• 한국재료학회지
• /
• 제23권2호
• /
• pp.128-134
• /
• 2013

A study on the corrosion behavior of Inconel alloys and Incoloy 800H in molten salt of LiCl-$Li_2O$ was investigated at $650^{\circ}C$ for 24-312 hours in an oxidation atmosphere. The order of the corrosion rate was Inconel 600 < Inconel 601 < Incoloy 800H < Inconel 690. Inconel 600 showed the best performance suggesting that the content of Fe, Cr and Ni are the important factor for corrosion resistance in hot molten salt oxidation conditions. The corrosion products of Inconel 600 and Inconel 601 were $Cr_2O_3$ and $NiFe_2O_4$, In case of Inconel 690, a single layer of $Cr_2O_3$ was formed in the early stage of corrosion and an outer layer of $NiFe_2O_4$ and inner layer of $Cr_2O_3$ were formed with an increase of corrosion time. In the case of Incoloy 800H, $Cr_2O_3$ and $FeCr_2O_4$ were observed. Most of the outer scale of the alloys was observed to be spalled from the results of the SEM analysis and the unspalled scale which adhered to the substrate was composed of three layers. The outer layer, the middle one, and the inner one were Fe, Cr, and Ni-rich, respectively. Inconel 600 showed localized corrosion behavior and Inconel 601, 690 and Incoloy 800H showed uniform corrosion behavior. Ni improves the corrosion resistance and too much Cr and/or Fe content deteriorates the corrosion resistance.

• 방사성폐기물학회지
• /
• 제22권1호
• /
• pp.67-80
• /
• 2024

Fundamental aspects of creating passivation layers for corrosion resistance in nuclear engineering applications, specifically the ability to form complete layers versus porous ones, are being explored in this study. Utilizing a laser ablation technique, 1,064 nm fire at 10 Hz with 60 pulses per shot and 0.5 mm between impact points, aluminum samples are treated in an attempt to create a fully formed passivation layer that will be tested in a LiCl-KCl eutectic salt. By placing these samples into an electrochemical environment mimicking a pyroprocessing system, corrosion rates, resistances and material characteristics are tested for one week and then compared between treated and untreated samples. In initial testing, linear sweep voltammetry indicates corrosion current density for the untreated sample at -0.038 mA·cm^-2 and treated samples at -0.024 mA·cm^-2 and -0.016 mA·cm^-2, respectively. This correlates to a control sample corrosion rate of -0.205 mm·yr^-1 and treated rates of -0.130 mm·yr^-1 and -0.086 mm·yr^-1 for samples 1 and 2. In addition, electrochemical impedance spectroscopy circuits show application of a longer-lasting porous passivation layer on the treated metal, compared to the naturally forming layer. However, the current technique fails to create a uniform protection layer across the sample.

• Journal of Electrochemical Science and Technology
• /
• 제11권4호
• /
• pp.368-378
• /
• 2020

In the paper, corrosion behavior of T91 steel in different concentrations of NaHSO₃ solution was studied in combination with scanning electron microscope (SEM) and electrochemical measurements. The results showed that the steel exhibited active anodic dissolution characteristics in the solution, and NaHSO₃ concentration affected both cathodic and anodic behaviors. The steel surface was covered by intact corrosion products in the solutions, but the compactness and mechanical properties of the corrosion products degraded with the increase of NaHSO₃ concentration. In low-concentration NaHSO₃ solution the steel tended to undergo uniform corrosion with slight corrosion pits, but its corrosion mode gradually transited to localized corrosion as the NaHSO₃ concentration increased. The mechanical property degradation of the corrosion products caused by sulfur compounds and the pH decrease of the solution are the important factors to accelerating its corrosion process.

