• Journal of Welding and Joining
• /
• v.30 no.5
• /
• pp.70-75
• /
• 2012

This study is related to the laser weldability of AZ31B magnesium alloy, an all-purpose wrought alloy with good strength and ductility. In general, AZ31B is classified into AZ31B-H24 and AZ31B-O depending on temper designation. Thus, in this study, the laser weldability of AZ31B-H24 and AZ31B-O was investigated and compared. CW Nd:YAG laser was used to produce bead and butt joints. And the effects of welding conditions on the weldability of these joints were examined in detail. As a result of this study, AZ31B-H24 was found to have thinner oxide film and smaller grain size compared with AZ31B-O. Due to such difference, in bead welding, AZ31B-H24 had more wide welding range for full penetration compared with AZ31B-O. Furthermore, it was also confirmed that AZ31B-H24 and AZ31B-O have different welding conditions to obtain stable keyhole in butt welding.

• Proceedings of the KSME Conference
• /
• 2001.06a
• /
• pp.256-261
• /
• 2001

Corrosion and tensile properties of zircaloy-4 cladding tube having a laser welding part in elevated temperature are studied to present the criterion of quality evaluation in nuclear reactor and to found the scientific basis of SCC, with laser welding method using by coupling up cladding tube to end cap. In the result of tensile test($400^{\circ}C$), the fracture is not happened in the welding part but base metal and the result of corrosion test($400^{\circ}C$ 1500psi steam), corrosion rate of the molten zone and PMZ is a little higher than the other zone.

• Journal of Welding and Joining
• /
• v.20 no.6
• /
• pp.72-72
• /
• 2002

Corrosion and tensile properties of zircaloy-4 cladding tube having a laser welding part in elevated temperature are studied to present the criterion of quality evaluation in nuclear reactor and find the scientific basis of SCC, with laser welding method using by coupling up cladding tube to end cap. In the result of tensile test(400℃), the fracture is not happened in the welding part but base metal and the result of corrosion test(400℃ 1500psi steam), corrosion rate of the molten zone and PMZ is a little higher than the other zone.

• Transactions of the Korean Society of Automotive Engineers
• /
• v.22 no.4
• /
• pp.30-35
• /
• 2014

According to weight lightning trend of automobile body, necessity of resistance spot welding (RSW) of Mg alloy on automobile industry is increasing rapidly because of the highest specific strength among commercial metals. Mg alloy has low electric resistance and high thermal conductivity like as Al alloy, so that needs applying high current in short time when welding. Thick oxide film of Mg alloy pollutes the electrodes and makes partial current carrying paths when on welding. Partial current carrying paths signify excessive concentration of current. There can initiate expulsion easily and reduces electrode life rapidly. Generating partial current carrying paths and expulsions are influenced by shapes of electrode. Therefore, electrode life also influenced by shape. In this study, we perform life test of RSW electrode of radius type. Measure tensile shear load and nugget size every spot alternately. As a result, radius type electrode can extend life over twice as dome type electrode.

