• Journal of the Korea Academia-Industrial cooperation Society
• /
• v.14 no.2
• /
• pp.943-948
• /
• 2013

In this study, the characteristics of polymer-modified mortar which include UM resin, eco-friendly resin, was studied for improving the durability of concrete. UM and cement mortar were mixed with a certain percentage. Eco-friendly UM resin polymer-modified mortar was evaluated by compressive strength, splitting tensile strength, flexural strength, water absorption and chemical resistance experiments. The characteristics of eco-friendly UM resin polymer-modified mortar were evaluated by experiments. Performance of compressive strength and splitting tensile strength were decreasing. On the other hand, performance of flexural strength, water absorption and chemical resistance were increasing. Eco-friendly UM resin polymer-modified mortar reinforced concrete durability performance is excellent.

• Journal of the Korea Academia-Industrial cooperation Society
• /
• v.17 no.9
• /
• pp.27-33
• /
• 2016

Phenolic resin has excellent heat resistance and good mechanical properties as a thermosetting resin. However, its thermosetting characteristics cause it to produce a non-recyclable waste in the form of sprue and runner which is discarded and represents up to 15~20% of the overall products. Forty thousand tons of phenolic resin sprue and runner are disposed of (annually). The (annual) cost of such domestic waste disposal is calculated to be 20 billion won. In this study, discarded phenol resin scraps were pulverized and treated by silanes to improve their interfacial adhesion with HDPE. The sizes of the pulverized pulverulent bodies and fine particles were (100um~1000um) and (1~100um), respectively. The pulverized phenol resin was treated with 3-(methacryloyloxy) propyltrimethoxysilane and vinyltrimethoxy silane and the changes in its characteristics were evaluated. The thermal properties were evaluated by DSC and HDT. The mechanical properties were assessed by a notched Izod impact strength tester. When the silane treated phenol resin was added, the heat distortion temperature of HDPE increased from $77^{\circ}C$ to $96^{\circ}C$ and its crystallinity and crystallization temperature also increased. Finally, its impact strength and tensile strength increased by 20% and 50%, respectively, in comparison with the non-treated phenol resin.

• Journal of the Korea Concrete Institute
• /
• v.25 no.3
• /
• pp.313-320
• /
• 2013

In this study, performance of fiber-reinforced polymer-modified mortar was studied for the development of eco-friendly materials for high performance repair and reinforcement. The general cement mortar and eco-friendly UM resin was mixed with a certain percentage for increased durability. To increase the strength of the polymer-modified mortar, PVA fiber, steel fiber and hybrid fiber were added at a constant rate. Hybrid fiber is contains the same percentage of PVA fiber and steel fiber. In order to determine the strength properties of fiber-reinforced polymer-modified mortar, the compressive strength test, the splitting tensile strength test and the flexural strength test were performed. And, in order to determine the durability properties of fiber-reinforced polymer-modified mortar, water absorption test and chemical resistance test were performed. From the experimental results, polymer-modified mortar using UM resin was improved durability. And the tensile strength and flexural strength increased, which were the vulnerability of fiber reinforced polymer-modified mortar. From this study, fiber-reinforced polymer-modified mortar using eco-friendly UM resin can be used to repair and reinforcement for the external exposure of concrete structures to improve the durability.

• The Journal of the Institute of Internet, Broadcasting and Communication
• /
• v.18 no.6
• /
• pp.107-112
• /
• 2018

Shielding effectiveness (SE) improvement with EMI shield layers fabricated by conformal spray coating system was studied. Silver or Nickel powder filled acrylic resin were sprayed on the samples. We compared the performance with the viscosity of 400 cPs and 100 cPs cases. The thickness range of the coating layer was 20 to 50 um for the silver, 60 to 120 um for the nickel. The shielding effectiveness was measured by ASTM D4935 using coaxial type TEM-cell. The silver-filled resin showed much better performance than that of the nickel-filled resin. The shielding effectiveness increased almost proportional to the thickness of the coating layers until being saturated around 63 dB for the silver-layer or around 34 dB for the nickel-layer. The best performance measured in this study was the shielding effectiveness of 63 dB with $35{\mu}m-thick$ of silver-layer.

