• Journal of the Korean Recycled Construction Resources Institute
• /
• v.3 no.2
• /
• pp.132-139
• /
• 2015

In this study, the different unit cement content by the ratio of water absorption and water-cement ratio are applied to examine the properties of the concrete used the aggregate recycled by the crushing treatment. According to the experimental results, in the mix of low strength and high water-cement ratio, both of the compressive strength is almost equal in the concrete using the recycled aggregate by the crushing treatment and the concrete using broken stones. It means that the recycled aggregate has the low effect of the amount of bonded mortar. But, in the mix of high strength and low water-cement ratio, the concrete using the recycled aggregate by the crushing treatment has 40% less of the compressive strength than that using broken stones by the effect of the amount of bonded mortar. On the other hand, after 8 weeks, the dry shrinkage of the recycled aggregate with 7% of the ratio of water absorption doubles that of the broken stones with 1% ($-350{\times}10^{-6}$), in other words $-700{\times}10^{-6}$. Thus, the dry shrinkage should be prior to any other conditions in recycling waste concrete for the aggregate for concrete. When the recycled aggregate with 3% of the ratio of water absorption is used, the compressive strength of the rich mix concrete ($450kg/m^3$ of the unit cement content) is equivalent to that of the concrete using broken stones, while in using the recycled aggregate with 7% of the ratio of water absorption, the rich mix concrete has 7% lower compressive strength than the concrete using broken stones. But, the compressive strength of the ordinary mix concrete ($350kg/m^3$ of the unit cement content) is far lower than that using broken stones.

• Journal of the Korean Recycled Construction Resources Institute
• /
• v.8 no.2
• /
• pp.153-160
• /
• 2020

In this study, the optimum ratio of soil-cement was derived to utilize carbon capture minerals(CCM) as soil-cement for deep mixing method, quality characteristics of soil-cement mixed with carbon capture minerals were evaluated. The CCM is generated in the form of a slurry, and as a result of evaluating water content, it was found to be about 50%. Accordingly, the water content of CCM was removed in the unit water of Soil-cement mix. As a result of field mixing of soil-cement using CCM on field soil, it showed that the design allowable bearing capacity was satisfied by showing 3.0MPa or more as of 28 days of age. As a result of the hazard verification of carbon capture minerals, 0.055mg/L of Cu was detected, but satisfies the acceptance criteria, and no other harmful substances were eluted.

• Journal of the Korea Concrete Institute
• /
• v.17 no.2 s.86
• /
• pp.293-302
• /
• 2005

This study describes data from determination of the optimum mix proportion and site application of the mass concrete placed in bottom slab and side wall having a large depth and section as main structures of LNG in-ground tank. This concrete requires low heat hydration, excellent balance between workability and consistency because concreting work of LNG in-ground tank is usually classified by under-pumping, adaptation of longer vertical and horizontal pumping line than ordinary pumping condition. For this purpose, low heat Portland cement and lime stone powder as cementitious materials are selected and design factors including unit cement and water content, water-binder ratio, fine aggregate ratio and adiabatic temperature rising are tested in the laboratory and batch plant. As experimental results, the optimum unit cement and water content are selected under $270kg/m^3$ and $l55{\~}l60 kg/m^3$ separately to control adiabatic temperature rising below $30^{\circ}C$ and to improve properties of the fresh and hardened concrete. Also, considering test results of the confined water ratio($\beta$p) and deformable coefficient(Ep), $30\%$ of lime stone powder by cement weight is selected as the optimum replacement ratio. After mix proportions of 5cases are tested and compared the adiabatic temperature rising($Q^{\infty}$, r), tensile and compressive strength, modulus of elasticity, teases satisfied with the required performances are chosen as the optimum mix design proportions of the side wall and bottom slab concrete. $Q^{\infty}$ and r are proved smaller than those of another project. Before application in the site, properties of the fresh concrete and actual mixing time by its ampere load are checked in the batch plant. Based on the results of this study, the optimum mix proportions of the massive concrete are applied successfully to the bottom slab and side wall in LNG in-ground tank.

• Proceedings of the Korea Concrete Institute Conference
• /
• 2001.11a
• /
• pp.1029-1034
• /
• 2001

The purpose of this research is to develop rapid setting cement latex modified concrete (RSLMC) which will be used to overlay bridge deck for maintaining and repairing. The main experimental variables were the types of rapid setting cement and variation of latex and antifoam agent contents were selected as admixture factor, then the properties of workability and strength development and durability properties were investigated. The results of this study show that latex content give increment of a slump due to surface tension in polymer particles and reduce unit weight of water for preservation of workability. In addition, When no and 1.6~3.2% antifoam agent were mixed, 8%, 2.0~3.8% were respectively obtained. An increasing the amount of latex produced concrete with increased flexural strength, but with slightly lower compressive strength. Rapid chloride permeability and freezing-thawing test carried out. As a results, according to increment of containing ratio antifoamer, strength of RSLMC increase, permeability showed lower value than ignorable 100 coulombs. Also, in the case of more than antifoamer 1.6%, the relativity dynamic modulus is mantained more than 90%, but in case of 0, 5%, it decrease. In consequence, with the view of strength and workability of RSLMC, it is considered that appropriate content ratio of antifoam agent and latex solid are respectively 1.6% by latex weight, 15% by cement weight.

