• Korean Chemical Engineering Research
• /
• v.57 no.1
• /
• pp.17-21
• /
• 2019

The redox flow battery (RFB) is a large-capacity energy storage equipment, and the vanadium redox flow cell is a typical RFB, but VRFB is expensive. Iron-chrome RFBs are economical because they use low-cost active materials, but their low performance is an urgent problem. One of the reasons for the low performance is the crossover of the active materials. In this study, the sulfonated Poly (ether ether ketone) (sPEEK) membrane, which is a hydrocarbon membrane, was used instead of the fluorine membrane to reduce the crossover of the active materials. The chromium ion permeability of the sPEEK membrane was $1.8{\times}10^{-6}cm^2/min$, which was about 1/33 of that of the Nafion membrane. Thus, it was shown that the use of the sPEEK membrane instead of the fluorine membrane could solve the high active material crossover problem. The activation energy of iron diffusion through the sPEEK membrane was 24.9 kJ/mol, which was about 66% of Nafion membrane. And that the e-PTFE support in the polymer membrane reduces the active material crossover through Iron-Chrome Redox Flow Battery (ICRFB).

• Journal of the Korea Academia-Industrial cooperation Society
• /
• v.19 no.10
• /
• pp.598-602
• /
• 2018

This study examined the characteristics of the waste catalyst used in the petroleum refinery operations. The total pore volume, specific surface area, and average pore size of the spent catalyst used in the petroleum refinery operations were 3.96cc/g, 13.81m2/g, and 1.15A, respectively. The weight loss observed in the range from $25^{\circ}C-700^{\circ}C$ for the spent catalysts using TG and DTA was approximately 23 wt. %. EDS analysis of the waste catalyst sample showed that the five major components were vanadium, nickel, manganese, iron, and copper. The extraction system is attractive for liquid-liquid extraction. In this study, Cynex 272 was used to extract vanadium from waste catalyst. The electrochemical characteristics of the extracted vanadium solution were measured by cyclic voltammetry (CV). As a result, an oxidation / reduction peak appeared, indicating the potential of an electrolytic solution.

• Resources Recycling
• /
• v.31 no.2
• /
• pp.20-32
• /
• 2022

This study implemented a chelating agent (Ethylenediaminetetraacetic acid, EDTA) in purification to obtain high-purity vanadium pentoxide (V₂O₅) for use in VRFB (Vanadium Redox Flow Battery). V₂O₅ (powder) was produced through the precipitation recovery of ammonium metavanadate (NH₄VO₃) from a vanadium solution, which was prepared using a low-purity vanadium raw material. The initial purity of the powder was estimated to be 99.7%. However, the use of a chelating agent improved its purity up to 99.9% or higher. It was conjectured that the added chelating agent reacted with the impurity ions to form a complex, stabilizing them. This improved the selectivity for vanadium in the recovery process. However, the prepared V₂O₅ powder exhibited higher contents of K, Mn, Fe, Na, and Al than those in the standard counterparts, thus necessitating additional research on its impurity separation. Furthermore, the vanadium electrolyte was prepared using the high-purity V₂O₅ powder in a newly developed direct electrolytic process. Its analytical properties were compared with those of commercial electrolytes. Owing to the high concentration of the K, Ca, Na, Al, Mg, and Si impurities in the produced vanadium electrolyte, the purity was analyzed to be 99.97%, lower than those (99.98%) of its commercial counterparts. Thus, further research on optimizing the high-purity V₂O₅ powder and electrolyte manufacturing processes may yield a process capable of commercialization.