• The Journal of Engineering Research
• /
• v.6 no.1
• /
• pp.161-168
• /
• 2004

In the present study, a simple method was successfully used for hydroxyapatite coatings on Ti-6AL-4V substrates deposited by using a sol-gel derived precursor. Prior to hydroxyapatite coating the samples were micropolished (0.1 micron) and divided into three sets. The first set, were the micropolished samples kept as such. The second set were coated with titania sol and the third set was treated with 5M NaOH. After three repetitions of hydroxyapatite coating procedures on each set and heat treatment at $600^{\circ}C$, the formation of hydroxyapatite has been confirmed by XRD analyses and the substrate material was found to be oxidized with negligible amount of CaO in the coating. The SEM studies revealed surface morphology. Hydroxyapatite, calcined at $600^{\circ}C$, displaying a porous structure arisen from heating of the bulk

• Korean Journal of Materials Research
• /
• v.15 no.7
• /
• pp.444-447
• /
• 2005

In this study, $Hydroxyapatite+TiO_2(HAp+TiO_2)$ composite sol coatings on Cp-Ti substrates were deposited by using a sol-gel derived precursor. Prior to hydroxyapatite coating, the samples were micropolished and divided into three sets. The first set was coated with hydroxyapatite (HAp) directly on Cp-Ti. The second set was first coated with intermediate titania layer and then coated with HAp. The third set samples were coated with $HAp+TiO_2$ (50:50) composite sol. Each samples were predried at $200^{\circ}C$, and heat treated at $600^{\circ}C$. The formation of hydroxyapatite has been confirmed by XRD analyses and the substrate material was found to be oxidized with negligible amount of CaO in the coating. The NaOH treated samples showed the presence of rutile crystal. The SEM studies revealed surface morphologies of each samples. $HAp+TiO_2$ composite sol coating layer was found to be smooth. The bonding strength of each samples were calculated using pull out tests. The bonding strength of the $HAp+TiO_2$ composite sol coating on substrate was 29.35MPa.

• Applied Chemistry for Engineering
• /
• v.32 no.5
• /
• pp.497-503
• /
• 2021

In this study, different methods to coat honeycomb and metal foam substrate with platinum/titania for removing odor gases and volatile organic compounds were investigated. Among them, the powder coating and the nano coating were compared. Scanning electron microscopy/energy dispersive X-ray spectroscopy (SEM/EDX) analysis was used to investigate the surface conditions and exposed platinum composition ratios on honeycomb and metal foam. Also, the catalytic oxidation performance of toluene, trimethylamine and isopropyl alcohol was compared according to the coating method.

• Korean Journal of Materials Research
• /
• v.12 no.5
• /
• pp.334-340
• /
• 2002

$TiO_2$-coated fly ash was synthesized by dropping method of coating agent in order to get $TiO_2$ coating layer with high photocatalytic activity on the surface of coal fly ash. The properties of the $TiO_2$ coating layer such as morphology, crystal structure, crystal size and photocatalytic activity were compared with those of the $TiO_2$-coated fly ash prepared by the traditional method of precipitation. $TiCl_4$ aqueous solution was used as a titanium stock solution and $NH_4HCO_3$ was used as a precipitant. The $TiO_2$ coating layer obtained by dropping method of coating agent was more uniform than that coated by precipitation. However, the crystal of $TiO_2$ coated by dropping method of coating agent was easy to grow by heat treatment because of the small primary particle size and bulky morphology, and its photocatalytic activity was consequently lower than that of the $TiO_2$ coated by precipitation. The $TiO_2$ coating layer obtained by both methods had a crystal structure of anatase, and the temperature of phase transformation into rutile was 90$0^{\circ}C$. The minimum crystal size of $TiO_2$ for the highest photocatalytic activity was found to be about 10nm.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.37 no.2
• /
• pp.182-187
• /
• 2024

Currently, the most developed new energy source is solar energy. Because solar power is installed outside, it is exposed to many pollutants. Pollutants are causing the characteristics of solar energy to deteriorate. Therefore, this study aims to develop a water-repellent coating to prevent contamination of solar modules. Silica and Titania materials are mainly used as water-repellent coating materials. In this study, it was based on silica and the contact angle characteristics were measured according to the change in the amount of silica and ammonia water added and the number of coatings. As a result of the measurement, it was confirmed that the contact angle was more than 60 degrees when 0.5 mol of TEOS was added to 50 mL and 0.15 M when 1 mL of ammonia water was added to 296.47 ml of distilled water. And it was confirmed that the contact angle improved when the number of coatings was applied twice. A water-repellent coating material was applied to low iron tempered glass used to protect dye-sensitized solar cell modules. The characteristics of the module were measured after spraying DI-Water on low-emission tempered glass with a water-repellent coating. As a result of the measurement, the efficiency of the module without application, the efficiency of the module coated once, and the module coated twice were 4.87%, 4.90%, and 4.91%, respectively. It was confirmed that the efficiency of the module increased by applying water-repellent coating. As a result of this study, it is determined that the water-repellent coating material will help improve solar power generation efficiency and lifespan by being self-cleaning and non-reflective.

