• Clean Technology
• /
• v.23 no.4
• /
• pp.378-387
• /
• 2017

To obtain epoxy resin with permanently attached flame-retardant groups, phosphorus compound containing di-hydroxyl group [10-(2,5-dihydroxyphenyl)-9,10-dihydro-9-oxa-10-phospha phenanthrene-10-oxide, DOPO-HQ] and silicone compound containing di-hydroxyl group (polydimethylsiloxane, hydroxyl terminated, PDMS) were reacted with uncured epoxy prepolymer (diglycidyl ether of bisphenol A, DGEBA) and then cured using 4,4-diaminodiphenylmethane (DDM) as a crosslinking agent. The properties of the resulting epoxy materials were characterized using Fourier transform infrared (FTIR) spectrometer, differential scanning calorimetry (DSC), thermogravimetric analysis (TGA), limiting oxygen index (LOI) test/vertical burning test (UL 94-V test), tensile properties test and impact test. This study examined the effect of phosphorus/silicone compound contents on the thermal/mechanical properties and flame retardancy of cured epoxy resins containing phosphorus and silicone compounds. It was found that the thermal/mechanical properties of epoxy resins containing phosphorus and silicone components were higher than those of simple epoxy resin. The flame-retardancy (LOI: 29.9 ~ 31.8% and UL 94-V: V-0) of all samples containing phosphorus compound and phosphrous compound/silicone compound was found to be passed the flame-retardant requirements (LOI: > 30%, UL 94-V: V-0) of LOI and vertical burning tests. However, the flame-retardancy (LOI: 21.4% and UL 94-V: no rating) of simple epoxy resin was found to be failed the flame-retardant requirements.