• Proceedings of the Korean Powder Metallurgy Institute Conference
• /
• 2006.09a
• /
• pp.642-643
• /
• 2006

Direct reduction and carburization process was thought one of the best methods to make nano-sized WC powder. The oxide powders were mixed with graphite powder by ball milling in the compositions of WC-5,-10wt%Co. The mixture was heated at the temperatures of $600{\sim}800^{\circ}C$ for 5 hours in Ar. The reaction time of the reduction and carburization was decreased as heating temperatures and cobalt content increased. The mean size of WC/Co composite powders was about 260 nm after the reactions. And the mean size of WC grains in WC/Co composite powders was about 38 nm after the reaction at $800^{\circ}C$ for 5 hours.

• Asian Journal of Innovation and Policy
• /
• v.12 no.3
• /
• pp.304-322
• /
• 2023

Text data mining ('big data methods') is one of the most widely used approaches during the COVID-19 pandemic. In particular, text data mining on Scopus databases or Web of Science (WoS). Text data mining is widely used to collect literature for later bibliometric analysis, and in the end, it becomes a literature review article. Therefore, in this article, we reveal the trend of publication of literature reviews in Scopus journals from Indonesia, Japan, South Korea, Vietnam, Singapore, and Malaysia. This article describes two essential parts, namely 1) a comparison of international publication trends and subject area of literature review publications, and 2) a comparison of Top 5 for Authors, Affiliation, Source Title, and Collaboration Country.

• Economic and Environmental Geology
• /
• v.12 no.4
• /
• pp.181-195
• /
• 1979

The Nambu orebodies of the Okbang tungsten mine are hosted in the Precambrian amphibolite and Weonnam formation. These orebodies can be classified into two types; The scheelite-bearing ore vein occurring in the amphibolite (the Nambu 1, 2 adits) and tungsten-bearing quartz vein along the contact between the amphibolite and the Weonnam formation (the Young-ho, -1, -2, -3 levels). The scheelite-bearing ore vein in the amphilbolite is discontinuous, narrow, and highly irregular in geometry, occurring only within the amphibolite with which of the vein is graduational. Based on these feature of the mode of occurrence, the origin of this ore type might be attributed to a potential segregation of tungsten ore fluid in situ from hornblenditic basic magma of the host rock. Tungsten-bearing quartz vein, however, is considered to have deposited along the N30-60E trending fractures as a later hypothermal vein after the hornblendite was emplaced. The principal ore mineral is scheelite with minor amount of wolframite, and the gangue minerals are quartz, and small amounts of fluorite, pyrrhotite, chalcopyrite and calcite. Fluid inclusion study of minerals from the Nambu orebody reveals that the fluids in fluorite of the scheelite-bearning ore vein attained a temperature range of $208{\sim}256^{\circ}C$ and those in quartz from the tungsten-bearing quartz vein a temperature range of $220{\sim}357^{\circ}C$. The real formation temperatures can be somewhat higher than filling temperatures, if pressure correction is made. Chemical analysis of 8 amphibolitc samples on major and some trace elements indicate that the amphibolite is igneous origin. On a Niggli diagram (al-alk)versus c, the analytical values are plotted on an igneous field, and on a Niggli diagram mg versus c they follow a karroo igneous trend line. According to the Ba, Cr, and Ni versus Niggli mg plots suggested by Leake (1964), Okbang amphibolite fall outside a pelitic field and compare favorably with his plots form ortho-amphibolites. Analitical values of $MoO_3$ of 8 samples of scheelite minerals from the Nambu orebody indicate that the tungsten-bearing quartz vein (type n) of Nambu orebody shows a range from 1. 69% to 4.38% which is higher than 0.94%~3.25% $MoO_3$ for the scheelite-bearing ore vein (type I). This fact indicates that the type II was deposited in a lower $fO_2/higher$ $fO_2$ environment and under lower temperature than the type I. Analysis of major components $WO_3$, MnO, and FeO of 6 samples of wolframite from the type II veins revealed that they contain 73.35~76.2% $WO_3$, 7.94~11.63% MnO, and 10.53~14.82% FeO. MnO/FeO ratios of wolframite shows the range of 0.85~1.17 which suggests a slightly higher temperature type of deposits than other major tungsten deposits in the country.

