• Journal of The Korean Society of Agricultural Engineers
• /
• v.51 no.6
• /
• pp.77-81
• /
• 2009

This study was performed to evaluate applicability of patching materials for underwater dam concrete structure. Two kinds of patching materials was investigated. Laboratory experimentals were conducted by workability, compressive strength, bond strength, chloride ion penetration, abrasion resistance. Test results showed that the most performances are relatively good except chloride ion penetration.

• Journal of the Korean GEO-environmental Society
• /
• v.22 no.10
• /
• pp.21-29
• /
• 2021

Most concrete gravity-type dams in and out of the country were constructed by column method to control cracks caused by concrete hydration heat generated during construction, resulting in a certain level of leakage after impoundment through various causes, such as contraction joints and construction joints. However, due to the characteristics of concrete structures that shrink and expand according to temperature, concrete dams have vertical joints and drains to allow penetration. PVC waterproof shows excellent effects in completion of the dam, which however increases the possibility of interfacial failure due to different thermal expansion. Other causes of penetration may include problems with quality control during installation, generation of cracks due to heat of hydration of concrete, waterproofing methods, etc. In the case of Bohyunsan Dam in Yeongcheon, North Gyeongsang Province, the amount of drainage in the gallery was checked and underwater, and it was confirmed that there are many penetrations from drainage holes connected to vertical joints, and that some of the PVC waterproofs are not fully operated. As a new method to prevent penetration through vertical joints, D.S.I.M. (Dam Sealing Innovation Method) developed by World E&C was applied to Bohyunsan Dam and checked the amount of drainage in the gallery. As a result of first testing three most leaking vertical joints, the drain in the gallery was reduced by 87% on the average and then applied to the remaining 13 locations, which showed a 83% reduction effect based on the total drain in the gallery. Summing up these results, it was found that D.S.I.M. preventing water leakage from the upstream face is a valid construction method to reduce the water see-through and penetration quantity seen in downstream faces of concrete dams. If D.S.I.M. is applied to other concrete dams at domestic and abroad, it is expected that it will be very effective to prevent water leakage through vertical joints that are visible from downstream faces.

• KSCE Journal of Civil and Environmental Engineering Research
• /
• v.29 no.5C
• /
• pp.207-215
• /
• 2009

Cemented soils or concrete are usually cured under moisture conditions and their strength increases with curing time. An insufficient supply of water to cemented soils can contribute to hydration process during curing, which results in the variation of bonding strength of cemented soils. In this study, by the consideration of in situ water supply conditions, cemented sand with cement ratio less than 20% is prepared by air dry, wrapped, moisture, and underwater conditions. A series of unconfined compression tests are carried out to evaluate the effect of curing conditions on the strength of cemented soils. The strength of air dry curing specimen is higher than those of moisture and wrapped cured specimens when cement ratio is less than 10%, whereas it is lower when cement ratio is greater than 10%. Regardless of cement ratio, air dry cured specimens are stronger than underwater cured specimens. A strength increase ratio with cement ratio is calculated based on the strength of 4% cemented specimen. The strength increase ratio of air dry cured specimen is lowest and that of wrapped, moisture, and underwater cured ones increased by square. Strength of air dry cured specimen drops to maximum 30% after wetting when cement ratio is low. However, regardless of cement ratio, strength of moisture and wrapped specimens drops to an average 10% after wetting. The results of this study can predict the strength variation of cemented sand depending on water supply conditions and wetting in the field, which can guarantee the safety of geotechnical structures such as dam.