• 한국수소및신에너지학회논문집
• /
• 제23권6호
• /
• pp.573-580
• /
• 2012

Corrosion resistance and basic physical properties of solid tantalum are not comparable to most of the structural metallic materials. The relative high cost and melting temperature of tantalum are obstacles to be widely applied to general engineering processes. Electrodeposition in molten salt enables compact and uniform tantalum coating. In this study, Ta was coated onto base metal (SUS316L) with different current densities (0.5, 5, $20mA/cm^2$) by using MSE (Molten Salt Electrodeposition). In this study, it showed that deposition efficiency and microstructure of Ta coating layer were strongly depended on current density. In the case of the current density of $5mA/cm^2$, densest microstructure was obtained. The current density above $5mA/cm^2$ caused non-uniform microstructure due to rapid deposition rate. Dense microstructure and intact coating layer contributed to significant corrosion resistance enhancement.

• 해양환경안전학회:학술대회논문집
• /
• 해양환경안전학회 2005년도 춘계학술발표회
• /
• pp.161-165
• /
• 2005

Recently, it is on the increase interest for Al alloy with new material for ship application to substitute for FRP ship. The reason is thatAl alloy ship has beneficial characteristics such as high sea speed, increase of loadage and easy to recycle compared with FRP ship. In this paper, mechanical and electrochemical properties are investigated by slow strain rate test experiment in various applied potential condition. These results will provide as reference data to design ship by deciding optimum protection potential regard to hydrogen embrittlement and stress corrosion cracking. In general, Al and Al alloys are not corroded with forming film which has the corrosion resistance property in neutral solution. However, it was observed that formation and destruction of passive film by $Cl^-$ ion in sea water environment. At comparison of current density after 1200 sec in potentiostatic experiment, the current density in the potential range of -0.68 $\~$-1.5 V is shown low value. The low current density means protection potential range. Elongation in applied potential of 0 V was high. However, the corrosion protection application in this condition is impossible potential because the toughness is low value by decreasing strength by active dissolution reaction at parallel part of specimen. The film composed with $CaCO_3$ and $Mg(OH)_2$ has a corrosion resistance property. However, the uniform electrodeposition coating at below -1.6 V potential is not formed since the time to form the uniform electrodeposition coating is short. Therefore, it is concluded that mechanical property is poor because effect by hydrogen gas generation is larger than that of electrodeposition coating. It is concluded that the optimum protection potential range from comparison of_maxim urn tensile strength, elongation and time to fracture is -1.3$\~$0.7 V (SSCE).

• 한국표면공학회지
• /
• 제44권3호
• /
• pp.82-88
• /
• 2011

A uniform chromium-free conversion coating treated with an alkaline phosphate- permanganate solution was formed on the AZ 31 magnesium alloy. The effect of acid pickling on the morphology and on the corrosion resistance of the alkaline phosphate-permanganate conversion coating was investigated. The chemical composition and phase structure of conversion coating layer were determined via optical microscopy, SEM, EDS, XPS and XRD. Results show that the conversion coatings are relatively uniform and continuous, with thickness 1.8 to $2.4\;{\mu}m$. The alkaline phosphate-permanganate conversion coating was mainly composed of elements Mg, O, P, Al and Mn. The conversion-coated layers were stable compounds of magnesium oxide and spinel ($MgAl_2O_4$). These compounds were excellent inhibitors to corrosion. The electrochemical corrosion behaviors of coatings in 3.5 wt.% NaCl solutions were evaluated by electrochemical impedance spectroscopy, potentiodynamic polarization technique. EIS results showed a polarization resistance of $0.1\;k{\Omega}$ for the untreated Mg and $16\;k{\Omega}$ for the alkaline phosphate-permanganate conversion treatment sample, giving an improvement of about 160 times. The results of the electrochemical measurements demonstrated that the corrosion resistance of the AZ 31 magnesium alloy was improved by the alkaline phosphate-permanganate conversion treatment.