• Restorative Dentistry and Endodontics
• /
• v.29 no.6
• /
• pp.520-531
• /
• 2004

The aim of this study was to investigate the effect of monomer and filler compositions on the rheological properties related to the handling characteristics of resin composites. Methods. Resin matrices that Bis-GMA as base monomer was blended with TEGDMA as diluent at various ratio were mixed with the Barium glass (0.7 um and 1.0 um), 0.04 um fumed silica and 0.5 um round silica. All used fillers were silane treated. In order to vary the viscosity of experimental composites, the type and content of incorporated fillers were changed, Using a rheometer, a steady shear test and a dynamic oscillatory shear test were used to evaluate the viscosity ($\eta$) of resin matrix, and the storage shear modulus (G'), the loss shear modulus (G"), the loss tangent ($tan{\delta}$) and the complex viscosity (${\eta}^*$) ofthe composites as a function of frequency ${\omega}{\;}={\;}0.1-100{\;}rad/s$. To investigate the effect of temperature on the viscosity of composites, a temperature sweep test was also undertaken. Results. Resin matrices were Newtonian fluid regardless of diluent concentration and all experimental composites exhibited pseudoplastic behavior with increasing shear rate. The viscosity of composites was exponentially increased with increasing filler volume%. In the same filler volume, the smaller the fillers were used, the higher the viscosities were. The effect of filler size on the viscosity was increased with increasing filler content. Increasing filler content reduced $tan{\delta}$ by increasing the G' further than the G". The viscosity of composites was decreased exponentially with increasing temperature.

• Proceedings of the Korean Society For Composite Materials Conference
• /
• 2005.11a
• /
• pp.111-116
• /
• 2005

In this study the compatibility of Epoxy resin with Phenolic using three different separation layer techniques was investigated; some important process variables such as pressure, flow front and deformation were monitored in order to get a better understanding of the process.

• The Journal of the Korean dental association
• /
• v.10 no.12
• /
• pp.785-794
• /
• 1972

• Journal of Dental Rehabilitation and Applied Science
• /
• v.36 no.1
• /
• pp.1-11
• /
• 2020

Purpose: The purpose was to compare shear bond strength (SBS) of three types of resin for temporary restoration to polyetherketoneketone (PEKK) depending on surface modification. Materials and Methods: Sixty disks made from PEKK were air-abraded with 110 ㎛ alumina particles (Cobra, Renfert GmbH, Hilzinge, Germany) and thirty specimens were divided into two groups each: PEKK without Visio.link (Bredent, Senden, Germany)(U) and with Visio.link (P). Resins for temporary restoration (polymethylmethacrylate; PMMA, polyethylmethacrylate; PEMA, bis-acryl composite resin) in the shape of a square with one side 3.2 mm were bonded to PEKK twenty respectively and classified into six groups (UM, UE, UC, PM, PE and PC). All specimens were stored in distilled water at 37℃ for 24 hours. SBS of each group was measured at a crosshead speed of 2 mm/min in universal testing machine. SBS was compared using one-way ANOVA and a Tukey HSD test (P = 0.05). Results: Group UM and group UE showed a significant difference in SBS with group UC (P < 0.05). Group PC showed a significant increase in SBS than group UC (P < 0.05). Conclusion: It is recommended to apply Visio.link to PEKK for adhering bis-acrylic composite resin, but not for PMMA and PEMA in clinical practice.

• Proceedings of the Korean Radioactive Waste Society Conference
• /
• 2018.11a
• /
• pp.377-378
• /
• 2018

• Advanced Composite Materials
• /
• v.18 no.2
• /
• pp.135-152
• /
• 2009

Liquid molding processes, such as resin transfer molding, involve resin flow through a porous medium inside a mold cavity. Numerical analysis of resin flow and mold filling is a very useful means for optimization of the manufacturing process. However, the numerical analysis is quite time consuming and requires a great deal of effort, since a separate numerical calculation is needed for every set of material properties, part size and injection conditions. The efforts can be appreciably reduced if similarity solutions are used instead of repeated numerical calculations. In this study, the similarity relations for pressure, resin velocity and flow front propagation are proposed to correlate another desired case from the already obtained numerical result. In other words, the model gives a correlation of flow induced variables between two different cases. The model was verified by comparing results obtained by the similarity relation and by independent numerical simulation.