• Journal of the Korean institute of surface engineering
• /
• v.29 no.6
• /
• pp.862-868
• /
• 1996

Cadmium sulfide is commonly used as the window material for thin film solar cells, and can be prepared by several techniques such as sputtering, spray pyrolysis, close spaced sublimation (CSS), thermal evaporation, solution growth methods, etc. In this study, CdS films were deposited by thermal evaporation, close spaced sublimation, and solution growth methods, respectively, and the effects of the methods on physical properties of polycrystalline CdS deposited on ITO/glass were investigated. Also, the effects of variously prepared CdS thin films on the physical properties of CdTe deposited on the CdS were investigated. The thickness of polycrystalline CdS films was maintained at $0.3\mu\textrm{m}$ except for the solution grown CdS when $0.2\mu\textrm{m}$ thick CdS was deposited. After the deposition, all the samples were annealed at $400^{\circ}C$ or $500^{\circ}C$ in H2 atmosphere. To investigate physical properties of the deposited and annealed CdS thin films, UV-VIS spectro-photometry, X-ray diffractometry (XRD), and Auger electron spectroscopy (AES), and cross sectional transmission electron microscopy(XTEM) were used to analyze grain size, crystal structure, preferred orientation, optical properties, etc. The annealed CdS showed the bandedge transition at 510nm and the optical transmittance high than 80% for all of the variously deposited films. XRD results showed that CdS thin films variously deposited and annealed had the same hexagonal structures, however, showed different preferred orientations. CSS grown CdS had [103] preferred orientation, thermally evaporated CdS had [002], and CdS grown by the solution growth had no preferred orientation. The largest grain size was obtained for the CSS grown CdS while the least grain size was obtained for the solution grown CdS. Some of the physical properties of CdTe deposited on the CdS thin film such as grain size at the junction and grain orientation were affected by the physical properties of CdS thin films.

• Analytical Science and Technology
• /
• v.6 no.3
• /
• pp.289-296
• /
• 1993

The formation of Mo(VI)-alizarin red S chelate ion and its extraction into an organic solvent by ion-pairing were studied for the separative determination of trace Mo(VI) in natural water samples. Natural water 100mL was sampled in 250mL separatory funnel. After Mo(VI)-ARS chelate ion was formed by adding 0.01M alizarin red S solution 0.5mL to the water sample of pH 4.0, 0.2% aliquat-336 chloroform solution 10mL was added and the solution was vigorously shaked for about 30 seconds to from the ion-pair between Mo(VI)-ARS and aliquat-336, completely. The solution was stood for about 90 minutes. And the organic phase was taken for the absorbance measurement of the ion-pair at 520 nm. The content of Mo(VI) in sample was obtained from the standard calibration curve. Several extraction conditions such as pH, adding amounts of alizarin red S and aliquat-336, and shaking and standing times were optimized. This procedure was applied to the analysis of river and tap waters. It could be confirmed from the recoveries of over 99% in samples spiked with a given amount of Mo(VI) that this method was quantitiative in the determination of trace Mo(VI) in a natural water.