• Proceedings of the Korean Society for Technology of Plasticity Conference
• /
• 2005.10a
• /
• pp.406-409
• /
• 2005

In the forging operation of large ingot two break-down process are upsetting and cogging. The first purpose of upsetting is to ensure sufficient forging ratio for subsequent cogging operations and consolidate the voids along the centerline. The second purpose is related to improve the physical properties for a final product. Voids which are generated during the casting process can be one of the decisive defects of materials. So it is necessary to know the standard of Judgment for void-closure in upsetting operation. In practical conditions, FEM analysis(DEFORM 2D 8.1) was carried out to decide how much effective strain has influence on void-closure. It is finally suggested that the function consists of the effective strain of analysis data and the area rate of void.

• Transactions of the Korean Society of Automotive Engineers
• /
• v.14 no.3
• /
• pp.44-50
• /
• 2006

The mono steel forged piston was improved a mechanical strength of an aluminum piston and reduced the weight of a articulated piston. The mono steel forged piston was composed of forged crown part and forged skirt part and was completed by friction welding process of two forged parts. Forging process analysis and friction welding analysis was done by finite element simulation using numerical package DEFORM. The preform shape and the initial billet dimension were decided by maximum stress of the die, amount of the flash and filling of die. The upset length of friction welding variable was decided by the shape of the flash that was created by friction welding analysis. Through this research, we developed a forging process of the mono steel forged piston, and decided the design variables of friction welding.

• Transactions of Materials Processing
• /
• v.27 no.4
• /
• pp.250-256
• /
• 2018

Oxygen-free copper (OFC) was prepared as a 90 mm cube and then processed with Multi-Axial Diagonal Forging - Initialization of Prior manufacturing History (MADF). The MADF process has been newly developed as a severe plastic deformation method. The MADF process consists of upset forging with a thickness reduction of 30% and diagonal forging with a diagonal angle of $135^{\circ}$. 1 cycle process consists of a 12 passes forging process. In order to analyze the characteristic changes according to the number of iterations, 1, 2, and 3 cycles of the MADF process were performed. The OFC specimens were MADF processed without surface cracks up to 3 cycles. The microstructure, hardness and tensile test of processed materials were analyzed to study the change of material properties according to the amount of MADF process. The results showed that the MADF process effectively refined the microstructure and increased the strength of OFC. In the case of specimens processed for more than 2 cycles, the grains of all measurement regions were refined to be less than $7{\mu}m$ of grain size. The 1 cycle MADF processed OFC showed the highest mechanical properties with the hardness of 132 HV and tensile strength of 395 MPa. Hardness and strength seemed to be saturated when processed over 2 cycles.

• Proceedings of the Korean Society of Precision Engineering Conference
• /
• 2003.06a
• /
• pp.418-421
• /
• 2003

Specimens of Ti-10Ta-10Nb have been hot upset forged after heating to either the $\alpha$+$\beta$ and $\beta$-phase field. The variety temperatures (At 650, 700, 750, 800, 85$0^{\circ}C$) and strain rates (At 0.001, 0.01. 0.1, 1, 10 $s^{-1}$ ) were used. On the basis of flow stress data obtained as a function of temperature and strain rate in compression, a processing map for hot working has been developed. At strain rates lower than about 0.1 $s^{-1}$ and almost temperatures, processing efficiency exhibited high, but at 0.001 $s^{-l}$, and temperature 80$0^{\circ}C$, low because the Shear band has occurred. On the basis of the processing map, the optimum processing routes available for hot working of this material are outlined.d.

• Transactions of the Korean Society of Mechanical Engineers
• /
• v.16 no.10
• /
• pp.1877-1889
• /
• 1992

Upsetting is performed in open-die press forging to deform metal in all directions in order to enhance soundness of a product and reduce directionality of properties caused by casting. It is necessary to ensure sufficient forging ratio for subsequent cogging operations and consolidate the void along the centerline. To obtain these benefits, the upper die shape (dome and dished shape) is considered as an upsetting parameter. Thermo-viscoplastic finite element analysis has been carried out so as to understand the influence of upper die shape on the effective strain, hydrostatic stress and temperature in the upset-forged ingots without internal defects. The analysis is focused on the investigation into internal void closure in ingots with pipe holes and circular voids. The computational results have shown that the volume fraction of the void is independent of the circular void size and the closure of internal voids is much more influenced by the effective strain than the hydrostatic stress around the void. It is finally suggested that the height reduction must be over 35% for consolidation of internal voids.

• Transactions of Materials Processing
• /
• v.20 no.3
• /
• pp.236-242
• /
• 2011

The two objectives of this study were, first, to determine the optimal friction welding process parameters using finite element simulations and, second, to evaluate the mechanical properties of the friction welded zone for large piston rods in marine diesel engines. Since the diameters of the rod and its connecting part are very different, the manufacturing costs using friction welding are reduced compared to those using the forging process of a single piece. Modeling is a generally accepted method to significantly reduce the number of experimental trials needed when determining the optimal parameters. Therefore, because friction welding depends on many process parameters such as axial force, initial rotational speed and energy, amount of upset and working time, finite element simulations were performed. Then, friction welding experiments were carried out with the optimal process parameter conditions resulting from the simulations. The base material used in this investigation was AISI 4140 with a rod outer diameter of 280 mm and an inner diameter of 160 mm. In this study, various investigation methods, including microstructure characterization, hardness measurements and tensile and fatigue testing, were conducted in order to evaluate the mechanical properties of the friction welded zone.

• Journal of Welding and Joining
• /
• v.32 no.3
• /
• pp.95-101
• /
• 2014

Joining of grey cast iron by fusion welding has much difficulties for its extremely low ductility and low toughness because of the flake form of the graphite. And the brittle microstructure, i.e. ledeburite may be formed during fusion welding by its rapid cooling rates. By these kinds of welding problem, preheat and post heat treatment temperature must be increased to avoid weld crack or welding problems. In order to avoid these fusion welding problem, friction welding of cast iron was carried out for improving joint soundness, establishing friction welding variables. There is no factor for evaluating friction weldability in continuous drive type friction welding. In this point of view, this study proposed the parameters for calculating friction weld heat input. The results obtained are as follows ; 1. There was a close relationship between tensile strength and flash appearance of friction welded joint. 2. Tensile strength was decreased and flash was severely oxidized as increasing frictional heating time. 3. As increased forging pressure $P_2$, flash had a large crack and tensile strength was decreased. 4. As powdered graphite by rotational frictional force induced flat surface and hindered plastic flow of metal, tensile strength of welded joint was decreased. 5. Heat input for continuous drive type friction welding could be calculated by the factors of $P_1$, $P_2$ and upset distance(${\delta}$).