, even under failure loads that exceed physiological chewing forces. Fatigue significantly reduced the failure load of 0.5 mm monolithic 3Y-TZP crowns.