• Journal of Welding and Joining
• /
• 제25권4호
• /
• pp.65-71
• /
• 2007

Laser weldability of the aluminized steel for the full penetration welding will be described in this paper. We focused on the effect of Al coating conditions on weld strength. For these objectives, aluminized steel sheets that have various thickness and coating weight were prepared for laser welding. And then, tensile-shear and hardness test were carried out. At the same time, Al contents in weld after laser welding were analyzed and their correlations with mechanical properties were investigated. Besides, as removing partially coating layer, weldability has been investigated according to the position of coating layer. As a result of this study, tensile-shear strength was decreased with increasing Al contents in weld, and Al of coating layer caused grain growth.

• 대한기계학회:학술대회논문집
• /
• 대한기계학회 2007년도 춘계학술대회A
• /
• pp.1317-1321
• /
• 2007

Aluminized steel sheet that Al coated on low carbon steel has a excellent heat resistance, thermal reflection and corrosion resistance. It has applied to fuel tank, automotive exhaust systems, etc. Laser weldability of the aluminized steel for the full penetration welding will be described in this paper. We focused on the effect of Al coating conditions on weld strength. For these objectives, aluminized steel sheets that has various thickness and coating weight were prepared for laser welding. And then, tensile-shear and hardness test were carried out. At that same time, Al content mixed in weld after laser welding was evaluated and investigated a correlation between the mixed Al and mechanical properties. Besides, as removing partially coating layer, weldability has been investigated according to position of coating layer. As a result of this study, as increasing Al content in weld, tensile-shear strength was decreased. Also it was identified that Al of coating layer caused grain growth.

• Journal of Advanced Marine Engineering and Technology
• /
• 제30권5호
• /
• pp.636-644
• /
• 2006

Recently, there were some successful examples that the laser welding was introduced into production line. However, the spread of laser welding is not sufficient in many industries. There are several reasons why it is difficult to penetrate the laser welding into production lines. Because it is different from reflection, absorption and permeation of laser beam according to material and surface condition. Moreover, there are significant problems in processing such as absorption and scattering of beam by the induced plasma or plume. Therefore, understanding of mechanism on formation of weld defect in laser welding of the laminated core for motor is very important. In this paper, it was analyzed in terms of materials which was source of defect in laser welding and conventional arc welding. As a results of analysis, insulation coating film of the laminated core was judged to main factor of weld defect. it could be well aware as tracing carbon volume, and it was deduced that weld defect by insulation coating film was caused by difference of mechanism between the two heat sources.

• Journal of Welding and Joining
• /
• 제34권4호
• /
• pp.55-61
• /
• 2016

During laser overlap welding of galvanized steel sheets, explosion of weld pool by the high pressure zinc vapor induces weld defects like porosity and blowhole. In this study, laser 2-pass welding was implemented to prevent the weld defects. Through the 1st pass welding, zinc layers on the faying surfaces were removed when proper heat input was applied. Excessive heat input could result in explosion even during the 1st pass welding and insufficient heat input could not remove enough region of zinc layer for the 2nd pass welding. Coating weights of $45g/m^2$ and $60g/m^2$ were considered and for both cases sound welds without weld defects could be achieved. In spite of 2-pass welding, softening of weld and heat affected zone was not observed and Zn coating was not diluted into the weld metal.

• 한국레이저가공학회지
• /
• 제13권3호
• /
• pp.19-26
• /
• 2010

In this study, fundamental experiment was conducted with various strength of UHSS (Ultra High Strength Steel) by $CO_2$ laser. And then, butt and lap joint laser welding with boron alloyed steel and Al-Si coated boron alloy steel have been done by changing laser beam feature, existence of gap and existence of coating layer to know welding characteristics of those materials. As a result, in case of fundamental experiment with various strength steel, hardening was found in the weld metal of all tested materials and softening was found at the heat affected zone of SGAFC 1180. In case of laser butt welding of UHSS, mechanical properties was improved by using small laser beam diameter and Al-Si coating layer caused fracture of weld metal. In case of laser lap welding of UHSS, Al-Si coating layer resulted in formation of intermetallic compound at the fusion boundary where fracture occurred. Al-Si coating layer caused lowering mechanical properties of weld metal.

• 대한용접접합학회:학술대회논문집
• /
• 대한용접접합학회 2003년도 춘계학술발표대회 개요집
• /
• pp.102-104
• /
• 2003

Laser weldability of aluminized steels of 0.8mm thick has been investigated. Test materials were cut from the commercial steels that were produced at the Coating Mill of POCOS. Test coupons for welding were prepared by using a conventional shearing machine and no additional edge treatment was peformed. Nd:YAG laser welding system was mainly applied to make weld specimens. Test results revealed that almost no spattering was observed even though the welding was peformed with no overlap joint clearance. Bead quality of aluminized steel laser weld was smooth and stable. According to x-ray inspection results, it was proved that the laser welds of aluminized steels were metallurgically defect free.

