• 한국초전도ㆍ저온공학회논문지
• /
• 제19권1호
• /
• pp.17-21
• /
• 2017

Vanadium slags is a kind of vanadiferous solid waste from steelmaking process. It not only occupies land, pollutes environment, but also leads to waste of resources. Based on the difference of magnetic susceptibility of different particles caused by their chemical and physical properties from vanadium slag, a new technology, superconducting high gradient magnetic separation was investigated for separation and extraction of valuable substances from vanadium slag. The magnetic concentrate was obtained under optimal parameters, i.e., a particle size -200 mesh, a magnetic flux density of 0.8 T, a slurry concentration of 5 g/L, an amount of steel wools of 25 g and a slurry flow velocity of 2 L/min. The content of $Fe_2O_3$ in concentrate could be increased from 39.6% to 55.0% and $V_2O_5$ from 2.5% to 4.0%, respectively. The recovery rate is up to 42.9%, and the vanadium slag has been effectively reused.

• 자원리싸이클링
• /
• 제9권1호
• /
• pp.52-62
• /
• 2000

건축용 고품질 골재, 시멘트 산업 그리고 체절용 플럭스 등 보다 더 가치 있는 분야로의 전로슬랙의 재활용을 극대화하기 위해서는 사용목적에 맞게 전로슬랙의 조성과 특성을 조절하는 것이 대단히 중요하다. 본 연구에서는 슬랙의 화원.개질을 목적으로 전로슬랙에 $SiO_2$의 첨가량을 바꾸고 일정량의 탄소를 섞어 $1650^{\circ}C$에서 환원 용해하였다. 환원이 종료된 후, 개질된 슬랙은 노대에서 상온까지 서냉하였다. 얻어진 슬랙에 대하여 SEM-EDX, XRD, Chemical Anaysis에 의해 상조직, 상분포, 조성분포등을 조사하였다. 또한 자연골재와의 물성비교를 위하여 압축강도와 밀도도 측정하였다. XRD분석에 의하면, 전로슬랙 중량에 대하여 10%의 $SiO_2$를 첨가하여 환원개질한 전로슬랙은 bredigite + merwmite의 혼합상으로 존재하며, 20% 및 30% $SiO_2$를 첨가한 경우엔 모두 akcrmante로 존재하고 있다. 그러나 SEM-EDX 분석 결과는 개질슬랙의 상분포가 슬랙조성에 따라 아주 민감하게, 그리고 복잡하게 변화함을 보여주고 있다. 또한 개질슬랙의 성질은 이러한 상분포에 의해 많은 영향을 받는다. 카드뮴 약 1/3과 바나듐의 약 1/5은 환원후에도 개질슬랙중에 남으며, 그밖의 많은 중금속원소들은 환원개질에 의해 90%~95% 이상의 금속철 중에 흡수되거나 휘발하여 제거된다. 25%의 $SiO_2$를 혼합하여 환원한 후 서냉에 의해 얻은 개질전로슬랙의 압축강도와 밀도는 자연화강암에 거의 근접한 값을 보이고 있어, 고품질의 건축용 골재로도 사용 가능하며, 이는 Thyssen 제철소에서 개발하여 건축용으로 공급하고 있는 $SiO_2$를 첨가한 산화개질 슬랙골재 보다도 우수한 것이다.