• Journal of Welding and Joining
• /
• 제33권5호
• /
• pp.31-34
• /
• 2015

Microstructure and tensile property in the weld heat-affected zone (HAZ) of austenitic Fe-Mn-Al-C low density steels were investigated through transmission electron microscopy analysis and tensile tests. The HAZ samples were prepared using Gleeble simulation with high heat input welding condition of 300 kJ/cm, and the HAZ peak temperature of $1200^{\circ}C$ was determined from differential scanning calorimetry (DSC) test. The strain- stress responses of base steels showed that the addition of V improved the tensile and yield strength by grain refinement and precipitation strengthening. Tensile strength and elongation decreased in the weld HAZ as compared to the base steel, due to grain growth, while V-added steel had a higher HAZ strength as compared than V-free steel.

• 한국생산제조학회지
• /
• 제9권4호
• /
• pp.131-136
• /
• 2000

This study deals with the mechanical properties of STS304-Al351 friction welding zone. Main results are as follows ; under the condition of upset pressure 75MPa, the tensile strength of STS304-al6351 friction weld interface was higher than that of Al6351 base metal, and the highest tensile strength(290MPa) was obtained at upset pressure 125MPa. The hardness profile across the weld interface shows that the hardness of both STS304 and Al6351 is higher around the weld interface, and sharply increased hardness on the STS304 side is related with the plastic deformation of micro volume. As the result of analyzing the tensile fracture, it showed perfect soft fracture.

• 비파괴검사학회지
• /
• 제29권1호
• /
• pp.43-48
• /
• 2009

The fatigue crack growth behavior of high strength X80 pipeline steel was investigated with compact tension specimens that crack growth directions were aligned either parallel or normal to the rolling direction of the pipeline. Also, the fatigue crack growth rates for welded joint of X80 pipeline steel were investigated with compact tension specimens that crack growth directions were aligned either parallel or normal to the welding line. The experimental results indicated the fatigue crack growth behavior was markedly different in three zones, weld metal, heat affected zone and base metal of welded joints. There was a trend toward increment in the fatigue life of weld metal and heat affected zone as compared with the X80 pipeline steel.

• 대한기계학회논문집A
• /
• 제30권2호
• /
• pp.187-193
• /
• 2006

The butt and the lap welding by friction stir welding performs with $2mm^t$ 1050 aluminum alloy sheet. This paper shows behaviors of property such as vickers hardness, yielding and ultimate stresses, and macro structures for weld zone cross section of the butt and the lap jointed specimens. It is also carried out making comparison with maximum loads, stress-strain diagrams, and deformation after the guided bending test and fracture behaviors between the butt and the lap jointed specimens. It is found that the weldability of the butt jointed specimen is better than that of the lap jointed specimen.

• 열처리공학회지
• /
• 제12권4호
• /
• pp.303-312
• /
• 1999

An investigation of the CrMoV rotor steel weldment which experienced by cyclic thermal aging heat treatment and as-received condition was performed. This evaluation was carried out to confirm whether this type of weldment is appropriate for the service environment in terms of microstructural examinations, microhardness measurements and tensile tests. The cyclic thermal aging heat treatment, containing continuous heating and cooling thermal cycle was programmed to simulate the real rotor service condition. The heat treatment was performed for 40 cycles(5920hrs). The results indicated that the weldment was composed of 4 different regions such as heat affected zone of the base metal, butter weld(initial weld), full thickness weld(final weld) and the base metal. The double welding process was applied to eliminate the susceptibility of reheat cracking at heat affected zone of base metal. The grain refinement at the HAZ due to the welding process could reduce the possibility of cracking susceptibility, but its tensile properties was appeared to be low due to the weld metal in as-received condition. The benefit effect, grain refinement was extended with carbides coarsening during the cyclic thermal aging heat treatment. However the poor mechanical properties of the weldment was more degraded as undergoing the heat treatment.

• Journal of Welding and Joining
• /
• 제26권3호
• /
• pp.45-50
• /
• 2008

SM45C steel rods being used generally for power transmission shafts and machine components was selected and welded by Butt-GMAW(Gas Metal Arc Welding) method. An estimation of fatigue life was studied by constructing S-N curve. Fatigue strength of base metal zone showed higher values than one of weld zone in low cycles between $10^4$ and $10^6$cycles. However, significant decrease in fatigue strength of base metal was found around $10^6$cycles, which were almost same as one of heat affected zone. This decrease was attributed that initial residual stress of the steel rods distributed by drawing process was diminished by continually applied load, and resulted in softening of base metal. The fatigue limit of the weld zone was highest in the boundary between deposited metal zone and heat affected zone, and followed by in the order of deposited metal zone, base metal zone, and heat affected zone. Based on these results, it is revealed that the stress for safety design of machine components using SM45C butt-welded steel rods must be selected within the region of the lowest fatigue limit of heat affected zone.

• 한국주조공학회지
• /
• 제14권6호
• /
• pp.541-547
• /
• 1994

The effects of weld repair on the durability in Al-10%Si-0.3%Mg castings were evaluated. The strength and fracture toughness in fusion zone were higher than those in the base metal by rapid cooling of fusion zone after welding. There were no significant differences between fatigue properties in castings and weld repaired specimen as the results of low cycle fatigue and rotating bending fatigue test. Therefore it was concluded that weld repairing did not have any significant effect on the mechanical properties of castings.

• 한국해양공학회지
• /
• 제9권1호
• /
• pp.151-160
• /
• 1995

The characteristics of low temperature impact toughness and stress corrosion resistance at boiling MgCl$_2$ solution of GTA and SMA weld of duplex stainless steels have been investigated. The impact toughness was highest at the GTAW weld metal and lowest at the SMAW weld, which was almost the same as that of the SMAW heat-affected zone. This was attributable to influence of austenite-ferrite phase balance, and the degree and nature of precipitation that occurred during welding. The SCC resistance of the weldments was slightly higher than that of the base metal, whereas no difference in the SCC resistance was found between two different weldments.

• International Journal of Precision Engineering and Manufacturing
• /
• 제7권3호
• /
• pp.30-34
• /
• 2006

We investigated fatigue crack growth behavior in laser-welded sheet metal caused by a single applied overload The fatigue specimens were made using butt jointed cold rolled sheet metal that was welded with a $CO_2$ laser, The effects of the specimen thickness and overload ratio were determined from fatigue crack propagation tests, These tests were performed in such a way that the fatigue loading was aligned parallel to the weld line while the crack propagated perpendicular to the weld line, Overload ratios of 1.0, 1.5, and 2. 0 were applied near the tip of the fatigue crack at points located 6, 4, and 2 mm from the weld line. The specimens were either 0.9 or 2.0 mm thick. The size of the plastic zone at the crack tip due to the single applied overload was also determined using finite element analysis.

• 동력기계공학회지
• /
• 제14권3호
• /
• pp.58-63
• /
• 2010

A laser beam welding and an electric arc welding were combined, and the positive points of each welding method are drawn such as high speed, low thermal load, deep penetration, and high productivity. The fiber laser-MIG conjugated welding. namely the hybrid welding has been studied mainly for the automation industry of a pipeline welding. In this study, the MIG welding was combined with a fiber laser welding to make up the hybrid welding. The weld shapes, microstructures and mechanical properties for weld zones after the hybrid welding or only fiber laser welding were investigated on the 700 MPa grade Ultra Fine Grained(UFG) high strength steel. The amount of acicular ferrite in weld metals and HAZ(heat affected zone) was observed larger after hybrid welding compared with after only laser welding. The Vickers hardness of the top area of the fusion zone after fiber laser welding was higher compared with after hybrid welding.