• Journal of Environmental Science International
• /
• v.12 no.1
• /
• pp.47-54
• /
• 2003

This paper have examined the optimum combination of SNCR and SCR by varying SNCR injection temperature and NSR ratio along with SCR space velocity. NOx reduction experiments using a SNCR/SCR combined process have been conducted in simple NO/NH$_3$/O$_2$ gas mixtures. Total gas flow rate was kept constant 4 liter/min throughout the SNCR and SCR reactors, where initial NOx concentration was 500 ppm in the presence of 5% O$_2$. Commercial catalyst, sulfated V$_2$O$\_$5/-WO$_3$/TiO$_2$, was used for SCR NOx reduction. The residence time and space velocity were around 1.67 sec, 2,400 h$\^$-1/ and 6,000 h$\^$-1/ in the SNCR and SCR reactors, respectively. SNCR NOx reduction effectively occurred in a temperature window of 900-950$^{\circ}C$. About 88% NOx reduction was achieved with an optimum temperature of 950$^{\circ}C$ and NSR=1.5. SCR NOx reduction using commercial V$_2$O$\_$5/-WO$_3$-SO$_4$/TiO$_2$ catalyst occurred in a temperature window of 200-450$^{\circ}C$ 80-98% NOxreduction was possible with SV=2400 h$\^$-1/ and a molar ratio of 1.0-2.0. A SNCR/SCR(SV=6000 h$\^$-1/) combined process has shown same NOx reduction compared with a stand-alone SCR(SV=2400 h$\^$-1/) unit process of 98% NOx reduction. The NH$_3$-based chemical could routinely achieve SNCR/SCR combined process total NOx reductions of 98% with less than 5 ppm NH$_3$ slip at NSR ranging from about 1.5 to 2.0, SNCR temperature of 900$^{\circ}C$-950$^{\circ}C$, and SCR space velocity of 6000 h$\^$-1/. Particularly, more than 98% NOx reduction was possible using the combined process under the conditions of T$\_$SNCR/=950$^{\circ}C$, T$\_$SCR/=350$^{\circ}C$, 5% O$_2$, SV=6000 h$\^$-1/ and NH$_3$/NOx=1.5. A catalyst volume was about three times reduced by SNCR/SCR combined process compared with SCR process under the same controlled conditions.

• Journal of Information Display
• /
• v.6 no.2
• /
• pp.25-29
• /
• 2005

The luminescent properties of $Eu^{3+}$ and $Sm^{3+}$ doped potassium tungstate phosphor are investigated. The $K_{4-3x}(WO_4)_2:Eu^{3+}\;_x,Sm^{3+}\;_y$ phosphor is produced by firing the mixed precursors, followed by re-firing with a flux. The re-firing process results in the defect-free surface and uniform growth of the particles. The strong absorption in the region of ultra violet light is observed due to the 4f-4f electron transitions of the $Eu^{3+}$ and $Sm^{3+}$ ions. The doping concentration of europium into potassium tungstate is relatively high, compared to other host materials. It is revealed that the crystal structure is a monoclinic with space group, C2/c. This crystal structure facilitated the $Eu^{3+}$ ions to be located with the Eu-Eu distance larger than 5 ${\AA}$ so that concentration quenching does not occur even at high doping concentration. The excitation spectrum could be adjusted by the introduction of the samarium. A small amount of the $Sm^{3+}$ ions that acts as a sensitizer increases the energy absorption peak around 405 nm.

• Proceedings of the Korean Institute of Surface Engineering Conference
• /
• 2014.11a
• /
• pp.178-179
• /
• 2014

In this study, $Ni-W-Si_3N_4$ alloy composite coatings were prepared by pulse electrodeposition method using nickel sulfate bath with different contents of tungsten source, $Na_2WO_4.2H_2O$, and dispersed $Si_3N_4$ nano particles. The structure and microstructure ofcoatings was separately analyzed by X-ray diffraction (XRD) and scanning electron microscope (SEM). Results indicated that nano $Si_3N_4$ and W content in alloy had remarkable effect on microstructure, microhardness and scratch resistant properties. Tungsten content in Ni-W and $Ni-W-Si_3N_4$ alloy ranged from 7 to 14 at.%. Scratch test results suggest that as compared to Ni-W only, $Ni-W-Si_3N_4$ prepared from Ni/W molar ratio of 1:1.5 dispersed with 20 g/L $Si_3N_4$ has shown the best result among different samples.

