• 동력기계공학회지
• /
• 제5권3호
• /
• pp.88-94
• /
• 2001

Stellite 12 alloy-powders were overlaid on 410 stainless steel valve seat using plasma transferred arc(PTA) process. Variation of the microstructure, hardness, wear and corrosion of overlaid deposit with current change was investigated. The deposit showed hypoeutectic microstructure, which was consisted of primary cobalt dendrite and networked $M_7C_3$ type eutectic carbides. As current increased, the amount of eutectic carbide decreased and its dendritic secondary arm spacing increased. Hardness of the deposit was decreased with increase of current. Stress relief heat treatment at $600^{\circ}C$ for two hours resulted in slight increase of hardness in the deposit and showed uniform hardness distribution in base metal without any hardened layer in HAZ. Specific wear decreased with increase of sliding distance. The deposit of high hardness with a lot of eutectic carbide showed relatively low specific wear. Initial corrosion current density of the deposit in 0.1N sulfuric acid was lower than those of 410 stainless steel, and showed a little variation with PTA current.

• Journal of Advanced Marine Engineering and Technology
• /
• 제40권9호
• /
• pp.768-773
• /
• 2016

엔진 밸브 시트와 페이스는 엔진 성능에 영향을 미치므로 내마모성, 내열성 및 내식성이 요구된다. 이러한 특성을 갖는 표면층을 형성하기 위해 일반적으로 PTA 프로세스를 사용하고 있지만 넓은 열 영향부와 높은 모재 희석 등과 같은 문제가 발생한다. 이러한 단점을 개선한 레이저 클래딩은 희석률이 낮고 열 영향 및 열 변형을 최소화하므로 더욱 우수한 클래드 층을 형성할 수 있다. 하지만 레이저 빔의 특성상 넓은 면적을 클래딩 할 경우, 1 패스 클래드 층의 중첩이 불가피하다. 중첩률 기준을 빔 사이즈와 클래드 층 폭으로 나누어 멀티패스 클래드 층을 형성한 결과, 기준에 관계없이 중첩률이 증가할수록 클래드 층의 폭이 감소하고 높이가 증가하였다. 하지만 빔 사이즈 기준 중첩률 조건으로 형성된 멀티패스 클래드 층이 다른 기준보다 모재 희석이 감소하여 더욱 높은 경도 값을 나타내었다. 결론적으로, 중첩률 기준을 클래드 층 폭으로 할 경우, 클래드 층 형상에 영향을 주는 공정변수가 변할 때 마다 폭의 길이가 달라지기 때문에 빔 사이즈를 중심으로 중첩률을 정의하였다.