• Corrosion Science and Technology
• /
• 제11권1호
• /
• pp.29-36
• /
• 2012

The resistance spot welding of high strength steel degrades the weldability because of its high strength with rich chemical composition and coating layer to protect from corrosion. During the each resistance welding process the electrodes tip reacts with coating layer, then subsequently deteriorates and shorten electrode life. In this study, the Al-coated HPF (Hot Press Forming) steels and Zn-coated TRIP steels were used to investigate the electrode life for resistance spot welding. Experimental results show that the reactivity of Al-coating on HPF steels to electrode tip surface behaviors different from the conventional Zn-coated high strength steels. The electrode tip diameter and nugget size in electrode life test of Al-coated HPF steels are observed to be constant with respect to weld numbers. For Al-coated HPF steels, the hard aluminum oxide layer being formed during high temperature heat treatment process reduces reactivity with copper electrode during the resistance welding process. Eventually, the electrode life in resistance spot welding of Al-coated HPF steels has the advantage over the galvanized steel sheets.

• 한국재료학회지
• /
• 제14권1호
• /
• pp.1-8
• /
• 2004

Laser weldability of aluminized steels for deep drawing application has been investigated. Test coupons for Nd:YAG laser welding and $CO_2$ laser welding were prepared trom the commercial steels. According to the test results, total penetration and back bead width of aluminized steels were sensitive to the welding conditions. Bead width at the half thickness of the overlap joint, however, was rather constant. Laser weldability of aluminized steels was superior to that of zinc coated steel. Weld microstructure revealed that overlap zone adjacent to the fusion line was filled with coated materials, which was thought to be desirable to protect weld from crevice corrosion. The aluminum coated materials was also found in the weld metal. Practically no spattering was observed in the laser welding of aluminized steels even when the welding was performed without joint gap. In the welding of zinc coated steel, however, spattering was so severe that it was difficult to get the acceptable weld. Bead quality of aluminized steel laser weld was smooth and stable.

• Journal of Welding and Joining
• /
• 제2권1호
• /
• pp.30-40
• /
• 1984

Moisture content in the coating of an electrode is known to cause defects such as porosities, fish eyes and cracks in the weld metal, however, quantitative relationship between them is not clearly understood. In this study widely consumed and the most common type of arc welding rods such as ilmenite and low hydrogen type were chosen for the investigation, and attempts were made to correlate the relationship between the mechanical properties and gas contents when welding was carried out with electrodes of various moisture contents. As the relative humidity changed from 70% to 92%, it was determined that moisture content to reach saturation was in the range of 0.6~6.8%. As the moisture content in the electrode coating was increased, the amount of gaseous components (H, O, N) in the weld metal was accordingly increased, especially diffusible hydrogen showed prominent effect, i.e. it increased proportionally to the increase of the moisture content. The mechanical properties of the weld metal was observed to become more inferior as the diffusible hydrogen was greater. It was determined for ilmenite type of electrode that the increase of hydrogen content was approximately 1.8ml per unit weight percent increase of moisture and also tensile strength resulted lowering from $45.3kg/\textrm{mm}^2$ to $42.7kg/\textrm{mm}^2$ as moisture content increased from 0.7% to 6.8%. For low hydrogen type the increase of the hyrogen was about 2.4ml per unit percent of moisture and tensile strength decreased from $63.0kg/\textrm{mm}^2$ to $53.8kg/\textrm{mm}^2$ particularly in the region of moisture content 0.1~4.2%.

• Journal of Advanced Marine Engineering and Technology
• /
• 제28권1호
• /
• pp.109-115
• /
• 2004

The spatter and porosity could be occurred during$CO_2$CW laser welding of Primer- coated steel for shipbuilding. This study has suggested an alternative idea by examining of weld-defect formation mechanism. The primer-coated plate induced the spatter humping bead and porosity and these are main part of the welding defect. attributed to the powerful vaporizing pressure of primer attached on the base metal The zinc of Primer has a boiling point that is the lower temperature than melting point of steel zinc vapor will build up at the interface between the two sheets and this tends to deteriorate the quality of the weld by ejecting weld material from lap position or leaving porosity. Therefore introducing a small gap clearance in the lap position. the zinc vapor could escape through it and sound weld beads can be acquired. In conclusion, we suggested the occurred and prevented mechanism of weld defects with searching the factor.