• Journal of Welding and Joining
• /
• v.18 no.2
• /
• pp.86-94
• /
• 2000

This study was performed to investigate types and formation mechanism of cracks in two Al alloy welds, A5083 and A7N01 spot-welded by pulse Nd : YAG laser, using SEM, EPMA and Micro-XRD. In the weld zone, three types of crack were observed : center line crack({TEX}$C_{C}${/TEX}), diagonal crack({TEX}$C_{D}${/TEX}), and U shape crack({TEX}$C_{U}${/TEX}). Also, HAZ crack({TEX}$C_{H}${/TEX}) was observed in the HAZ region, furthermore, mixing crack({TEX}$C_{M}${/TEX}) consisting of diagonal crack and HAZ crack was observed. White film was formed at th hot crack region in the fractured surface after it was immersed to 10% NaOH water. In the case of A5083 alloy, white films in {TEX}$C_{C}${/TEX} crack and {TEX}$C_{D}${/TEX} crack region were composed of low melting phases, {TEX}$Fe_{2}SiAl_{8}${/TEX} and eutectic phases, $Mg_2$Al$_3$ and $Mg_2$Si. Such films observed $CuAl_2$, {TEX}$Mg_{32}(Al,Zn)_{3}${/TEX}, MgZn$_2$, $Al_2$CuMg and $Mg_2$Si were observed in the whitely etched films near {TEX}$C_{C}${/TEX} crack and {TEX}$C_{D}${/TEX} crack regions. The formation of liquid films was due to the segregation of Mg, Si, Fe in the case of A5083 alloy and Zn, Mg, Cu, Sim in the case of A7N01 alloy, respectively. The {TEX}$C_{C}${/TEX} and {TEX}$C_{D}${/TEX} cracks were regarded as a result of the occurrence of tensile strain during the welding process. The formation of {TEX}$C_{M}${/TEX} crack is likely to be due to the presence of liquid film at the grain boundary near the fusion line in the base metal as well as in the weld fusion zone during solidification. The {TEX}$C_{U}${/TEX} crack is considered a result of the collapsed keyhole through incomplete closure during rapid solidification.

• Proceedings of the Korean Society of Tribologists and Lubrication Engineers Conference
• /
• 1999.06a
• /
• pp.345-353
• /
• 1999

This paper presents friction and wear related results of thermite and gas pressure welded rails under various environmental contact conditions. A welded rail which is manufactured by thermite welding and gas pressure one has been tested rail full range of test conditions in a pin-on-disk wear testing machine. The results show that the friction coefficient and wear rates of a welded rail are heavily dependent on the contact pressures and sliding environments for two welding methods such as thermite and gas pressure weldings.

• Proceedings of the Korean Society of Precision Engineering Conference
• /
• 2005.06a
• /
• pp.430-433
• /
• 2005

Laser bonding between similar and dissimilar thermoplastics has been investigated by making use of laser transmission weld technique. Spot welding of two layers of plastic materials has been demonstrated by using of a high-quality diode-laser with 808nm wavelength. Weld areas increases according to power density, exposure time. The results of peel out test show that peel strengths increase with the area of molten plastics. Layers, which have the same chemical properties, have good bonding qualities. A bonding method which dye film is coated on the interface is used for laser bonding between plastics with high transmission for laser wavelength. Laser transmission bonding is worthy of attention because it is not in contact, requires a few tooling devices, allows a flexible energy delivery and produces nearly invisible welds

• Proceedings of the Korean Society of Tribologists and Lubrication Engineers Conference
• /
• 1998.10a
• /
• pp.59-66
• /
• 1998

This paper presents friction and wear related results of thermite and gas pressure welded rails under various environmental contact conditions. A welded rail which is fabricated by thermite welding and gas pressure one has been tested over full range of test conditions in a pin-on-disk wear testing machine. The results show that the friction coefficient and wear rates of a welded rail are heavily dependent on the contact pressures and sliding environments for two welding methods such as thermite and gas pressure weldings.

• Journal of the Korean Society of Industry Convergence
• /
• v.25 no.4_2
• /
• pp.687-697
• /
• 2022

An automated system is needed for the effectiveness of non-destructive testing. In order to utilize the radiographic testing data accumulated in the film, the types of welding defects were classified into 9 and the shape of defects were analyzed. Data was preprocessed to use deep learning with high performance in image classification, and a combination of one-stage/two-stage method and convolutional neural networks/Transformer backbone was compared to confirm a model suitable for welding defect detection. The combination of two-stage, which can learn step-by-step, and deep-layered CNN backbone, showed the best performance with mean average precision 0.868.

• Journal of Welding and Joining
• /
• v.12 no.4
• /
• pp.110-116
• /
• 1994

This paper has been researched bondability of electronics devices, such as lead frame and the thick film of Ag/Pd on an alumina substrate by different heat sources. To obtain the bonds with high quality, it is very important to consist of different materials. Therefore, this paper clarifies not only heat mechanism of micro parallel gap resistance bonding method and pulse heat tip bonding method but also investigates selection of heat sources with micro-electronic materials for bonding. Finally, it is realized fluxless bonding process with filler metal such as plating layers.