• Steel and Composite Structures
• /
• v.25 no.5
• /
• pp.535-544
• /
• 2017

Box sections are symmetrical sections and they have high moment of inertia in both directions, therefore they are good members in tall building structures. For the rigid connection in structures with box column continuity plates are used on level of beam flanges in column. Assembly of the continuity plates is a difficult and unreliable work due to lack of weld or high welding and cutting in the fourth side of column in panel zone, so the use of experimental stiffeners have been considered by researchers. This paper presented an experimental investigation on connection in box columns. The proposed connection has been investigated in four cases which contain connection without internal and external stiffeners(C-0-00), connection with continuity plates(C-I-CP), connection with external vase shape stiffener (C-E-VP) and connection with surrounding plates(C-E-SP). The results show that the connections with vase plates and surrounding plates can respectively increase the ultimate strength of the connection up to 366% and 518% than the connection without stiffeners, in case connection with the continuity plates this parameter increases about 39%. In addition, the proposed C-E-VP and C-E-SP connection provide a rigid and safe connection to acquire rigidity of 95% and 98% respectively. But C-I-CP connection is classified as semi-rigid connections.

• Journal of Advanced Marine Engineering and Technology
• /
• v.37 no.8
• /
• pp.869-876
• /
• 2013

In order to estimate the fatigue life of mufflers at the early stage of researches and designs, the new prediction process was developed by the artificial neural network, which has the algorism of weldment properties. Bending fatigue test was carried out for defining the characteristics of muffler weldment fatigue life and damage. For considering and predicting mechanical and fatigue properties of the muffler, the maximum stress of weldment was adapted as the variable of artificial neural network training. Also, it was compared with the fatigue life predicting results using fatigue notch factors, for proving the newly developed process of the artificial neural network.

• Transactions of the Korean Society of Machine Tool Engineers
• /
• v.15 no.3
• /
• pp.120-126
• /
• 2006

In this paper, we investigated the characteristics of fatigue fracture on TB(Tailored Blank) weldment by comparing the fatigue crack propagation characteristics of base metal with those of TB welded sheet used for vehicle body panels. We also investigated the influence of center crack on the fatigue characteristic of laser weld sheet of same thickness. We conducted an experiment on fatigue crack propagation on the base metal specimen of 1.2mm thickness of cold-rolled metal sheet(SPCSD) and 2.0mm thickness of hot-rolled metal sheet(SAPH440) and 1.2+2.0mm TB specimen. We also made an experiment on fatigue crack propagation on 2.0+2.0mm and 1.2+1.2mm thickness TB specimen which had center crack. The characteristics of fatigue crack growth on the base metal were different from those on 1.2+2.0mm thickness TB specimen. The fatigue crack growth rate of the TB welded specimens is slower in low stress intensity factor range$({\Delta}K)$ region and faster in high ${\Delta}K$ region than that of the base metal specimens.

• Journal of Welding and Joining
• /
• v.28 no.2
• /
• pp.79-83
• /
• 2010

In this study, newly developed welding consumables for EGW were welded in EH 36 TM steel plates and their welded joints were evaluated in point of mechanical properties and microstructures compared with imported consumables. Newly developed welding consumables were evaluated as good arc stability and slag fluidity, substantially the same with imported products. The tensile strength of all welded joints were sufficient to meet the requirements specified in a ship’s classification(490~640MPa) and all areas of fracture were heat affected zone(HAZ). Charpy absorbed energy values of all EG welded metals were sufficient to meet the requirements of classification(min. 34J) and those of newly developed wires were evaluated to be better than those of imported wires. As a result observing microstructures of single and tandem EG welded metals through optical and scanning electron microscope (OM&SEM), no grain boundary ferrite(PF(G)) were created in a prior austenite grain boundary and a volume fraction of a fine acicular ferrite were observed very high.

• Proceedings of the KWS Conference
• /
• 2009.11a
• /
• pp.61-61
• /
• 2009

This paper has been performed in order to figure out the reason of failure in T23 weldments used for boiler tube at 550 $^{\circ}C$. Defects such as cracks and cavities occurred in CGHAZ (coarse grain heat-affected-zone) and multi pass of weld metal, and these crack propagated along grain boundary. Microstructure evolution such as grain growth and carbide precipitation was investigated by optical microscope (OM), transmission electron microscope(TEM). Moreover, Auger electron spectroscope (AES) was employed in order to examine segregation along the grain boundaries. There is significant difference in grain size and precipitation distribution in the region where cracking took place. In addition, sulfur segregation was observed. Based on the results of this investigation, it has been possible to establish that this type of cracks were consistent with reheat cracking and creep damage. Selection of optimal filler metal, heat input, and PWHT temperature is required for prevention in order to avoid this type of cracking.