• 수산해양기술연구
• /
• 제24권2호
• /
• pp.94-100
• /
• 1988

평면 굽힘부식피로 시험기를 사용하여 선박용 알루미늄합금재의 부식피로파양에 관한 연구를 한 결과 다음과 같은 결론을 얻었다. 1. 비저항이 증가함에 따라서 초기 부식피로균열발생까지의 반복회수는 지연되고, 그 부식감수성은 감소하는 양상을 나타낸다. 2. 비저항이 감소할수록 Paris rule의 실험상수 m 값은 작아지면서 응력강도 계수값에 비해 부식에 의한 영향이 더욱 민감해 진다. 3. 알루미늄 5086 합금의 부식피로균열은 입계균열파양의 양상을 보이고 있다. 4. 응력강도계수값이 증가함에 따라 부식감수성은 감소되어지고 응력강도계수값이 40kg.mm super(-3/2) 이상일 때 부식감수성은 거의 균일하게 된다.

• 한국표면공학회지
• /
• 제52권2호
• /
• pp.103-110
• /
• 2019

As an anti-corrosion method in seawater, cathodic protection is widely recognized as the most effective and technically appropriate corrosion prevention methodology for marine structures against harsh corrosive environment. When applying the cathodic protection in seawater, the surface of the metal facilities the formation of compounds of $CaCO_3$ and $Mg(OH)_2$. These mixed compounds are generally called 'calcareous deposits'. This layer functions as a barrier against the corrosive environment and functions to further inhibit the corrosion process and then leading to a decrease in current demand for cathodic protection. However, calcareous deposit films are partially formed on the surface of the cathode and there are some difficulties to maintain both a corrosion resistance for a long period of time and a strong adhesion between deposits and base metal. In this study, the pulse electrodeposition process was applied to improve adhesion and corrosion resistance of the calcareous deposit films, and to solve the problem of hydrogen embrittlement at high current density. The uniform and compact calcareous deposit films were prepared by pulse electrodeposition process, and their properties were characterized using various surface analytical techniques together with electrochemical methods.

• 한국건축시공학회지
• /
• 제21권6호
• /
• pp.539-550
• /
• 2021

일반 전기 아크에 의한 금속용사공법에 비해 시공속도와 효율성능이 우수한 플라즈마 아크 용사장비를 개발하여 이 플라즈마 용사장비에 의한 코팅의 부식특성 평가가 요구되었다. 본 연구에서는 일반 탄소강에 Zn 및 Zn-15Al을 플라즈마 아크 금속 용사법으로 코팅한 후 해수 환경과 유사한 3.5wt.% NaCl 용액에 침지하여 내식성을 평가하였다. SEM 및 XRD에 의한 표면 형상 분석 시험 결과, Zn 코팅이 다공성이고 침상 형태로 되어 있어 용액의 침투가 용이하여 부식 속도가 빠른 것을 알 수 있었다. 반면, Zn-15Al 코팅은 균일하고 조밀한 형태를 보여 부식을 억제하는 것으로 나타났다.

• Corrosion Science and Technology
• /
• 제22권4호
• /
• pp.257-264
• /
• 2023

Ti-6Al-4V alloys are mainly used as dental materials due to their excellent biocompatibility, corrosion resistance, and chemical stability. However, they have a low bioactivity with bioinertness in the body. Therefore, they could not directly bond with human bone. To improve their applications, their bone bonding ability and bone formation capacity should be improved. Thus, the objective of this study was to improve the bioinert surface of titanium alloy substrate to show bioactive characteristics by performing surface modification using wollastonite powder. Commercial bioactive wollastonite powder was successfully deposited onto Ti-6Al-4V alloy using a room temperature spray process. It was found that wollastonite-coated layer showed homogeneous microstructure and uniform thickness. Corrosion resistance of Ti-6Al-4V alloy was also improved by plasma electrolytic oxidation treatment. Its wettability and bioactivity were also greatly increased by wollastonite coating. Results of this study indicate that both plasma electrolytic oxidation treatment and wollastonite coating by room temperature spray process could be used to improve surface bioactivity of Ti-6Al-4V alloy substrate.