• Journal of Welding and Joining
• /
• 제18권5호
• /
• pp.77-83
• /
• 2000

This study proposes the analysis and evaluation method of time series ultrasonic signal using the attractor analysis. Features extracted from time series signal analyze quantitatively characteristics of weld defects. For this purpose, analysis objective in this study is fractal dimension and attractor quadrant feature. Trajectory changes in the attractor indicated a substantial difference in fractal characteristics resulting from distance shifts such as parts of head and flange even though the types of defects are identified. These difference in characteristics of weld defects enables the evaluation of unique characteristics of defects in the weld zone. In quantitative fractal feature extraction, feature values of 3.848 in the case of part of head(crack) and 4.102 in the case of part of web(side hole) and 3.711 in the case of part of flange(crack) were proposed on the basis of fractal dimensions. Proposed attractor analysis and DAC in this study can enhance the precision rate of ultrasonic evaluation for defect signals of rail weld zone such as side hole and crack.

• 한국레이저가공학회지
• /
• 제13권3호
• /
• pp.1-6
• /
• 2010

The in-process monitoring of $CO_2$ welding of Zn-coated steel plates has been studied and compared with that of conventional thin plates. Relationships between weld defects and plasma emission signals were evaluated in laser lap joint of thick Zn-coated steel. According to the study, weld defects were found to increase with Zn content. As a result, measured plasma emission signals also decreased. In case of plate with $15{\mu}m$-thick Zn-coated layer, defects caused by evaporation of Zn could, therfore, controled by gap of 0.1mm, resulting in a stable emission signals. However, the amplitude of signals fluctuated very widely. Variation of amplitude sould be limited in 3-8V by FFT smoothing.

• 대한기계학회:학술대회논문집
• /
• 대한기계학회 2003년도 춘계학술대회
• /
• pp.316-321
• /
• 2003

The spatter and porosity could be occurred during $CO_2$ CW laser welding of Primer-coated Steel for Shipbuilding. This study has suggested an alternative idea by examining of weld-defect formation mechanism. The primer-coated plate has caused the spatter, humping bead and porosity and these are main part of the welding defect, attributed to the powerful vaporizing pressure of primer attached on the base metal. The zinc of primer has a boiling point that is the lower temperature than melting point of steel. Zinc va}X)f will build up at the interface between the two sheets and this tends to deteriorate the quality of the weld by ejecting weld material from lap position or leaving porosity. Therefore introducing a small gap clearance in the lap position, the zinc vapor could escape through it and sound weld beads can be acquired. In conclusion, we suggested the occurred and prevented mechanism of weld defects with searching the factor.

• Journal of Welding and Joining
• /
• 제2권1호
• /
• pp.49-57
• /
• 1984

The influence of weld defect, residual stress and microstructure on the Low Cycle Fatigue(L. C. F.) behaviour of AISI 304L austenitic stainless steel weldment has been studied. The specimens were welded by shielded metal are welding process, post weld heat treated(PWHT) at 900.deg.C for 1.5hrs, and tested under total strain controlled condition at room temperature. The results of the experiment showed that weld defect affected the L.C.F. behaviour of weldment deleteriously compared to the residual stress or microstructure, and it reduced the L.C.F. life about 70-80%. The PWHT exhibited beneficial effect on the L.C.F. behaviour and increased the L.C.F. life about 120%. This enhancement by PWHT was attributed to the removal of residual stress and recovery of weld metal ductility. The cyclic stress flow of as welded specimens showed intermediate cyclic softening, whereas those of heat treated specimens showed continuous cyclic hardening, and this difference was explained in terms of the residual stress removal and dislocation behaviour. Scanning electron microscopy studies of fatigue fracture surface showed that weld defects of large size and near weld surface were detrimental to the L.C.F. behaviour of weldment.

• 한국컴퓨터정보학회논문지
• /
• 제20권1호
• /
• pp.11-20
• /
• 2015

기존 벨로우즈의 용접 불량은 현미경을 이용한 작업자의 수작업과 육안확인으로 진행되고 있어 효율과 능률면에서 많은 부작용이 있다. 본 논문에서 이러한 문제점을 해결하고자 서포트 벡터 머신을 이용한다. 제안된 시스템은 서포트 벡터 머신을 이용하여 작업자의 경험적인 방법을 대체하고, 이미지 처리 과정에서 작업자로부터 발생하는 불규칙성을 극복할 수 있다. 또한 현미경과 3D 디스플레이 시스템을 통하여 제품불량을 쉽게 확인할 수 있다. 자동화 측정 장치로부터 얻어진 실험결과를 통하여 용접불량은 허용되는 에러 범위 아래로 개선됐음을 알 수 있다.

• 대한기계학회:학술대회논문집
• /
• 대한기계학회 2008년도 추계학술대회A
• /
• pp.317-321
• /
• 2008

Piping in the Nuclear Power plants (NPP) are mostly consisted of carbon steel pipe. The wall thinning defect is mainly occurred by the affect of the flow accelerated corrosion (FAC) of fluid which flows in carbon steel pipes. This type of defect becomes the cause of damage or destruction of piping. Therefore, it is very important to measure defect which is existed not only on the welding partbut also on the whole field of pipe. Over the years, Infrared thermography (IRT) has been used as a non destructive testing methods of the various kinds of materials. This technique has many merits and applied to the industrial field but has limitation to the materials. Therefore, this method was combined with lock-in technique. So IRT detection resolution has been progressively improved using lock-in technique. In this paper, the quantitative analysis results of the location and the size of wall thinning defect that is artificially processed inside the carbon steel pipe by using IRT are obtained.

• 한국안전학회지
• /
• 제33권5호
• /
• pp.9-14
• /
• 2018

The piping system of a nuclear power plant plays a role of transferring high energy fluid to equipment and various devices. The safety and soundness of these piping systems are very closely related to the operability of the power plant. In the case of a welded part of a small diameter pipe, it may grow as a microcrack due to a lack of penetration, and it may grow to a size that affects the safety of the pipe due to the influence of mechanical vibration and fatigue load. Resonance refers to an increase in energy as the natural frequency of an object coincides with the frequency applied to the external force. When this resonance occurs, the frequency is the resonance frequency. In this study, when defects exist in the welds of small diameter pipe, the natural frequency of the pipe changes and resonance may occur. Since these resonances are likely to cause fatigue damage to the piping, resonance frequency changes due to the size and shape of the defects are analyzed and evaluated. As a result of the vibration test, the resonance frequency tended to decrease as the depth of the defect deepened, and the influence was larger when the defect existed at the bottom of the top of the trough. Also, it was confirmed that the Transverse cracks had an effect on the resonance frequency in the presence of the cracks in the weld bead, compared to the longitudinal cracks. As a result of this study, it is expected that the cause of the defect and the condition of the pipe can be monitored because the resonance frequency tendency according to the shape of the crack is analyzed.

• 대한용접접합학회:학술대회논문집
• /
• 대한용접접합학회 1998년도 특별강연 및 추계학술발표 개요집
• /
• pp.303-304
• /
• 1998

• 대한용접접합학회:학술대회논문집
• /
• 대한용접접합학회 1997년도 특별강연 및 추계학술발표 개요집
• /
• pp.5-8
• /
• 1997

• 대한용접접합학회:학술대회논문집
• /
• 대한용접접합학회 1996년도 특별강연 및 춘계학술발표 개요집
• /
• pp.190-192
• /
• 1996