• Journal of the Korea Furniture Society
• /
• v.18 no.1
• /
• pp.20-30
• /
• 2007

This experiment was carried out to investigate the effects of number and location of finger joints on the bending strength of glue-laminated lumbers. Urea resin adhesives were used in this experiment and the resin content was 70% for cold pressing. The lamina were edge-jointed and end-jointed. The specimen were composed of one or three layers. The obtained results are summarized as follows; The effects of finger joints on the decrease of bending strength of glue laminated woods were different according to the number and location of finger joints. The decrease of MOR was highest on the middle position of laminated woods. The effects of several arrangements of finger joints on the bending strength of glue laminated woods showed on Figure 7 and 8. The variance of thickness-laminating on the bending strength of glue laminated woods were larger than those of width-laminating.

• Journal of the Korean Wood Science and Technology
• /
• v.1 no.2
• /
• pp.3-10
• /
• 1973

This study was carried out to examine the characeristics of waste sanders(S)from. plywood and pre-finishing plywood surface sanding and double saw finishing, as a new extander in urea-formaldehyde resin(UFR) in plywood adhesive, and to focus, adhesive strength using the glue extended with milled sanders(MS) as extender, leveling the optimum amount of MS to be added, and examining the physical properties of glue extended MS & S. Also economical good feasibility of substitution for wheat flour(WF) with MS as a new extender is analyzed and presented in details. Selecting three standard samples of 80, 100 and 180 mesh, sorking them in distilled water at $20^{\circ}C$, 24 hours, redrying at $105^{\circ}C$ and rescreening the sample with standard screen, again, the 3 samples of 80, 100, and 180 mesh are passed 23 percent through 80 mesh sander standard sample 27 percent through on 100 mesh and only 10.9 percent through 180 mesh, respectively. The particle size of retained parts are greater in size of redried form. It seems undoubtly that particles to be extended in glue are got swollen and become greater in size and coarser in shape. The shape of fresh S particles are irregular thin needle with small scale, as shown in Figure 5. PFS are so finer than plywood S that only 9.8 percent of the S retained on 100 mest screen, 24. 30 percent on 100-160 mesh, and 65.9% on 160-180 mesh. But particle size of the fresh S is large enough to make the viscosity of glue direct extended with S too high to apply it glue spreader. The glue extended with milled sanders(MS). 3 hours milled PFS or 6 hours milled plywood S, having particle sizes shown in Tables 7 and 8, as ratio of Reain/MS/WF/water: 100/8/8/10, indicate good viscosity of 16 to 24 ps, as shown in Figure 5, for applying direct to glue spreader, have high tensile-shear strength (adhesive strength), 102.4 kp/$cm^2$, and 94 percent wood failure.

• Journal of the Korean Wood Science and Technology
• /
• v.32 no.5
• /
• pp.59-65
• /
• 2004

The present study aims to optimise the process parameters of fish glue and adhesion property through room temperature in terms of curing time and opened assembly time for attaining best adhesion strength to wood (Yellow birch, B. alleghaniensis). The uncured and cured fish glue have been characterised by TGA, DSC, FT-JR. It is observed that with increasing curing time up to 48 H, tensile lap shear strength of adhesive joint of fish glue to wood increases and decreases after 48 H. At 15 min. opened assembly time, lap shear strength increases up to 4833 kgf/cm² and decreases after 15 min.

• Journal of Conservation Science
• /
• v.37 no.6
• /
• pp.801-806
• /
• 2021

In order to improve the usability of glue, a traditional adhesive material, and the gelation process of seaweed extract carrageenan, a liquid adhesive for wood preservation was prepared by mixing the two materials. The prepared wood adhesive was mixed with a 15 wt% aqueous solution of glue, λ-carrageenan, an antibacterial agent, an antifoaming agent, and the maximum adhesive strength of 1.80 Mpa was confirmed. As a result of comparison, the adhesive strength was superior to that of 5 different types of traditional natural adhesive ingredients (aqueous solution) and 1 type of polyvinyl acetate-based adhesive.

• Journal of the Korean Wood Science and Technology
• /
• v.23 no.3
• /
• pp.33-39
• /
• 1995

To accelerate the cure of phenolic resin adhesives for plywood, the complexation with melamine resin and the addition of cure-accelerating agents were discussed. The hot-pressing temperature and time of phenol resin could be decreased by complexation with melamine resin. but the wet glue-joints strength of phenol melamine resin was lower than that of ordinary phenol resin in case of plywood using spruce veneer at core layer. Among the tested cure-accelerating agents. the sodium carbonate showed the greatest effect on shortening gelation time of phenolic resin. In addition, in the manufacturing scale test, the hot-pressing time of phenol resin with the addition of 5 parts sodium carbonate could be shortened about 20% compared with ordinary phenol resin which had same glue-joints properties.

