• 대한안전경영과학회지
• /
• 제3권4호
• /
• pp.45-52
• /
• 2001

In order to Investigate water tree degradation behavior on XLPE cable, direct voltage of 200 to 800V has been applied to the material at 5$0^{\circ}C$~10$0^{\circ}C$, and the water tree property has been correlated with voltage and temperature. The leakage current was increase as temperature increased and the Ohm's law was generally satisfied in this experiment though some experimental errors were found. The leakage current was decreased and reached to the stable state with time. It was also shown that the time for the stabilization of leakage current was lessened as voltage increased

• 한국전기전자재료학회:학술대회논문집
• /
• 한국전기전자재료학회 2001년도 추계학술대회 논문집 Vol.14 No.1
• /
• pp.262-265
• /
• 2001

In order to investigate the water tree degradation behavior on XLPE cable, direct voltage of 200 to 800V has been applied to the material at $50^{\circ}C\sim100^{\circ}C$. and the water tree property has been correlated with voltage and temperature in this study. The leakage current was shown to increase as temperature increased and the Ohm's law was generally satisfied in this experiment though some experimental errors were found. The leakage current was shown to decrease and reach to the stable state with time. It was also shown that the time for the stabilization of leakage current was lessened as voltage increased

• 한국전기전자재료학회:학술대회논문집
• /
• 한국전기전자재료학회 2001년도 추계학술대회 논문집
• /
• pp.262-265
• /
• 2001

In order to investigate the water tree degradation behavior on XLPE cable, direct voltage of 200 to 800V has been applied to the material at 50$^{\circ}C$∼100$^{\circ}C$, and the water tree property has been correlated with voltage and temperature in this study. The leakage current was shown to increase as temperature increased and the Ohm's law was generally satisfied in this experiment though some experimental errors were found. The leakage current was shown to decrease and reach to the stable state with time. It was also shown that the time for the stabilization of leakage current was lessened as voltage increased

• 한국산학기술학회논문지
• /
• 제21권5호
• /
• pp.516-522
• /
• 2020

수트리의 진행과정은 십수년이 걸리며 보통 매우 오래된 지중케이블에서 발견된다. 이러한 지중케이블들은 이미 접근이 어려운 곳에 있어 수트리를 검출하기 위해서는 많은 비용과 시간이 소요된다. 이러한 지중케이블의 유지보수 비용과 시간을 절감하기 위해서는 수트리가 진행된 지중케이블이 전력망에 미치는 영향을 분석할 수 있는 수학적 모델링이 필요하고, 이를 이용한 수트리 탐지 기술개발이 매우 필요한 실정이다. 본 논문에서는 수트리가 포함된 XLPE 케이블 대한 수학적 모델링을 하고자 수트리의 복잡한 구조를 Vented tree의 확인된 특정 패턴 2가지를 기준으로 가정하여 단순화 하였다. 그리고 수트리의 발달에 따른 케이블 절연층의 캐패시턴스 및 레지스턴스를 계산 및 분석하기 위해 matlab으로 시뮬레이션을 실시하였으며, 모델링의 유용성을 검증하기 위해서 참고문헌 Burkes 논문의 케이블 데이터를 동일하게 적용하였다. 시뮬레이션 결과, 캐패시턴스 크기의 변화는 케이블에 수트리 영역이 절연층에 95%까지 진행되었을 때 정상대비 약 0.025×10^-13[Farads/mm] 증가됨을 확인하였다. 레지스턴스 값의 경우 정상대비 약 0.5×10¹⁶[ohm/m] 정도 감소되는 것을 확인하였다. 따라서, Burkes 논문의 물리적 모델링 시뮬레이션 결과와 비교하였을 때 그 변화값이 매우 유사하여 본 논문에서 제시한 수학적 모델링의 유용성을 검증하였다.