• The Korean Journal of Ceramics
• /
• v.6 no.3
• /
• pp.318-321
• /
• 2000

Most compressive strengths commonly used in the construction field are in a range of 240 to 300 kgf/$\textrm{cm}^2$ at 28 days. To get this rage of strengths, however, high-flowing concrete requires cementitious binders more than 400 to 450 kg/$\textrm{cm}^2$ for preventing segregation and sedimentation of aggregates. This amount of cementitious binder generates a large emission of excessive hydration heat, which may consequently induce harmful cracks in concrete structure. In order to reduce excessive hydration heat, thus, this paper aims at fabricating a high-flowing concrete under the condition that cement content is kept as low as 350kg/$\textrm{cm}^3$ by using viscose agents. In a parametric study, effects of cement types such as a ternary blended cement and Type V on he physical characteristics of high-flowing concrete were evaluated. In addition, the influence of viscosity was also investigated by applying two different viscose agents, one in a range of 6,000 to 10,000 cps and the others of 10,000 to 14,000 cps. In terms of chemical admixtures used in concrete mixture, the superplasticizer was Sulfonated Melamine-Formaldehyde Condensate with about 30,000 of molecular weight, and main component of viscose agent was HPMC (Hydroxy Propyl Methyl Cellulose). Slump flow was fixed at 50cm with different dosages of superplasticizer in weight.

• Proceedings of the Korean Institute of Building Construction Conference
• /
• 2009.05b
• /
• pp.45-48
• /
• 2009

The performance of concrete mainly depend upon its water-cement ratio. If water percentage is excess in concrete, it may cause the degradation of performance. Because of these reasons, the change of water content is managed by using various evaluation method of unit water content. And criterion for the change of water content is regulated and used. However the criterion is set only considering production error and measurement error but criterion does not consider performance degradation of concrete. Therefore this study tries to investigate degradation of performance while adding extra water by artificial manipulation or management error in concrete, The contents of extra water for tests are set as 0, 20, 40, 60kg/m3, to examine the performance degradation of concrete, strength, shrinkage, cracks, carbonation are tested This study conclude that, when extra water content is excess than 20kg/m3 in concrete, then performance level of concrete declined rapidly. 80 it is very important to maintain quality of concrete for its better performance.

• Proceedings of the Korea Concrete Institute Conference
• /
• 1996.10a
• /
• pp.133-139
• /
• 1996

As construction technology advances, most of civil engineering structures are becoming larger and taller. Therefore, high strength concrete is necessary for them. For high strength concrete, it needs a large amount of unit cement content and low water-cement ratio inevitably, so that a large amount of heat occurs in concrete. The thermal cracks make the durability and quality of concrete structures become worse, result from temperature rise and thermal stress due to heat of hydration. In this study, the proposal of using ground granulated blast furnace slag, fly ash and chemical admixtures was investigated to decrease the temperature rise of concrete.

• Computers and Concrete
• /
• v.8 no.5
• /
• pp.583-595
• /
• 2011

This paper studied the cement efficiency factor (k factor) of high calcium Class F fly ash. This k factor represents a unit of fly ash with efficiency equivalent to k unit of cement. The high calcium Class F fly ash was used to replace cement in concrete. The modified Bolomey's law with linear relationship was used for the analysis of the result of compressive strength, cement to water ratio (c/w) and fly ash to water ratio (f/w) by using the multi-linear regression to determine the k factor and other constants in the equations. The results of analysis were compared with the results from other researcher and showed that the k factor of high calcium Class F fly ash depends on the fineness of fly ash, replacement level and curing age. While the amount of CaO content in Class F fly ash not evident. Furthermore, necessary criteria and variables for the determination of the k factor including the use of the k factor in concrete mix design containing fly ash were proposed.

• Journal of the Korean Recycled Construction Resources Institute
• /
• v.6 no.3
• /
• pp.88-93
• /
• 2011

To resolve the problem which is demand and supply imbalance of fine aggregate by the shortage of natural fine aggregate and the environment regulations, the studies for the application of recycled fine aggregate made from waste concrete have been recently carried out. The objective of this study is to shed light on the mechanical properties and durability performance of concrete using recycle fine aggregate with various water to cement ratios and unit water contents. And it is intend to propose the fundamental data for structural application of recycled concrete. In particular, the effects according to the variations of water to cement ratios and unit water contents in recycled concrete with recycled fine aggregate replacement of 100 percent are discussed by the test results, such as air content, slump, time of set, compressive strength, tensile strength, carbonation, chloride penetration.

• Proceedings of the Korea Concrete Institute Conference
• /
• 1993.04a
• /
• pp.34-39
• /
• 1993

Recently inappropriate aggregates are used as a raw material for ready-mixed concretes, due to the shortage of natural aggregate resources and the prohibition of their extraction for the environmental protection. We, therefore, have conducted experiments to obtain some knowledge of properties of domestic aggregates and to investigate subsequent changes in the properties of the fresh and hardened concretes. To this end, aggregates currently used in 13 domestic ready-mixed concrete plants were collected. Most of aggregate used in this experiment satisfied the KS in density and unit weight. But some of the aggregates have the particle size distribution that can effect bad influence on concrete. In this experiment the aggregates are found to have a bad particle size distribution, resulting in high amount of a unit water content and a unit cement content in concrete.