• Resources Recycling
• /
• v.24 no.2
• /
• pp.55-61
• /
• 2015

In this study, mechanical properties of waste ground rubber tire powder were investigated to evaluate the influence of pre-treatment process for recycling. The tensile test, fracture test and morphology observation were carried out using various kinds of waste ground tire powders, which were produced by grinding and devulcanization process, respectively. As a results, it was found that the produced rubber powder through grinding process increased its tensile strength and elongation with decreasing particle size because of decreasing surface area. Devulcanized rubber powder also increased its tensile strength and elongation by de-crosslink with sulfur. It could be also suggested that devulcanization treatment after grinding process was more efficient recycling process for both increasing tensile property and fracture elongation of waste ground rubber tire powders.

• Resources Recycling
• /
• v.23 no.3
• /
• pp.44-50
• /
• 2014

In this study, a method of shear crushing and a two-stage disk mill were introduced to grind the waste tire powder. Rubber chips with various size were obtained during the crushing or grinding step. The two-stage disk mill was composed of two drum-type blades rotating at various speed and in opposite directions. Therefore, more roughly surfaced particles of micronized waste tire powder were obtained using shear crushing rather than using conventional cutting crushing. In this study, the shape of shear-crushed waste tire particles was compared with conventional cutting crushing particles by scanning electron microscope. In addition, the particle size analyzer was employed to determine the appropriate particle size of waste ground tire powders obtained in this study.

• Elastomers and Composites
• /
• v.31 no.2
• /
• pp.95-103
• /
• 1996

Nowadays, recycling of waste materials is one of great attention among all industries. Especially, the waste tires become a significant problem with increasing in a number of automobiles. For recycling of the waste tires, a polyurethane binder was mixed with the scrapped rubber powders obtained from tread part of the waste tire. This study covered the effect of processing conditions;curing temperature and curing time;on the mechanical properties of the blend. We also compared the experimental results from labors-tory scale with those from scale-up.

• Elastomers and Composites
• /
• v.29 no.5
• /
• pp.431-435
• /
• 1994

For recycling of the waste tires, polyurethane binder mixed with the scrapped rubber powders which obtained from tread part of waste tire. This study covered the effect of the binder contents on the mechanical properties of the blend. We also studied the change of the properties after aging on properties compared with those of before aging. The curing reaction of the binder was also investigated in this study. We obtained conclusions the suitable binder content was 15phr in this system.

• Elastomers and Composites
• /
• v.41 no.2
• /
• pp.97-107
• /
• 2006

The recycled polyethylene composites with various ratio of ground waste tire powder were manufactured by using a fully intermeshing co-rotating twin screw extruder for the reuse of waste tire scrap. In this investigation, the ground waste tire powders (GWTP) were blended with virgin HDPE and recycled polyethylene in the weight ratio of 0 to 50 wt.%. Mechanical properties such as tensile strength, elongation at break and impact strength were measured by using ASTM standard. The experimental results for the various composite showed that the tensile strength of composites decreased with increasing GWTP ratio, while elongation at break increased with the amounts of GWTP. On the other hand, the impact strength for the three kinds of composites showed maximum at the 30 wt.% of GWTP and then decreased. Morphology of the fracture surface tends to be rough with increasing waste tire powder content. Rheological properties were investigated by measuring the shear viscosity against shear rates and softening temperatures. They showed that melt viscosity of rubber composites in this study subsequently increased with increasing GWTP content as a result of increase of flow resistance against external stress and followed a Power-law behavior.

• Resources Recycling
• /
• v.24 no.3
• /
• pp.59-65
• /
• 2015

Recycling of vulcanized rubber products is a serious problem in the world. A quantity of generated waste tires becomes much more and more because of increasing demands on automobiles, resulted in the cause of serious secondary pollution by sulfur component that is crosslinked to incineration or landfill. In addition, crosslinked surfur is used to interfere with the binding of the raw material rubber. In this study, we analyzed the degree of devulcanization by the chemical devulcanization. Devulcanization ratio of the samples were systematically analysed by variables such as time and temperature. In addition, the effect of swelling method as a pre-treatment process was also measured. A rubber specimen was deepened in a organic 2-buthanol solutions during various times of 1 ~ 5 hrs at 100, 150, $200^{\circ}C$ respectively, then to calculate the crosslink density and the number average molecular weight by using a parallel expansion process, which showed devulcanization degree of analyzed samples quantitatively. Also, the mechanical properties were measured with the samples prepared by using a hot press.