• Journal of the Korean Wood Science and Technology
• /
• v.3 no.1
• /
• pp.16-19
• /
• 1975

• Journal of the Korean Wood Science and Technology
• /
• v.15 no.4
• /
• pp.64-68
• /
• 1987

To develope the utilities of the chestnut bur, which is wasted after harvesting chestnut in farmhouses, the feasibilities of adhesion(urea resin) extenders of the powder for plywood were examined. These experiments were implemented on experimental scale at Forestry Research Institute(Seoul) and on a plywood mill scale at Eugon Industrial Co LTD(Inchon) for more reliable data. In this paper, it was proved that the chestnut bur powder caused to rise the glue viscosity but the chaff powder to down reversely. The most effective mixing ratio were wheat flour 5kg, chaff powder: 5kg and chestnut bur powder. 5kg per 100kg of urea resin. At this condition, the viscosity were most appropriate (1,320 2,230 cps) for glue spreading operations, and the dry shear strengthes were most adequate(10.7-13.2kg/$cm^2$), wood failure ratio 82-88%). The chestnut bur powder, can be utilized for plywood adhesion extenders without any change of present process lines in plywwod mills.

• Composites Research
• /
• v.30 no.4
• /
• pp.235-240
• /
• 2017

Animal glue, a water-soluble adhesive, has been used historically for high-performance traditional furniture despite the disadvantage of weakness against moisture. Many scientists studied the ways to improve water resistance of animal glue. Improvements on the interfacial, thermal, and water resistance properties of wood sandwich composites (WSC) was studied with carbon nanotube (CNT) wt% in animal glue. Real-time temperature of WSC was measured after WSC was heated with increasing CNT wt%. Lap shear test was performed to determine the interfacial properties of wood and animal glue with CNTs. Water resistance properties of animal glue were determined by lap shear test using specimens dipped in water and the results were compared with the dry case. Hydrophobicity of animal glue by static contact angle was correlated with the variation of lap shear test. Interfacial, thermal, and water resistance properties for animal glue were improved with properly added CNTs.

• Journal of the Korean Wood Science and Technology
• /
• v.47 no.2
• /
• pp.239-248
• /
• 2019

This research presents an improvement of the physical and mechanical properties of composite board (com-ply) made of Oriented Strand Board (OSB) coated with wood veneer of Pine (Pinus merkusii), Avocado (Persea Americana) and Mahogany (Swietenia mahogany). 1.5 mm thick veneers of those three wood types were adhered to the surface of OSB using two adhesive types: epoxy and isocyanate. The adhesive with the glue spread of $250g\;m^{-2}$ applied using single glue line was spread and then cold pressed with the pressure of $15kg\;cm^{-2}$ for 3 hours. The research result showed an improving dimension stability of com-ply, but not found on all parameters of physical property test. The moisture content seemed to be influenced by the com-ply type, yet not related to its thickness swelling, water absorption and linear expansion. The exception took place in the parallel linear expansion when immersed for 2 hours. The highest to the lowest increases of MOE and MOR were consecutively found on OSB coated with wood veneer of Pine, Mahogany and Avocado. However, the increases were statistically insignificant. The highest increasing screw hold power was found at the com-ply type AE (avocado veneer and epoxy adhesive) that was by 28%.

• Journal of Applied Biological Chemistry
• /
• v.42 no.2
• /
• pp.81-84
• /
• 1999

Blood glue was prepared to reutilize porcine blood. Plasma proteins after lyophilization were treated by addition of wood flour, sodium hydroxide, sodium silicate, and hydrated lime to make blood glue with a suitable adhesivity. Characteristics of the prepared blood glue was monitored by measuring the viscosity with time, and the relationship between degree of hydrolysis of plasma proteins by addition of various amounts of sodium hydroxide and adhesivity was studied. To prevent the emission of formaldehyde during manufacturing of plywood by blood glue, the cross-linking reaction of plasma protein with formaldehyde was also examined. Fourier transform infrared, circular dichroism, and fluorescence spectroscopy study showed that blood plasma proteins react with formaldehyde, resulting in removal of formaldehyde by cross-linking reaction.