• 펄프종이기술
• /
• 제32권2호
• /
• pp.8-15
• /
• 2000

This study is a continuation of the previous experimental analysis and is mostly focused on handsheet strength properties. Four completely different fibers, which were Hw-BKP, SW-BKP, White ledger, and OCC, were selected to investigate the effect of mechanical pre-treatment by Hobart mixer on handsheet strehgth properties. After equal time mechanical pre-treatment, the fibers were refined with laboratory valley beater for 10, 20 and 30 minutes, and handsheets were prepared from the fibers for physical strength comparison. Handsheets from SW-BKP and OCC showed 5-30% increase of breaking length, burst index, tear index, and compression index while handsheets from HW-BKP and White ledger no increase except tear index. In Hobart mixer pre-treatment, HW-BKP and White ledger fibers were easily attached to the wall of the mixer bowl and mechanical action was not effectively applied. The fiber length of Hw-BKP and White ledger were 0.837 mm and 1.591 mm, respectively, while SW-BKP and OCC were 2.744 mm and 2.033 mm, respectively, in weight weighted length. The effective mechanical pre-treatment seems to be related to the fiber length. Tear indexes of the pre-treated furnish were much higher than no pre-treatment at the same breaking length level.

• 한국펄프종이공학회:학술대회논문집
• /
• 한국펄프종이공학회 2000년도 춘계학술발표논문집
• /
• pp.70-70
• /
• 2000

This study is a continuation of the previous experimental analysis and is mostly focused on handsheet strength properties. Four completely different fibers, which were Hw-BKP, Sw-BKP, white ledger, and OCC, were selected to investigate the effect of mechanical pre-treatment by Hobart mixer on handsheet strength properties. After equal time mechanical pre-treatment, the fibers were refined with laboratory valley beater for 10, 20 and 30 minutes, and handsheets were prepared from the fibers for physical strength comparison. Handsheets from SW-BKP and OCC showed 5-30% increase of breaking length, burst index, tear index, and compression index while handsheets from HW-BKP and white ledger no Increase except tear index. In Hobart mixer pre-treatment, HW-BKP and white ledger fibers were easily attached to the wall of the mixer bowl and mechanical action was not effectively applied. The fiber length of Hw-BKP and white ledger were 0.837mm and 1.591 mm, respectively, while SW-BKP and OCC were 2.744 mn and 2.033 mm, respectively, in weight weighted length. The effective mechanical pre-treatment seems to be related to the fiber length. Tear indexes of the pre-treated furnish were much higher than no pre-treatment at the same breaking length level.