• Journal of the Korean Ceramic Society
• /
• v.28 no.4
• /
• pp.338-346
• /
• 1991

The alumina-titania composite powders coated with Al2O3 were prepared by the method of hydrolysis-deposition of mixed aluminium salt solution of Al2(SO)4-Al(NO3)3-Urea. The effects of coating-process parameters on the characteristics of coated composite powders were also investigated. As the content of TiO2 dispersed in deionized water increased, the coated composite powders were found to be more uniform in size and unagglomerated. When TiO2 powders were coated for 30 min, the optimum TiO2 content in the coating process was 400 mg/ι. The size of TiO2 particle was increased approximately from 0.7${\mu}{\textrm}{m}$ to 1.0${\mu}{\textrm}{m}$ through coating of Al2O3. The IEP of coated composite powders was pH=8.3 identical to the value of aluminium hydroxides and the zeta-potential showed nearly similar values each other. When heat treating coated composite powders at 130$0^{\circ}C$, only two phases of TiO2(rutile) and Al2TiO5 were observed. These results showed that the suface of TiO2 could be uniformly coated with the aluminium hydroxide.

• Korean Journal of Materials Research
• /
• v.19 no.12
• /
• pp.649-656
• /
• 2009

Inorganic oxide colloids dispersed in alcohol were applied to a stainless steel substrate to produce oxide coatings for the purpose of minimizing emissive thermal transfer. The microstructure, roughness, infrared emissive energy, and surface heat loss of the coated substrate were observed with a variation of the nano oxide sol and coating method. It was found that the indium tin oxide, antimony tin oxide, magnesium oxide, silica, titania sol coatings may reduce surface heat loss of the stainless steel at 300${\circ}C$. It was possible to suppress thermal oxidation of the substrate with the oxide sol coatings during an accelerated thermal durability test at 600${\circ}C$. The silica sol coating was most effective to suppress thermal oxidation at 600${\circ}C$, so that it is useful to prevent the increase of radiative surface heat loss as a heating element. Therefore, the inorganic oxide sol coatings may be applied to improve energy efficiency of the substrate as the heating element.

• Journal of the Korean institute of surface engineering
• /
• v.40 no.4
• /
• pp.190-196
• /
• 2007

Dye sensitized solar cells(DSSC) are the most promising future energy resource due to their high energy efficiency, low production cost, and simple manufacturing process. But one problem in DSSC is short life time compared to silicon solar cells. This problem occurred from photocatalytic degradation of dye material by nanometer sized $TiO_2$ particles. To prevent dye degradation as well as to increase its life time, the transparent coating film is needed for UV blocking. In this study, we synthesized nanometer sized $TiO_2$ particles in sols by increasing its internal pressure up to 200 bar in autoclave at $120^{\circ}C$ for 10 hrs. The synthesized $TiO_2$ sols were all formed with brookite phase and their particle size was several nm to 30 nm. Synthesized $TiO_2$ sols were coated on the backside of fluorine doped tin oxide(FTO) glass by ink jet printing method. With increasing coating thickness by repeated ink jet coating, the absorbance of UV region (under 400 nm) also increases reasonably. Decomposition test of titania powders dispersed in 0.1 mM amaranth solution covered with $TiO_2$ coating glass shows more stable dye properties under UV irradiation, compared to that with as-received FTO glass.

• Journal of the Korean Ceramic Society
• /
• v.29 no.5
• /
• pp.403-409
• /
• 1992

The titania membrane thickness coated on the porous alumina support by the sol-gel method was analyzed using the slipcasting model. The thickness of calcined membrane layers increased linearly from 1.3 to 3.8 ${\mu}{\textrm}{m}$ with the square root of the dipping time (4~40 min). Growth rates of the thickness of wet gels and calcined layers were well described quantitatively by the slipcasting model. Through the regression of experimental data using model equations, the permeability and the pressure drop across wet gels, and the thickness and their growth rate constants of wet gels and calcined layers could be determined. It was also known that the gellation concentration of the TiO2 sol used in this work and the porosity of wet gel layes were 25 mol/ι and 0.53, respectively.

• Korean Journal of Materials Research
• /
• v.4 no.4
• /
• pp.466-471
• /
• 1994

The polymeric titania sol was prepared via partial hydrolysis of titanium isopropoxide and its characteristics were investigated. The effect of solvent, catalyst and water content on the sol stability was investigated. The shear viscosities of sol solution at different temperatures were measured to determine the gel time. Employing the spin coating technique, optically clear and transparent titanium oxide thin film was fabricated. Even after doped with second-order nonlinear optical(NL0) active monomers, the film quality was maintained very homogeneous. The film was corona-poled under 3~ 5kV at 50~$100^{\circ}C$ range. The electro-optic coefficient, $r_{33}$ was measured to be 1.5~5pm/V using the wavelength, 632.8nm from He-Ne laser.