• Proceedings of the Korean Society for Technology of Plasticity Conference
• /
• 1999.03b
• /
• pp.88-94
• /
• 1999

This study is to investigate the effects of warm deep drawing with steel sheets of SCP3C and SCP1 for improving deep drawability. Experiments were carried out in various working conditions such as forming temperature and lubricantion. The effect of lubricantion and temperature on drawabillity of steel sheets as well as thickness distribution of drawn oil pan were examined and discussed. One step forming at room temperature and uniform distribution of thickness was achieved at optimum formability for lubricantion. The optimum forming temperature was obtained that both the die and the blankholder were heated to 10$0^{\circ}C$ while the punch was cooled by circulating coolant of $0^{\circ}C$.

• Transactions of Materials Processing
• /
• v.15 no.8 s.89
• /
• pp.597-602
• /
• 2006

Bulk plastic forming characteristics were studied for the magnesium alloy, AZ31 in warm backward extrusion. Effects of process conditions such as extrusion ratio, forming temperature, and punching speed were investigated respectively. Variation of microstructure induced by the warm backward extrusion process was observed. Microstructure of the work piece showed evidences of recrystallization under the experiment conditions. It is estimated that in specific punch speed region fast stroke accelerates recrystllization and reduces the forming load.

• Proceedings of the Korean Society for Technology of Plasticity Conference
• /
• 2003.10b
• /
• pp.152-157
• /
• 2003

A typical die-set for enclosed-die forging of half axle gears in double action hydraulic press is presented, the important factors those influence on precision forming of half axle gears are analyzed, warm forming process of half axle gears is simulated by FEM software $DEFORM\_3D$. The results show, that proper die structure and dimension, suitable web thickness and position can improve material filling, ensure full filling of tooth cavity.

• Transactions of Materials Processing
• /
• v.18 no.2
• /
• pp.112-115
• /
• 2009

Press forming of magnesium alloy sheet is conducted at elevated temperatures to improve the press formability due to its low formability at room temperature. At elevated temperatures, magnesium alloy sheet formability is known to be very sensitive to the strain rate. In this paper, warm deep drawing tests of magnesium alloy AZ31 sheet was conducted under double forming velocity as well as single forming velocity to examine the formability change by forming velocity profile. The observed formability improvement by double forming velocity was analyzed by using the finite element analysis.

• Proceedings of the Korean Society for Technology of Plasticity Conference
• /
• 2002.02a
• /
• pp.136-143
• /
• 2002

Warm draw die technique which is one of the new forming technologies to improve formability of sheet metal is applied to the cylindrical and square cup drawing of stainless-aluminum clad sheets. In experiments the temperature of die and blank holder is varied from room temperature to $180^{\circ}C$, while the punch is cooled by circulation of coolant to increase the fracture strength of workpiece on the punch comer area. Test materials chosen for experiments are STS304-A1050-STS304 clad sheets. Teflon film as a lubricant is used on both sides of a workpiece. The limit drawing ratio and relative drawing depth as well as quality of drawn cups(distribution of thickness)are investigated and validity of warm drawing process is also discussed. No separation between each laminated material after drawing occurred through inspection by microscope as well as application of penetrant remover and bond strength test. Therefore, warm forming technique was confirmed to give better results in deep drawing of stainless clad sheet metal.

• Proceedings of the Korean Society for Technology of Plasticity Conference
• /
• 1998.06b
• /
• pp.8-18
• /
• 1998

The effect of press warm forming in cylindrical deep drawing of stainless-aluminum clad sheet metals are examined . The temperature of die and blank holder is varied from room temperature to 20$0^{\circ}C$, while the punch is kept cooled during test to increase the fracture strength of workpiece on the punch corner area. Test materials chosen for experiments are STS304-Al050-STS304, STS304-A1050-STS430-, STS304 and Al050 metals and teflon film as a lubricant is used on both sides of a workpiece. The limit drawing ration as well as quality of drawn cups (distribution of thickness and hardness)are investigated and discussed.

• Transactions of Materials Processing
• /
• v.8 no.2
• /
• pp.152-159
• /
• 1999

This study is to investigate the effects of warm deep drawing with aluminum sheets of A1050-H16 and A5020-H32 for improving deep drawability. Experiments for producing circular cups and square cups were carried out for various working conditions, such as forming temperature and blank shapes. The limit drawing ratio(LDR) of 2.63 in warm deep drawing of circular cups in case of A5020-H32 sheet, whereas LDR of 2.25 in case of A1050-H16, could be obtained and the former was 1.4 times higher than the value at room temperature. The maximum relative drawing depth for square cups of A5020-H32 material was also about 1.92 times deeper than the depth drawn at room temperature. The effects of blank shape and forming temperature on drawability as well as thickness distribution of drawn cups were examined and discussed.

• Journal of the Korean Society of Manufacturing Process Engineers
• /
• v.7 no.4
• /
• pp.44-49
• /
• 2008

The characteristic of magnesium alloy is the most light in utility metal, the effect of electromagnetic wave interception, excellent specific strength and absorptiveness of vibration. Although magnesium alloy with above characteristic is a subject matter which is suitable in world-wide tendency of electrical component frame, sheet magnesium alloy is difficult to process. Therefore, forming analysis of sheet magnesium alloy and applying warm-working to process are indispensable. Among Finite element method, the static implicit finite element method is applied effectively to analyze sheet magnesium alloy stamping process, which include the forming stage. In this study, it was focused on the crack, wrinkling and spring back on sheet magnesium alloy stamping by the static implicit analysis. According to this study, the result of simulation will give engineers good information to access the forming technique on sheet magnesium alloy. And its application is being increased especially in the production of electrical component frame for the cost reduction, saving of defective ratio, and improvement of Productivity.

• Proceedings of the Korean Society for Technology of Plasticity Conference
• /
• 2007.10a
• /
• pp.246-249
• /
• 2007

This study is concerned with deep drawability of magnesium sheets(AZ31B) at the warm conditions. Especially the dependency on forming speed has been investigated at the temperature of $200^{\circ}C$ and $300^{\circ}C$. Deep drawing test has been carried out at the temperature of $200^{\circ}C$ and $300^{\circ}C$. The die and blank holder are kept at test temperature by local heating and the punch is kept at room temperature by cooling technique. The magnesium sheets called AZ31B with the thickness of 0.5mm have been applied to deep drawing of circular cup. The drawability has been estimated at the conditions of forming speed (0.1, 1, 10 mm/sec). The results of deep drawing experiments show that the drawability is better at $300^{\circ}C$. Also the deep drawability is improved at the low speed(1mm/sec).

• Transactions of the Korean Society of Mechanical Engineers A
• /
• v.24 no.1 s.173
• /
• pp.87-93
• /
• 2000

Warm, forming technique which is one of the new forming technologies to improve formability of sheet metal is applied to the cylindrical cup drawing of stainless-aluminum. clad sheets. In experiments the temperature of die and blank holder is varied from room temperature to 18$0^{\circ}C$, while the punch is cooled by circulation of coolant to increase the fracture strength of workpiece on the punch corner area. Test materials chosen for experiments are STS304-A1050-STS304, STS304-A1050-STS430 clad sheets and A1050-0 aluminum sheet. Teflon film as a lubricant is used on both sides of a workpiece. The limit drawing ratio as well as quality of drawn cups(distribution of thickness and hardness)are investigated and validity of warm drawing process is also discussed.