• Journal of Power System Engineering
• /
• v.18 no.5
• /
• pp.122-128
• /
• 2014

Generally, the mechanical components and structures are joined by many welding techniques, and therefore the welded joints are inevitable in the construction of structures. The Alloy 617 was initially developed for high temperature applications above $800^{\circ}C$. It is often considered for use in aircraft and gas turbines, chemical manufacturing components, and power generation structures. Especially, the Alloy 617 is the primary candidate for construction of intermediate heat exchanger (IHX) on a very high temperature reactor (VHTR) system. In the present paper, the low cycle fatigue (LCF) life of Alloy 617 base metal (BM) and the gas tungsten arc welded (GTAWed) weld joints (WJ) are evaluated by using the previous experimental results under strain controlled LCF tests. The LCF tests have been performed at room temperature with total strain ranges of 0.6, 0.9, 1.2 and 1.5%. The LCF lives for the BM and WJ have been evaluated from the Coffin-Manson and strain energy based life methods. For both the BM and WJ, the LCF lives predicted by both Coffin-Manson and strain energy based life methods was found to well coincide with the experimental data.

• Journal of the Korean Ceramic Society
• /
• v.50 no.1
• /
• pp.37-42
• /
• 2013

Tristructural-isotropic (TRISO)-coated particles were fabricated by a fluidized-bed chemical vapor deposition (FBCVD) method for use in a very high temperature gas-cooled reactor (VHTR). ZrC as a constituent layer of TRISO coating layers was deposited by a chloride process using $ZrCl_4$ and $CH_4$ source gases in a temperature range of $1400^{\circ}C$ and $1550^{\circ}C$. The change in the microstructure of ZrC depending on the deposition temperature and its effect on the hardness were evaluated. As the deposition temperature increased to $1500^{\circ}C$, the grain size of the ZrC increased and the hardness of the ZrC decreased according to the Hall-Petch relationship. However, at $1550^{\circ}C$, the ZrC layer was highly non-stoichiometric and carbon-rich and did not obey the Hall-Petch relationship in spite of the decrease of the grain size. A considerable amount of pyrolytic carbon at the grain boundaries of the ZrC as well as coarse granular pyrolytic carbon were locally distributed in the ZrC layer deposited at $1550^{\circ}C$. Therefore, the hardness decreased largely due to the formation of a large amount of pyrolytic carbon in the ZrC layer.

• Applied Chemistry for Engineering
• /
• v.24 no.2
• /
• pp.165-170
• /
• 2013

An external gelation method in place of an internal gelation method applied to the fabrication process of an intermediated compound of Uranium Oxy-Carbide (UCO) kernel spheres for Very High Temperature Reactor (VHTR) fuel preparation is under development in Korea. For the preliminary experiments of the UCO kernel sphere preparation using an external gelation method, the carbon black dispersion experiments were carried out using a simulated broth solution. From the selection experiments of various kinds of carbon black through dispersion experiments in a viscous metal salt solution, Cabot G carbon black was selected owing to its dispersion stability, and the homogeneous dispersing state of carbon black particles in our system. For the effective dispersion of nano-size aggregated carbon black particles in a high viscous liquid, the carbon black particles in a metal salt solution were first de-aggregated with ultrasonic force. The mixed solution was then dispersed secondly by the use of the extremely high-speed agitation with a mechanical mixer of 6000 rpm after feeding the Poly Vinyl Alcohol (PVA) in the solution. This results in the broth solution with good stability and homogeneity alongside no further changes in physical properties.