• Proceedings of the Korean Institute of Surface Engineering Conference
• /
• 2015.05a
• /
• pp.171-172
• /
• 2015

$Ni-W-Si_3N_4$ alloy composite coatings were prepared by pulse electro-deposition method using nickel sulfate bath with different contents of tungsten source, $Na_2WO_4.2H_2O$, and dispersed $Si_3N_4$ nano-particles. The structure and micro-structure of coatings was separately analyzed by X-ray diffraction (XRD) and scanning electron microscope (SEM). Results indicated that nano $Si_3N_4$ and W content in alloy had remarkable effect on micro-structure, micro-hardness and scratch resistant properties. Tungsten content in Ni-W and $Ni-W-Si_3N_4$ alloy ranged from 7 to 14 at.%. Scratch test results suggest that as compared to Ni-W only, $Ni-W-Si_3N_4$ prepared from Ni/W molar ratio of 1:1.5 dispersed with 20 g/L $Si_3N_4$ has shown the best result among different samples.

• Korean Journal of Chemical Engineering
• /
• v.35 no.12
• /
• pp.2365-2378
• /
• 2018

We investigated the correlation between vanadium surface density and VOx structure species in the selective catalytic reduction of NOx by $NH_3$. The properties of the $VOx/TiO_2$ catalysts were investigated using physicochemical measurements, including BET, XRD, Raman spectroscopy, FE-TEM, UV-visible DRS, $NH_3-TPD$, $H_2-TPR$, $O_2-On/Off$. Catalysts were prepared using the wet impregnation method by supporting 1.0-3.0 wt% vanadium on $TiO_2$ thermally treated at various calcination temperatures. Through the above analysis, we found that VOx surface density was $3.4VOx/nm^2$, and the optimal V loading amounts were 2.0-2.5 wt% and the specific surface area was $65-80m^2/g$. In addition, it was confirmed that the optimal VOx surface density and formation of vanadium structure species correlated with the reaction activity depending on the V loading amounts and the specific surface area size.

• Journal of the Korean earth science society
• /
• v.21 no.5
• /
• pp.553-562
• /
• 2000

Daejeonsa basalt in the Mt. Juwang area is composed of 12 lava flows alternate with 9 peperites, and each lava and peperite has variable thickness. Globular peperites yielded in Daejeonsa basalt are mixed basalt clasts with reddish shale. Based on field description, when lava flows over unconsolidated wet shale or injectes into unconsolidated wet shale, peperites were formed at the contacts between lava and shale. Daejeonsa basalt are massive lava flows with rare vesicules: some vesicules are found in upper part of a flow unit. The basalt has mainly pseudomorphs of olivine as phenocryst, and also plagioclase and clinopyroxene phenocrysts in rocks with higher Mg-number. Matrix is mainly subophitic texture, sometimes showing ophitic and intergranular textures due to different cooling rate. Clinopyroxene is augite(Wo$_{41.6}$En$_{45.1}$Fs$_{13.3}$), and plagioclase is mostly labradorite(An$_{55.0}{\sim}_{67.7}$), but some is andesine(An$_{44.3}$) and bytownite(An$_{74.5}$). Oxide minerals are composed of titanomagnetite and ilmenite.

• Applied Chemistry for Engineering
• /
• v.5 no.2
• /
• pp.327-336
• /
• 1994

The synergistic effects in mechanical mixture catalysts of Mo-V-O and metal oxide were investigated for the selective oxidation of acrolein. The metal oxides used are $SnO_2$, ${\alpha}-Sb_2O_4$, $WO_3$, ${\alpha}-Al_2O_3$, CuO, $MnO_2$, $Cu_2O$, MgO, CoO, and ZnO. Mechanical mixtures of Mo-V-O plus $SnO_2$ or ${\alpha}-Sb_2O_4$ had resulted in higher conversion of acrolein and higher yield of acrylic acid than Mo-V-O. The origin of the synergy is attributed to the cooperation of Mo-V-O and $SnO_2$ or ${\alpha}-Sb_2O_4$, in which $SnO_2$ or ${\alpha}-Sb_2O_4$ forms dissociated oxygens at their oxygen vacancies and transports them to Mo-V-O. $Cu_2O$, MgO, CuO, and $MnO_2$, increased conversion of acrolein but decreased yield of acrylic acid. CoO and ZnO inhibited the catalytic performance of Mo-V-O. The different role of these metal oxides is explained in terms of their oxidation-reduction properties.