• Journal of the Korea Academia-Industrial cooperation Society
• /
• v.11 no.9
• /
• pp.3155-3160
• /
• 2010

Nowadays, most car manufactures have tried to improve fuel efficiency and corrosion resistance of car body. Therefore, use of high strength steels and coated steel becomes more and more increased. In this study, spot weld characteristics according to lap sequence of sheets were analyzed using simulation method for three different steel sheet of car body which were EDDQ class coated steel with 0.7t, high strength steel 440R with 1.2t and advanced high strength steel DP 590 with 1.0t. Using simulation, weldability was evaluated by nugget size of welded zone according to nugget growth curve and welding current with respect to lap sequence of sheets. Contact resistance of each sheets contact point was used to analyze formation of nugget and optimal lap sequence was suggested.

• Journal of Welding and Joining
• /
• v.33 no.2
• /
• pp.56-61
• /
• 2015

IRW(Inverter Resistance Welding) process and DSW(Delta-spot welding) process for dissimilar materials of DP590 and Al5052 were performed to evaluate the welding quality and mechanical properties. IRW experiment was carried out with changing the welding current. The other welding parameters such as pressure force, weld time, squeezing time and holding time were fixed. On the anther hand, DSW experiment was performed using the process tape at welding current of 11.5kA. The other conditions were same as IRW conditions. The various testes such as shear tensile strength, nugget diameters, EDS, SEM and cross-sectional observation for weld zone was performed. As a result, IMC(Inter Metallic Compound) thickness at 11.5kA was thinner than those of 9.5kA and 10.5kA conditions. In addition, thined IMC layer was observed when high electric current apply to the materials(DP590 and Al5052) in a short time throught dissimilar resistance spot welding controling welding conditions. The relationship between the thickeness of IMC and current intensity was after discussed.

• Proceedings of the KWS Conference
• /
• 2006.10a
• /
• pp.268-270
• /
• 2006

• Korean Journal of Materials Research
• /
• v.19 no.7
• /
• pp.369-375
• /
• 2009

The spot weldability of dissimilar metal joints between stainless steels (AISI316) and interstitial free (IF) steels were investigated. This study was aimed to determine the spot welding parameters for a dissimilar metal joint and to evaluate the dissimilar metal joint's weldability, including its welding nugget shape, tensileshear strength, hardness, and microstructure. The fracture surface was investigated by using a Scanning Electron Microscopy (SEM). The experimental results showed that the shape of nugget was asymmetric, in which the fusion zone of the STS316 sheet was larger due to the higher bulk-resistance. The microstructure of the fusion zone was fully martensite. In order to evaluate the microstructure further, dilution of stainless steels were calculated and imposed onto the Schaeffler diagram. The predicted microstructure from the Schaeffler diagram was martensite. In order to confirm the predicted microstructure, XRD measurements were carried out. The results showed that that initial weld nugget was composed of austenite and martensite.

• Journal of Welding and Joining
• /
• v.32 no.6
• /
• pp.1-7
• /
• 2014

For the resistance spot welds of CR1180 and GA1180 TRIP steels, the weld quality evaluation method using the digitalized X-ray transmission imaging apparatus was investigated in comparison with the crosssectional examination method. In the case of the resistance spot welding of CR1180, three circular regions, such as WZ(white zone), GZ(grey zone) and DZ(dark zone), appeared on X-ray image and they corresponded to the diameters of indentation mark, nugget and corona bond, respectively. The variation of X-ray transmission thickness due to the thickness variation of the weld seemed to be mainly responsible for the formation of those contrasts. The X-ray image contrast formed from the variation of transmission thickness at the outer border line of DZ could also enable the inspections of the notch shape, nonuniformity of the welding pressure and spatter from its sharpness, concentricity and the normal straight line, respectively. The X-ray image of the resistance spot weld of galvannealed GA1180 TRIP steel was very similar to that of CR1180 TRIP steel except the crown shaped outer border line of DZ which was considered to be due to the melting behavior of zinc having the boiling temperature even lower than the melting temperature of steel.

• Proceedings of the KWS Conference
• /
• 2001.10a
• /
• pp.184-186
• /
• 2001

Quality estimation of the weld has been one of the important issues in RSW which is a main process of the sheet metal fabrication in auto-body industry. It was well known that among the various welding process variables, dynamic resistance has a close relation with nugget formation. In this study, a new quality estimation algorithm is developed with the primary dynamic resistance measured at welding machine timer. For this, Back propagation algorithm of neural network is used.

• Journal of Convergence for Information Technology
• /
• v.9 no.7
• /
• pp.94-99
• /
• 2019

Friction stir welding was first reported by TWI(The Welding Institute) in 1991, and this welding method has been rapidly used in various industrial areas such railway, automobile, aerospace and shipbuilding industry. Here, we study core characteristics of friction stir welding (FSW) applied to Al 6005-T6 extruded sheets, which is the typical alloy used for railway car bodies. With the fixed welding speed of 500 mm/min, the rotating tool speed was varied from 600 to 1800 RPM. The results of hardness measurement revealed that the hardness of nugget area is ~70% with respect to the parent material, and for the selected range of rotation speed, no clear dependence was observed and the hardness values close to the parent materials were achieved for the area located 5 mm away from the welding interface. The tension test shows that yield strength and tensile strength were slightly decreased with increasing RPM, with no observed difference for the elongation.

• Journal of Welding and Joining
• /
• v.21 no.5
• /
• pp.513-517
• /
• 2003

Resistance welding processes are widely used in automotive applications. In particular, Mash-Seam resistance welding is typically used in Tailored Blank process. If spot welds are changed to a continuous weld, it's easy to reduce noise and to be more stable in cars. A arc welding, laser welding, seam welding using wheel electrode are available to make continuous welds on a car body, but they demand operator with advanced skills and expensive cost to develop. Therefore, flat electrode continuous mash-seam resistance welding process has been used to improve the weak points in currently available system in lap seam welding. This developed process has much more strength and air tightability, and also has much better plastic workability than laser welding. Moreover, commercial RSW machine can be readily used in this welding process.

• Proceedings of the KWS Conference
• /
• 1999.05a
• /
• pp.68-71
• /
• 1999

• Proceedings of the KWS Conference
• /
• 2001.05a
• /
• pp.186-188
• /
• 2001