• Clean Technology
• /
• v.14 no.3
• /
• pp.204-210
• /
• 2008

A series of $V_{2}O_{5}-TiO_2$ xerogel catalysts were prepared by nonhydrolytic sol-gel method and analysed by various characterization techniques. These catalysts showed much higher surface areas and total pore volumes than conventional V$V_{2}O_{5}-TiO_2$ xerogel and impregnated $V_{2}O_{5}/TiO_2$ catalysts. It was found that the textural property of $V_{2}O_{5}-TiO_2$ material varies with the method and conditions of synthesis. Surface vanadates and $TiO_2$ anatase phase are the crucial factors to obtain high catalytic activities. The selective oxidation of hydrogen sulfide in the presence of excess water and ammonia was studied over these catalysts. Xerogel catalysts prepared by non-hydrolytic sol-gel method showed very high conversion of $H_{2}S$ without harmful emission of $SO_2$. The highest catalytic activity shown by these $V_{2}O_{5}-TiO_2$ catalysts may be due to their high surface area and good dispersion of vanadia species in the titania matrix.

• Applied Chemistry for Engineering
• /
• v.32 no.3
• /
• pp.326-331
• /
• 2021

In this study, the preparation conditions for a TiO₂-based vanadium-based catalyst for oxidizing hydrogen sulfide at room temperature were optimized. Four types of commercial TiO₂ were used as a catalyst support and the performance evaluation of hydrogen sulfide oxidation at room temperature of V/TiO₂ by varying vanadium contents prepared using the impregnation method was performed. Among the types of TiO₂ tested, it was confirmed that the catalyst with the vanadium content of 5% and based on TiO₂(A) has the best hydrogen sulfide conversion rate of 58%. By comparing the physical and chemical properties of the catalyst, the specific surface area of the support and the species of dominant vanadium are the major factor in catalyst performance. In order to confirm the regeneration characteristics of the catalyst with reduced activity, heat treatment was performed at 400 ℃ for 2 h, and the amount of hydrogen sulfide oxidation decreased by 10% due to the partial deposition of sulfur in the regenerated catalyst, but it was confirmed that the initial performance was similar.

• Applied Chemistry for Engineering
• /
• v.32 no.1
• /
• pp.35-41
• /
• 2021

VWTi, which is used as a commercial catalyst in NH3-SCR, exhibits excellent denitrification performance at 300 to 400 ℃, but there is a problem that efficiency decreases at low temperatures below 300 ℃. Research on catalysts containing promoter to increase low-temperature denitrification efficiency is steadily progressing. However, research on the cause of the improvement in low-temperature denitrification efficiency of the catalyst and the catalyst properties is insufficient. In this study, it was confirmed that by adding Sb to VWTi, denitrification performance was improved by more than 10% in NH3-SCR reaction below 300 ℃. At this time, the space velocity and the size of the catalyst particles were controlled to exclude the influence of external/internal diffusion. In addition, the catalytic properties according to the presence or absence of Sb were investigated by performing BET, TEM/EDS, O2-TPD, H2-TPR and DRIFTs analysis. It was judged that the addition of Sb increased the adsorbed oxygen species on the surface of the catalyst, thereby enhancing the redox properties of the catalyst at low temperature and exhibiting excellent denitrification performance.