• Korean Journal of Chemical Engineering
• /
• v.35 no.12
• /
• pp.2365-2378
• /
• 2018

We investigated the correlation between vanadium surface density and VOx structure species in the selective catalytic reduction of NOx by $NH_3$. The properties of the $VOx/TiO_2$ catalysts were investigated using physicochemical measurements, including BET, XRD, Raman spectroscopy, FE-TEM, UV-visible DRS, $NH_3-TPD$, $H_2-TPR$, $O_2-On/Off$. Catalysts were prepared using the wet impregnation method by supporting 1.0-3.0 wt% vanadium on $TiO_2$ thermally treated at various calcination temperatures. Through the above analysis, we found that VOx surface density was $3.4VOx/nm^2$, and the optimal V loading amounts were 2.0-2.5 wt% and the specific surface area was $65-80m^2/g$. In addition, it was confirmed that the optimal VOx surface density and formation of vanadium structure species correlated with the reaction activity depending on the V loading amounts and the specific surface area size.

• Applied Chemistry for Engineering
• /
• v.33 no.6
• /
• pp.594-599
• /
• 2022

In the study, NH₃-SCO (selective catalytic oxidation) reaction activity accodrding to vanadium loading amount were compared when preparing Pt/V/TiO₂. Considering both NH₃ conversion rate and N₂ selectivity, V 2 wt% loading of the catalyst showed the best activity. When the correlation between physical/chemical characteristics and reaction activity was confirmed, it was confirmed that the increase in lattice oxygen and (V³⁺ + V⁴⁺) ratios were active factor. In addition, when the SO₂ durability experiment was conducted using the best catalyst, it was confirmed that the influence was insignificant even if the high concentration of SO₂ was injected.

• Bulletin of the Korean Chemical Society
• /
• v.28 no.12
• /
• pp.2459-2465
• /
• 2007

V2O5/TiO2-ZrO2 catalyst modified with V2O5 was prepared by adding Ti(OH)4-Zr(OH)4 powder into an aqueous solution of ammonium metavanadate followed by drying and calcining at high temperatures. The characterization of prepared catalysts was performed using XRD, DSC, solid-state 51V NMR, and FTIR. In the case of calcination temperature of 500 oC, for the catalysts containing low loading V2O5 below 25 wt % vanadium oxide was in a highly dispersed state, while for catalysts containing high loading V2O5 equal to or above 25 wt % vanadium oxide was well crystallized due to the V2O5 loading exceeding the formation of monolayer on the surface of TiO2-ZrO2. The strong acid sites were formed through the bonding between dispersed V2O5 and TiO2-ZrO2. The larger the dispersed V2O5 amount, the higher both the acidity and catalytic activities for acid catalysis.

• Applied Chemistry for Engineering
• /
• v.33 no.5
• /
• pp.482-487
• /
• 2022

In this study, the activity test and characterization were performed to evaluate the hydrogen sulfide removal characteristics using a V/TiO₂ catalyst at room temperature. The optimal vanadium loading was 10 wt%, and the durability was greater than 60 minutes at 60~80% relative humidity. The Brunauer-Emmett-Teller (BET) surface area and raman spectroscopy results confirmed that the structure of the vanadium site exposed to the surface was a dominant factor in catalyst activity. From Scanning Electron Microscope (SEM), Energy Dispersive Spectroscopy (EDS) and X-ray crystallography (XRD) analyses, it was found that sulfur can be accumulated on the catalyst surface, which results in a decrease in durability under catalytic activity tests. Therefore, it is judged that a combined process of catalytic oxidation and regeneration is needed.

• Applied Chemistry for Engineering
• /
• v.23 no.5
• /
• pp.485-489
• /
• 2012

We investigated vanadium (V) loading effects on selective catalytic reduction (SCR) activity and $SO_2$ resistance using commercial SCR catalysts applied on a power plant and incinerator with different amounts of V loading. These catalysts were characterized using XRD, Raman, ICP, BET analysis and found to contain $TiO_2$ (anatase) supported $V_2O_5$ added $WO_3$ and $SiO_2$. The SCR activity of the catalysts increased by increasing either the $V_2O_5$ or the $WO_3$ loading amounts; the SCR activity of the catalysts added $WO_3$ is higher than that of $WO_3$-free catalysts. As the V loading amount in the catalyst increased, the $SO_2$ durability decreased. The $V_2O_5$ supported $TiO_2$ catalyst added $WO_3$ and $SiO_2$ inhibits the deactivation process by $SO_2$. The $SO_2$ resistance of catalysts added $SiO_2$ is higher than that of catalysts added $WO_3$.

