• 한국분말야금학회:학술대회논문집
• /
• 한국분말야금학회 2006년도 Extended Abstracts of 2006 POWDER METALLURGY World Congress Part 1
• /
• pp.555-556
• /
• 2006

The study examines hardness pattern of SH737-2Cu-.9C samples transient liquid phase sintered at different temperatures viz. $1120^{\circ}C$, $1180^{\circ}C$ and $1250^{\circ}C$, heat treated by various methods and then tempered at different temperatures. Sintered samples were characterized for density and densification parameter, and austenitized at $900^{\circ}C$, subsequently cooled by four different methods viz. annealing, normalizing, oil and brine quenching. Hardness pattern was found minimum for air cooled and maximum for brine quenched, and samples sintered at $1250^{\circ}C$ had relatively higher hardness. The O.Q and B.Q samples were then tempered at $200^{\circ}C$, $400^{\circ}C$, $600^{\circ}C$ and $700^{\circ}C$. Hardness pattern typically showed secondary hardness taking place, with maximum around $600^{\circ}C$.

• 한국분말재료학회지
• /
• 제17권6호
• /
• pp.489-493
• /
• 2010

Nickel-based and iron-based alloys have been developed and commercialized for a wide range of high performance applications at severely corrosive and high temperature environment. This alloy foam has an outstanding performance which is predestinated for diesel particulate filters, heat exchangers, and catalyst support, noise absorbers, battery, fuel cell, and flame distributers in burners in chemical and automotive industry. Production of alloy foam starts from high-tech coating technology and heat treatment of transient liquid-phase sintering in the high temperature. These technology allow for preparation of a wide variety of foam compositions such as Ni, Cr, Al, Fe on various pore size of pure nickel foam or iron foam in order for tailoring material properties to a specific application.

• 한국세라믹학회지
• /
• 제29권5호
• /
• pp.410-418
• /
• 1992

Si3N4, AlN and Y2O3 powder mixtures of the Y0.1(Si, Al)12(N, O)16 composition were hot-pressed at 1900℃ for 0 to 60 min under 30 MPa in order to fabricate the partially-stabilized α-Sialon ceramics (X=0.1). Room and high temperature flexural strengths of the specimens were compared with those of Si3N4-5 wt%Y2O3, Si3N4-5 wt%Y2O3-2 wt%Al2O3, and β-Sialon (Z=0.5) ceramics. The flexural strength of the α-Sialon ceramics which was hot-pressed for 15 min showed the highest value of 820 MPa at 1400℃ that is relatively higher temperature. It is guessed that a little amount of glassy phase existed in grain boundary because Y2O3 and AlN components were incoperated in Si3N4 grains, or transient liquid phase sintering, and microstructure with the smaller grain size and the interlocked grains of α'-and β-Si3N4 was obtained by the hot-pressing at high temperature of 1900℃ for the short time (15 min).

• 마이크로전자및패키징학회지
• /
• 제29권1호
• /
• pp.7-16
• /
• 2022

최근 자동차 산업은 친환경, 편리함, 안전성과 같은 키워드를 중심으로 기술 발전이 이뤄지면서 빠르게 변화하고 있다. 친환경에 대한 관심과 맞물려 그린 카(green car)가 이목을 끌고 사용자 편의를 위한 첨단 기술 및 기능을 갖춘 고성능 자동차가 시장에 출시되고 있다. 발전하는 차량 성능으로 인해서 이에 맞는 전장품의 개발 또한 필수적이다. 자동차용 전장품은 고온, 고습, 열충격, 진동, 오염 등 복합적인 환경에서 사용되기 때문에 여타 산업에 비해 높은 수준의 신뢰성 검증이 필요하다. 특히, 부품 내 접합부의 신뢰성을 확보하여 무리없이 기능을 수행하고 운전자의 안전을 보장하는 것이 핵심이다. 따라서 저자는 차량 전장품의 최근 동향을 살펴보고 신뢰성을 향상시킬 수 있는 접합 방법으로 솔더링, TLP 접합 및 소결접합을 소개하였다.

• 한국표면공학회지
• /
• 제50권6호
• /
• pp.510-515
• /
• 2017

In this study, a transient liquid phase sintering (TLPS) process of Ag pastes mixed with a fusible metal alloy of Bi58Sn42 with the melting temperature of $138^{\circ}C$, was examined. After screen printing of the Ag pastes with and without Bi58Sn42 powders on polyimide (PI) substrates, the electrodes were heat-treated at different temperatures in the range between 150 and $300^{\circ}C$ for 60 min in air. Comparing the electrical conductivity of the Ag pastes with and without Bi58Sn42 alloy powder after the heat treatment, it was manifested that the low melting temperature alloy definitely played a major role in an increased conductivity when it is added into the Ag pastes by providing more electrical conduction paths between Ag particles. This can be explained by the fact that capillary force of the melts of Bi58Sn42 can contribute to the rearrangement of the Ag particles during the heat-treatment inducing better connectivity between the Ag particles.