• Journal of Power System Engineering
• /
• v.18 no.2
• /
• pp.62-69
• /
• 2014

In this paper, in order to investigate the effects of marco and microscopic observations of fatigue crack growth in friction stir welded (FSWed) 7075-T651 aluminum alloy plates, fatigue crack growth tests were performed under constant amplitude loading condition at room temperature with three different pre-cack locations, namely base metal (BM-CL) and two kinds of pre-crack locations in welded joints, weld metal (WM-CL) and heat affected zone (HAZ-CL) specimens. The fatigue crack growth behavior of FSWed 7075-T651 aluminum alloy plates were discussed based on the marco and microscopic fractographic observations. The marcoscopic aspects of surface crack growth path for BM-CL and HAZ-CL specimens indicate relatively straight lines, however, the crack growth paths of WM-CL specimens grow first straight and by followed toward the TMAZ and HAZ. The microscopic aspects of fatigue fracture for BM-CL and HAZ-CL specimens indicate typical fatigue striation, but WM-CL showed intergranular fracture pattern by micro structural changes of FSW process.

• Journal of Welding and Joining
• /
• v.24 no.1
• /
• pp.77-87
• /
• 2006

Considering ferrite grain size in the base metal, the prediction model for $A_{c3}$ temperature and prior austenite grain size at just above $A_{c3}$ temperature was proposed. In order to predict $A_{c3}$ temperature, the Avrami equation was modified with the variation of ferrite grain size, and its kinetic parameters were measured from non-isothermal data during continuous heating. From calculation using a proposed model, $A_{c3}$ temperatures increased with increasing ferrite grain size and heating rate. Meanwhile, by converting the phase transformation kinetic model that predicts the ferrite grain size from austenite grain size during cooling, a prediction model for prior austenite grain size at just above the $A_{c3}$ temperature during heating was developed.

• Proceedings of the KWS Conference
• /
• 2005.06a
• /
• pp.370-376
• /
• 2005

Magnesium alloys are becoming important material for light weight car body, due to their low specific density but high specific strength. However they have a poor weldability, caused high oxidization tendency and low vapor temperature. In this study, the welding performance of magnesium alloys was investigated for automobile application. The materials were rolled magnesium alloy sheet contains Al and Zn such as AZ3l , AZ6l and AZ9l. Three types of welding process were studied, that were GTAW, Laser beam welding and FSW. To evaluate the weldability, we examined the appearance of welding bead. Also we checked bead shape and internal defects such as crack and porosity on cross section of welding bead. The mechanical property was measured for welded specimen by tensile test. For determination of the strength change by welding process, the hardness profile across the welding center was measured. For the results, the tensile properties of welded specimen were decreased obviously on all welding process. For the fusion welding process such as GTAW and laser beam welding, the surface of the welding bead was covered with oxidized magnesium dust but it was removed by simple cleaning work as wipe-out with tissue. Also under cut, that caused vaporization of base metal was occurred. for the friction stir welding, there was no oxidation, under-cut or internal defects. However it had poor weld performance, the reason was cleavage fracture occurred at plastic deformation zone. For welding of magnesium alloy, the laser beam welding process was recommended.

• Journal of Welding and Joining
• /
• v.34 no.6
• /
• pp.35-41
• /
• 2016

The experimental study has been performed through residual stress using the Ti6Al4V, investigate the effect of laser shock peening on laser welding process residual stress of Ti6Al4V welds in a reduce safety weld zone. This research evaluated the effects of shock waves from laser shock peening with a pulsed Nd:YAG laser on Ti6Al4V welding specimens, through the analysis of the residual stress of the specimens. The residual stress could be formed by the depth of 1 mm if the proposed method of reducing the residual stress is performed in the optimal condition. The welded structures and products during the production process increase the mechanical property of repeated stress, which could be expected to extend the fatigue life of the structure.

• Journal of Ocean Engineering and Technology
• /
• v.14 no.4
• /
• pp.56-61
• /
• 2000

This study has been performed for mechanical properties of underwater wet welding electrode with rolled steel (KR-RA) for ship structure, one kind (E 4313) of domestic covered arc welding electrode used in the air and two kinds (UWE-01, UWE-02) of underwater covered arc welding electrode experimentally developed on the same welding condition. The results obtained were as follows : The hardness value of underwater covered arc welding electrode (UWE-01) was about 8.3% lower than domestic covered arc welding electrode(E 4313) in heat affected zone of test of UWF-02 was lower about 4.5%. Tensile strengths of UWE-01 were about 0.9%, and those of UWE-02 were about 6.5% higher than those of domestic covered arc welding electrodes (E 4313) in test specimens. The impect value of UWE-01 were about 15.5%, and those of UWE-02 were about 21.7% highter than those of domestic covered arc welding electrodes(E 4313) in test specimens. So mechanical properties of the underwater arc welding electrode were improved by the composition ratios of covering materials.