• Journal of Korean Society for Atmospheric Environment
• /
• v.13 no.6
• /
• pp.487-495
• /
• 1997

The most desirable diesel oxidation catalyst (DOC) should have the properties of oxidizing CO, HC and SOF effectively at low exhaust gas temperature while minimizing the formation of sulfate at high exhaust gas temperature. Precious metals such as platinum and palladium have been known to be sufficiently active for oxidizing SOF and also to have high activity for the oxidation of sulfur dioxide $(SO_2)$ to sulfur trioxide $(SO_3)$. There is a need to develop a highly selective catalyst which can promote the oxidation SOF efficiently, on the other hand, suppress the oxidation of $SO_2$. In this study, a Pt-V catalyst was prepared by impregnating platinum and vanadium onto a Ti-Si wash coated ceramic monolith substrate. A prepared Pt-V catalytic converter was installed on a heavy duty diesel engine and the effect of fuel sulfur on particulate matter (PM) of heavy duty diesel engine was measured. The effect of fuel sulfur on PM of Pt-V was also compared with that of a commercialized Pt catalyst currently being used in some of the heavy duty diesel engines in advanced countries. Only 1 $\sim$ 3% of sulfur in the diesel fuel was converted to sulfate in PM for the engine without catalyst, but almost 100% of sulfur conversion was achieved for the engine with Pt catalyst at maximum loading condition. In the case of Pt-V catalyst, there was no big difference in conversion with the base engine even at maximum loading condition. The reason of SOF increase according to the increase of suflate emission was identified as the washing off effect of bound water in sulfate.

• Journal of the Korean Chemical Society
• /
• v.55 no.1
• /
• pp.81-85
• /
• 2011

$V_{0.9}Sb_{0.1}O_x$ systems, bulk and deposited on different supports (five types of $\gamma$-aluminas, $\alpha$-alumina, silica-alumina, silica gel, magnesium oxide), have been tested in the oxidative dehydrogenation (ODH) of iso-butane. Catalytic performance of VSb oxides has shown to be highly dependent on the support and the nature of the support decreasing in a series: $\gamma$-$Al_2O_3$ > $\alpha$-$Al_2O_3$ > Si-Al-O > $SiO_2$ $\approx$ MgO $\gg$ unsupported. Variation of the V-Sb-O-loading in the studied range of coverage (0.5-2 theoretical monolayer) only slightly influences the catalysts' activity and selectivity. The best catalytic performance of $\gamma$-alumina-supported $V_{0.9}Sb_{0.1}O_x$ systems can be explained by the optimal surface interaction between support and supported components resulting in the formation of well-spread amorphous active $VO_x$-component with vanadium in a high oxidation state.

• Korean Chemical Engineering Research
• /
• v.51 no.3
• /
• pp.313-318
• /
• 2013

In order to investigate the effect of $V_2O_5$ loading of $V_2O_5-WO_3/TiO_2$ catalyst on the NO reduction and the formation of $N_2O$, the experimental study was carried out in a differential reactor using the powder catalyst. The NO reduction and the ammonia oxidation were, respectively, investigated over the catalysts compose of $V_2O_5$ content (1~8 wt%) based on the fixed composition of $WO_3$ (9 wt%) on $TiO_2$ powder. $V_2O_5-WO_3/TiO_2$ catalysts had the NO reduction activity even under the temperature of $200^{\circ}C$. However, the lowest temperature for NO reduction activity more than 99.9% to treat NO concentration of 700 ppm appeared at 340 with very limited temperature window in the case of 1 wt% $V_2O_5$ catalyst. And the temperature shifted to lower one as well as the temperature window was widen as the $V_2O_5$ content of the catalyst increased, and finally reached at the activation temperature ranged $220{\sim}340^{\circ}C$ in the case of 6 wt% $V_2O_5$ catalyst. The catalyst of 8 wt% $V_2O_5$ content presented lower activity than that of 8 wt% $V_2O_5$ content over the full temperature range. NO reduction activity decreased as the $V_2O_5$ content of the catalyst increased above $340^{\circ}C$. The active site for NO reduction over $V_2O_5-WO_3/TiO_2$ catalysts was mainly related with $V_2O_5$ particles sustained as the bare surface with relevant size which should be not so large to stimulate $N_2O$ formation at high temperature over $320^{\circ}C$ according to the ammonia oxidation. Currently, $V_2O_5-WO_3/TiO_2$ catalysts were operated in the temperature ranged $350{\sim}450^{\circ}C$ to treat NOx in the effluent gas of industrial plants. However, in order to save the energy and to reduce the secondary pollutant $N_2O$ in the high temperature process, the using of $V_2O_5-WO_3/TiO_2$ catalyst of content $V_2O_5$ was recommended as the low temperature catalyst which was suitable for low temperature operation ranged $250{\sim}320^{\circ}C$.