• 한국철도학회논문집
• /
• 제3권2호
• /
• pp.77-83
• /
• 2000

This study proposes the integrity evaluation of the bogie frame using ultrasonic fractography analysis. Analysis objectives in this study are to investigate fracture planes of damaged zone by the A-scan method. The surface condition of fracture planes shows degree of degradation by the stress concentration. The detection of the natural defects in the bogie frame is performed using the characteristics of echodynamic pattern in ultrasonic signal. Results of ultrasonic testing agree fairly well with those of actual fracture plane. In quantitative fractography analysis, microstructures of actual fracture plane turned out to be intergranular and transgranular fracture. Proposed ultrasonic fractography analysis in this study can be used for the integrity evaluation of the bogie frame.

• 한국정밀공학회지
• /
• 제10권2호
• /
• pp.154-160
• /
• 1993

A mothod to decide the optimal frequency for the fracture velocity measurement by ultrasonic fractography is presented. A theoretical formula to decide the optimal frequency for ultrasonic fractography testing is made and it is compared with experimental value. According to the formula the optimal frequency is shown to be depending on the attenuation coefficient and size(width) of the specimen. In the case of PMA specimen with ligament 43mm the theoretical value for the optimal frequency is about 260 KHz and it is good agreement with experimental value.

• 한국철도학회:학술대회논문집
• /
• 한국철도학회 2000년도 추계학술대회 논문집
• /
• pp.461-467
• /
• 2000

This study proposes the integrity evaluation of bogie frame using ultrasonic waves-fractography analysis. Analysis objectives in this study are to investigate fracture planes of damaged zone by the A-scan method. The surface condition of fracture plane shows degree of degradation by stress concentration. The detection of the natural defects in bogie frame is performed using the characteristics of echodynamic pattern in ultrasonic signal. Results of ultrasonic testing agree fairly well with those of actual fracture plane. In quantitative fractography analysis, microstructures of actual fracture plane turned out to be intergranular and transgranular fracture, Proposed ultrasonic-fractography analysis in this study can be used for the integrity evaluation of the bogie frame

• 한국가스학회지
• /
• 제4권1호
• /
• pp.55-62
• /
• 2000

Pit형 표면결함으로부터 발생하는 작은 피로균열의 거동을 초음파의 표면파를 이용하여 이를 위하여 피로시험중인 Al 2024-T3를 시험재료, 피로시험도중 초음파를 이용하여 피로균열의 거동을 조사하였다. 즉, 피로시험에서 균열이나 Pit로부터 발생하는 작은 피로균열을 여러 응력조건하에서 나타나는 표면파의 반사특성에 관하여 연구하였다. 또한 이론적 결과와 실험적 결과를 상호 비교, 분석하였고, SEM을 사용하여 이들 작은 피로균열을 관찰하였다. 초음파를 이용한 피로균열의 균열 개구 거동에 관한 연구에서 피로균열의 유효균열 특성을 초음파법으로 평가 할 수 있었다.

• 대한기계학회논문집
• /
• 제18권3호
• /
• pp.600-611
• /
• 1994

The purpose of this research is to propose a model for the prediction of residual strength. For this purpose, two-paremeter model based on Caprino's is developed and formulated by the ratio of indentation due to impact and normalized residual strength. The damage zone is considered only as an indentation. Impact tests are carried out on laminated composites by steel balls. Test material is carbon/epoxy laminate. The specimens are composed of $[{\pm}45^{\circ}/0^{\circ}/90^{\circ}]_2$ and $[\pm}45^{\circ}]_4$ stacking sequence and have $0.75^T{\times}0.26^W{\times}100^L(mm) dimension. A proposed model shows a good correlation with the experimental results And failure mechanism due to high impact velocity is discussed on CFRP laminates to examine the initiation and development of damage by fractography and ultrasonic image ststem. The effect of the unidirectional ply position on the residual strength is considered here.

• 한국정밀공학회지
• /
• 제11권3호
• /
• pp.105-121
• /
• 1994

In this paper, we proposed the two-parameter model for predicting the residual strength in CFRP laminated composites subjected to high velocity impact and developed and formulated it based upon Cparino's by using the ratio of impact and the normalized residual strength. Critical indentation was obtained by the statical indentation tests. Impact tests were carried out through air-gun type impact equipment with the velocities varied 30-100m/sec. Projectiles were steel balls with 5 and 7mm in diameter. Test material was carbon/epoxy. The specimens were composed of [ .+-. 45 .deg. /0 .deg. /90 .deg. ]$\_$2/ and [ .+-. 45 .deg. ]$\_$4/stacking sequences and had 0.75$\^$T/*0.26$\^$W/*100$\^$L/(mm) dimension. Results from the proposed model were in good agreement with the test data. And failure mechanism due to high velocity impact is given here to examine the initation and deveolpment of damage by fractography and ultrasonic image system. The effects of the 0 .deg. -direction ply position and the amount to damage area on the residual strength are considered here.